SABIC Innovative Plastics Valox® 830R PBT (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Valox® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Valox® 830R PBT (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
30% glass filled, release grade, polyester alloy.This data was supplied by SABIC-IP for the Asia Pacific region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.54 g/cc | 1.54 g/cc | ASTM D 792 |
| Water Absorption | 0.060 % @Time 86400 sec |
0.060 % @Time 24.0 hour |
ASTM D 570 |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0080 cm/cm @Thickness 3.20 mm |
0.0030 - 0.0080 in/in @Thickness 0.126 in |
SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 106 MPa | 15400 psi | Type I, 50 mm/min; ASTM D 638 |
| Tensile Strength, Yield | 103 MPa | 14900 psi | Type I, 50 mm/min; ASTM D 638 |
| Elongation at Break | 4.0 % | 4.0 % | Type I, 50 mm/min; ASTM D 638 |
| Flexural Yield Strength | 172 MPa | 24900 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| Flexural Modulus | 6.89 GPa | 999 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| Izod Impact, Notched | 0.800 J/cm @Temperature 23.0 °C |
1.50 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 45.3 µm/m-°C @Temperature -40.0 - 60.0 °C |
25.2 µin/in-°F @Temperature -40.0 - 140 °F |
ASTM E 831 |
| Deflection Temperature at 1.8 MPa (264 psi) | 192 °C @Thickness 3.20 mm |
378 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| 193 °C @Thickness 6.40 mm |
379 °F @Thickness 0.252 in |
unannealed; ASTM D 648 | |
| UL RTI, Electrical | 120 °C | 248 °F | UL 746B |
| UL RTI, Mechanical without Impact | 120 °C | 248 °F | UL 746B |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 4.00e+16 ohm-cm | 4.00e+16 ohm-cm | ASTM D 257 |
| Dielectric Constant | 3.5 @Frequency 1.00e+6 Hz |
3.5 @Frequency 1.00e+6 Hz |
ASTM D 150 |
Users viewing this material also viewed the following:
- Latrobe LSSâ„¢ H19 Hot Work Tool Steel (ASTM H19)
- M. Holland Company SA400 Styrene Acrylonitrile
- Solvay Specialty Polymers Amodel® A-1133 HS Polyphthalamide (PPA), 33% Glass Fiber (Conditioned)
- Techmer ES Plastiblend® PA6 GF20 RM BK Nylon 6
- ExxonMobil 2 Ronex Extra Duty
- Toyobo Pelprene™ P-280B Polyester TPE
- E-Polymers SEPAZ® V200L Unfilled PPA
- ConocoPhillips Hydroclear® 6 Ultra-Clean Spindle Oil
- Saint-Gobain CHR® 2916-7 Glass Cloth Backing Silicone Adhesive Pressure Sensitive Tape
Copyright © lookpolymers.com All Rights Reserved