Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Yield Strength | 81.0 MPa | 11700 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Cycoloy® LG9000 PC+ABS (Europe-Africa-Middle East) CYCOLOY LG9000 is a low gloss PC+ABS injection moulding grade. LG9000 combines good impact / heat and UV resistance with a low gloss surface appearence. It is suitable for automotive interior applic.. |
|||
Flexural Yield Strength | 81.0 MPa | 11700 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics Lexan® 191 PC (Asia Pacific) Nonhalogenated. 8.5 MFR. High impact. Thick wall sections. Opaques only. |
|||
Flexural Yield Strength | 81.0 MPa | 11700 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
SABIC Innovative Plastics Lexan® 193 PC Nonhalogenated. 8.5 MFR. High impact. Thick wall sections. UV-stabilized. Opaques only.This data was supplied by SABIC-IP for the Americas region. |
|||
Flexural Yield Strength | 81.0 MPa | 11700 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics Lexan® 201 PC 7.0 MFR, for thicker sections without sinks. Improved flame retardance. |
|||
Flexural Yield Strength | 81.0 MPa | 11700 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics Lexan® 201 PC (Asia Pacific) 7.0 MFR, for thicker sections without sinks. Improved flame retardance. |
|||
Flexural Yield Strength | 81.0 MPa | 11700 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics Lexan® EM1210 PC Automotive interiors. Excellent heat/impact resistance and outstanding property retention over wide temperature range/severe automotive conditions |
|||
Flexural Yield Strength | 81.0 MPa | 11700 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics Lexan® EM1210 PC (Asia Pacific) Automotive interiors. Excellent heat/impact resistance and outstanding property retention over wide temperature range/severe automotive conditions |
|||
Flexural Yield Strength | 81.0 MPa | 11700 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics Lexan® EM3110 PC Automotive interiors. Optimizes flow/processability for cost effective thinner wall design uses. |
|||
Flexural Yield Strength | 81.0 MPa | 11700 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics Lexan® EM3110 PC (Asia Pacific) Automotive interiors. Optimizes flow/processability for cost effective thinner wall design uses. |
|||
Flexural Yield Strength | 81.0 - 195 MPa | 11700 - 28300 psi | Average value: 124 MPa Grade Count:11 |
Overview of materials for PET + PBT Unreinforced This property data is a summary of similar materials in the MatWeb database for the category "PET + PBT Unreinforced". Each property range of values reported is minimum and maximum values of appropr.. |
|||
Flexural Yield Strength | 81.0 MPa | 11700 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics Cycolac® BDT5510 ABS Automotive. High heat resistance, low gloss, color concentratable for interior applications. Natural only. |
|||
Flexural Yield Strength | 80.4 MPa @Thickness 3.20 mm |
11700 psi @Thickness 0.126 in |
15mm/min; ASTM D790 |
LG Chemical LI970HF Co-Extrusion ASA Description: Good Weatherability, Scratch Resistance, High FlowApplication: Window Profile, Siding, Rain GutterCAS: 26299-47-8Information provided by LG Chemical |
|||
Flexural Yield Strength | 80.4 MPa @Thickness 3.20 mm |
11700 psi @Thickness 0.126 in |
15 mm/min; ASTM D790 |
LG Chemical RS650 ABS Feature: Extrusion Molding, General PurposeApplication: MiscellaneousCAS No. 9003-56-9Information provided by LG Chemical |
|||
Flexural Yield Strength | 80.4 MPa @Thickness 3.20 mm |
11700 psi @Thickness 0.126 in |
15 mm/min; ASTM D790 |
LG Chemical RS657 ABS, Chemical Resistance to Cyclopentane Feature: Extrusion Molding, Chemical Resistance to Cyclopentane, Thin ThicknessApplication: Refrigerator Inner LinerCAS No. 9003-56-9Information provided by LG Chemical |
|||
Flexural Yield Strength | 81.0 MPa | 11700 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP ZL003 PPE+PS (Europe-Africa-Middle East) LNP* LUBRICOMP* ZL003 is a compound based on PPE+PS Blend resin containing PTFE. Added features include Internally Lubricated. |
|||
Flexural Yield Strength | 81.0 MPa | 11700 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Valox® 175 PBT Unreinforced, neat PBT resin for compounding only. Natural Color Only, Not intended for injection molding.This data was supplied by SABIC-IP for the Americas region. |
|||
Flexural Yield Strength | 81.0 MPa | 11700 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Valox® 175 PBT (Europe-Africa-Middle East) Unreinforced, neat PBT resin for compounding only. Natural Color Only, Not intended for injection molding. |
|||
Flexural Yield Strength | 81.0 MPa | 11700 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Valox® 176 PBT Unreinforced, neat PBT resin for fibers. Natural Color Only, Not intended for injection molding. |
|||
Flexural Yield Strength | 81.0 MPa | 11700 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Valox® 176HP PBT Unreinforced, FDA compliant neat PBT resin for fibers. Natural Color Only, Not intended for injection molding. |
|||
Flexural Yield Strength | 81.0 MPa | 11700 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP 67001XXH PBT+PC LNP* THERMOCOMP* 67001XXH is a compound based on PC + PBT resin containing proprietary antimicrobial additives. Designed for touch surfaces in patient critical healthcare applications. Added featu.. |
|||
Flexural Yield Strength | 80.4 MPa | 11700 psi | ASTM D790 |
Samyang Tribit® 1501N PBT, Flame Retardancy Crystallization is fast, formability is excellent and thermal resistance, chemical resistance, electrical properties and abrasion resistance are excellent.1501N is a V-2 flame retardancy grade.Appli.. |
|||
Flexural Yield Strength | 80.4 MPa | 11700 psi | ASTM D790 |
Samyang Trirex® 3015NF Polycarbonate, Flame Retardancy PC is characterized by its excellent impact resistance, dimensional stability and excellent thermal resistance.3015NF is a flame retardant grade.Applications: Mobile Phone - battery caseInformation.. |
|||
Flexural Yield Strength | 81.0 MPa | 11700 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP Thermocomp WB006 PBT (Europe-Africa-Middle East) LNP* THERMOCOMP* WB006 is a compound based on Polybutylene Terephalate resin containing Glass Bead.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region. |
|||
Flexural Yield Strength | 81.0 MPa | 11700 psi | ASTM D790 |
Toyobo Vylopet® EMC605 PET/PBT Blend Key Feature: Flame retardant V-0 UL 94 classApplications: glossy surface componentsPET/PBT blends suggested for glossy surfaces. General features of Vylopet® include heat resistance, good mechanic.. |
|||
Flexural Yield Strength | 81.0 MPa | 11700 psi | ISO 178 |
Eastman Eastar AN004 Natural PCTA Copolyester EASTAR AN004 Copolyester contains a mold release. It has excellent appearance and is nearly water-clear. Its most outstanding features are its chemical resistance and processing capabilities. Exp.. |
|||
Flexural Yield Strength | 81.0 MPa | 11700 psi | ASTM D790 |
Eastman Eastar MN052 Polyester, Natural Eastar polyester MN052 is a thermoplastic condensation homopolymer produced by a continuous melt-phase polymerization process followed by a solid-state polymerization process. It has been crystalliz.. |
|||
Flexural Yield Strength | 80.6 MPa | 11700 psi | chs 0.05 in/min; ASTM D790 |
Diamond Polymers DIAMALOY 1418 Polycarbonate/Polyester Alloy Information Provided by Diamond Polymers, Inc. & Network Polymers, Inc. |
|||
Flexural Yield Strength | 81.0 MPa | 11700 psi | ASTM D790 |
Chang Chun Plastic Longlite PM T308J General Purpose Phenolic Molding Compound ASTM Grade per ASTM D700 is 3.Information provided by Dowell Trading Company Ltd. |
|||
Flexural Yield Strength | 80.4 MPa @Thickness 6.40 mm |
11700 psi @Thickness 0.252 in |
ASTM D-790 |
Bhansali Engineering Abstron IMG-1115 Glass Reinforced Grade Glass Reinforced ABS & SAN Resins for product specific requirement of very high rigidity and temperatureInformation provided by Bhansali |
|||
Flexural Yield Strength | 80.4 MPa @Thickness 6.40 mm |
11700 psi @Thickness 0.252 in |
5 mm/min; ASTM D790 |
Bhansali Engineering Abstron IM14GL ABS Injection Molding Grade Super High Rigidity, Medium Impact, High Chemical ResistanceInformation provided by Bhansali |