Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Yield Strength | 35.0 MPa @Temperature 90.0 °C |
5080 psi @Temperature 194 °F |
ISO 178, ASTM D790 |
Nilit Nilitop BT FR C3 Unfilled, Flame Retardant PBT Description: Nilitop BT FR C3 is an unfilled, flame retardant PBT with halogens. The flame retardant does not contain PBB and PBDE, so it is compliant with the WEEE directive.Key characteristics: Go.. |
|||
Flexural Yield Strength | 35.0 MPa | 5080 psi | ASTM D790 |
North Wood Plastics HDPE with 40% Wood Fiber Data provided by North Wood Plastics, Inc. |
|||
Flexural Yield Strength | 35.0 - 35.0 MPa @Temperature 90.0 - 90.0 °C |
5080 - 5080 psi @Temperature 194 - 194 °F |
Average value: 35.0 MPa Grade Count:1 |
Overview of materials for Polybutylene Terephthalate (PBT), Flame Retardant This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), Flame Retardant". Each property range of values reported is minimum an.. |
|||
Flexural Yield Strength | 35.0 MPa @Temperature 90.0 °C |
5080 psi @Temperature 194 °F |
ISO 178, ASTM D790 |
Nilit Nilamid A3 N H2 Nucleated, Heat Stabilized Nylon 66 Description: Nilamid A3 N H2 is a nucleated, heat stabilized NYLON 66 with excellent flow characteristics and very fast cycle time. It is widely used throughout many industries for mass production a.. |
|||
Flexural Yield Strength | 35.0 MPa | 5080 psi | DIN 53452 |
Ineos Nova S-4600 High Impact Compact Polystyrene
(discontinued **) High impact polystyrene with excellent flow characteristics, a very high toughness and a high elongation. Main application are injection molding of technical parts and housings. For injection mold.. |
|||
Flexural Yield Strength | <= 35.0 MPa | <= 5080 psi | ASTM D790 |
3M Dyneon™ CC144/S PTFE, 40% Bronze Filled
(discontinued **) Product Form: Brown, non-pelletized powder. Applications include bearings, rider rings, and piston rings.Data provided by Dyneon. |
|||
Flexural Yield Strength | 35.0 - 35.0 MPa @Temperature 90.0 - 90.0 °C |
5080 - 5080 psi @Temperature 194 - 194 °F |
Average value: 35.0 MPa Grade Count:1 |
Overview of materials for Nylon 66, Heat Stabilized This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, Heat Stabilized". Each property range of values reported is minimum and maximum values of appr.. |
|||
Flexural Yield Strength | 35.0 MPa | 5080 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP STAT-KON FX91304 PE LNP* STAT-KON* FX91304 is a compound based on Polyethylene resin containing Proprietary Filler(s). Added feature of this grade is: Electrically Conductive. |
|||
Flexural Yield Strength | 35.0 MPa | 5080 psi | ASTM D790 |
Tipco Tipcolene® NPI 200 IN - 25% Talc/Mineral Reinforced Polypropylene Copolymer with Very High Flow, Stiffness & Impact Strength 20% Mineral Reinforced, Very High Stiffness & Very High Impact PP CopolymerApplications: Automotive DashboardsProcessing: Injection MoldingInformation provided by the Manufacturer, Tipco Industries .. |
|||
Flexural Yield Strength | 35.0 MPa | 5080 psi | 2 mm/min; ISO 178 |
Eurostar Starpylen MX06023 PP, 20% Milled Glass Fiber Filled, Injection Molded Starpylen MX06023 is a 20% Milled Glass Fiber Reinforced Polypropylene Injection Molding ResinInformation provided by Eurostar. |
|||
Flexural Yield Strength | 35.0 - 138 MPa | 5080 - 20000 psi | Average value: 110 MPa Grade Count:15 |
Overview of materials for Nylon 66, Nucleated This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, Nucleated". Each property range of values reported is minimum and maximum values of appropriat.. |
|||
Flexural Yield Strength | 35.0 MPa | 5080 psi | ASTM D790 |
Ineos Nova 5711 High Impact Polystyrene
(discontinued **) High flow, High impact, USP Class VIApplications: Thin wall, Medical, Housewares, ToysProperties were determined on injection molded specimens at 23°C and 50% R.H. unless otherwise specified.Inform.. |