North Wood Plastics 60 HDPE + UNIFILL (20% Wood Fiber)

Category	Polymer , Renewable/Recycled Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Wood Filled
Manufacturer	North Wood Plastics
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	North Wood Plastics 60 HDPE + UNIFILL (20% Wood Fiber).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Data provided by North Wood Plastics, Inc. UNIFILL-60 is a general purpose polyolefin compound compatible in both PP and HDPE. It is a masterbatch with 60% high quality pine wood flour filler. It is made with only the highest quality recycled resins. 2:1 HDPE:UNIFILL-60 yields an end product with 20% fiber.

Physical Properties	Metric	English	Comments
Density	0.994 g/cc	0.0359 lb/in³	ASTM D792
Linear Mold Shrinkage	0.012 cm/cm	0.012 in/in	ASTM D955
Melt Flow	2.0 g/10 min @Temperature 190 °C	2.0 g/10 min @Temperature 374 °F

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	15.0 MPa	2180 psi	ASTM D638
Elongation at Break	15 %	15 %	ASTM D638
Tensile Modulus	1.80 GPa	261 ksi	ASTM D638
Flexural Yield Strength	38.0 MPa	5510 psi	ASTM D790
Flexural Modulus	1.20 GPa	174 ksi	ASTM D790
Izod Impact, Notched	0.430 J/cm	0.806 ft-lb/in	ASTM D256
Izod Impact, Unnotched	2.40 J/cm	4.50 ft-lb/in	ASTM D256

Thermal Properties	Metric	English	Comments
Deflection Temperature at 1.8 MPa (264 psi)	43.0 °C	109 °F	ASTM D648

Processing Properties	Metric	English	Comments
Processing Temperature	<= 200 °C	<= 392 °F	To prevent fiber degradation.