Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Yield Strength | 38.0 MPa | 5510 psi | ASTM D790 |
Nylene® 401, Nylon 6, at 50% Relative Humidity Injection molding grade. Nylene 401 is recommended for general purpose nylon molding applications in both thin and heavy sections. Nylene 401 has high flow characteristics at minimal processing temp.. |
|||
Flexural Yield Strength | 38.0 MPa | 5510 psi | ASTM D790 |
Nylene® 404 Nylon 6, 50% RH Injection molding grade. Nylene 404 is a heat stabilized version of 401 which is recommended for general purpose nylon molding applications in both thin and heavy sections. In addition to protection.. |
|||
Flexural Yield Strength | 38.0 MPa | 5510 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Cycolac® INPBMAT ABS Cross-linked SAN in styrenic matrix. Provides excellent gloss reduction properties. Maintains original polymer properties such as impact etc. Compatible with various polymer such as PVC and ABS. C.. |
|||
Flexural Yield Strength | 38.0 MPa | 5510 psi | ASTM D790 |
North Wood Plastics 60 HDPE + UNIFILL (20% Wood Fiber) Data provided by North Wood Plastics, Inc. UNIFILL-60 is a general purpose polyolefin compound compatible in both PP and HDPE. It is a masterbatch with 60% high quality pine wood flour filler. It.. |
|||
Flexural Yield Strength | 38.0 MPa | 5510 psi | ASTM D790 |
North Wood Plastics 60 PP + UNIFILL (20% Wood Fiber) Data provided by North Wood Plastics, Inc. UNIFILL-60 is a general purpose polyolefin compound compatible in both PP and HDPE. It is a masterbatch with 60% high quality pine wood flour filler. It.. |
|||
Flexural Yield Strength | 38.0 - 285 MPa | 5510 - 41300 psi | Average value: 161 MPa Grade Count:54 |
Overview of materials for Acetal Copolymer, 30% Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Acetal Copolymer, 30% Glass Fiber Reinforced". Specific grades with glass content between 25% and 34% ar.. |
|||
Flexural Yield Strength | 38.0 MPa | 5510 psi | ASTM D790 |
PolyOne Lubri-Tech™ AT-15GP/05T Acetal With Graphite - 5% PTFE
(discontinued **) Data provided by PolyOne. |
|||
Flexural Yield Strength | 38.0 - 110 MPa @Temperature -40.0 - 80.0 °C |
5510 - 16000 psi @Temperature -40.0 - 176 °F |
Average value: 75.5 MPa Grade Count:1 |
Overview of materials for Nylon 6, 20% Mineral Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, 20% Mineral Filled". Specific grades with primary filler content between 15% and 24% are includ.. |
|||
Flexural Yield Strength | 38.0 - 140 MPa @Temperature -40.0 - 80.0 °C |
5510 - 20300 psi @Temperature -40.0 - 176 °F |
Average value: 86.8 MPa Grade Count:2 |
Overview of materials for Nylon 66, Unreinforced, Flame Retardant This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, Unreinforced, Flame Retardant". Each property range of values reported is minimum and maximum .. |
|||
Flexural Yield Strength | 38.0 MPa | 5510 psi | ASTM D790 |
Tipco Tipcolene® FPW 10 PPC - 10% Wollastonite Reinforced Polypropylene Copolymer, High Impact Strength 10% Wollastonite Reinforced PP CopolymerApplications: Automotive & AppliancesProcessing: Injection MoldingInformation provided by the Manufacturer, Tipco Industries Ltd.,
India. |
|||
Flexural Yield Strength | 38.0 MPa | 5510 psi | ASTM D790 |
Covestro Baydur® 730 IBS Polyurethane Structural Foam RIM, Density 40 pcf, MDI-based 2-Component Liquid System 0.25 in. thickness. IBS = Interactive Blowing System RIM = Reaction Injection MoldingInformation provided by Bayer Corporation, Polyurethanes DivisionAs of 1 September 2015, Bayer MaterialScience .. |
|||
Flexural Yield Strength | 38.0 MPa | 5510 psi | ASTM D790 |
Bulk Molding Compounds BMC 940 Vinyl Ester Bipolar Plate Material Product Introduction: Bulk Molding Compounds, Inc. is the largest manufacturer of thermoset bulk molding compounds in North America, serving the automotive, appliance, and electrical markets. BMC t.. |
|||
Flexural Yield Strength | 38.0 - 142 MPa | 5510 - 20600 psi | Average value: 92.7 MPa Grade Count:29 |
Overview of materials for Acrylic, Extruded This property data is a summary of similar materials in the MatWeb database for the category "Acrylic, Extruded". Each property range of values reported is minimum and maximum values of appropriate .. |
|||
Flexural Yield Strength | 38.0 - 103 MPa | 5510 - 15000 psi | Average value: 57.6 MPa Grade Count:19 |
Overview of materials for Polypropylene, Wood Filled This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene, Wood Filled". Each property range of values reported is minimum and maximum values of app.. |