Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Yield Strength | 186 MPa | 27000 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics Lexan® 3414R PC 40% GR, provides improved mechanical properties and UL94V-1 rated at 0.058"". Internal mold release added. |
|||
Flexural Yield Strength | 186 - 894 MPa | 27000 - 130000 psi | Average value: 311 MPa Grade Count:19 |
Overview of materials for Polyaryletherketone (PAEK), Carbon Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyaryletherketone (PAEK), Carbon Fiber Filled". Each property range of values reported is minimum and .. |
|||
Flexural Yield Strength | 186 - 276 MPa | 27000 - 40000 psi | Average value: 225 MPa Grade Count:7 |
Overview of materials for Nylon 11 + Carbon Fiber This property data is a summary of similar materials in the MatWeb database for the category "Nylon 11 + Carbon Fiber". Each property range of values reported is minimum and maximum values of approp.. |
|||
Flexural Yield Strength | 186 MPa @Thickness 3.20 mm |
27000 psi @Thickness 0.126 in |
1.3mm/min; ASTM D790 |
LG Chemical LUMID LW4303B(W) PA66+MF30%, Low Warpage Feature: Injection Molding, PA66+MF30%, Low WarpageApplication: Automotive PartsCAS No. 32131-17-2, 13983-17-0 and 65997-17-3Information provided by LG Chemical |
|||
Flexural Yield Strength | 186 MPa @Thickness 3.20 mm |
27000 psi @Thickness 0.126 in |
1.3mm/min; ASTM D790 |
LG Chemical Lupox® GP2306FB PBT+GF30% Description: Injection Molding, PBT+GF30%, Flame Retardant Application: IT/OA, E&E (Connector)CAS No. 68928-70-1, 65997-17-3, 24968-12-5, 25038-59-9 and 1309-64-4Information provided by LG Chemical |
|||
Flexural Yield Strength | 186 MPa @Thickness 3.20 mm |
27000 psi @Thickness 0.126 in |
1.3mm/min; ASTM D790 |
LG Chemical Lupox® GP2306FS PBT+GF30% Description: Injection Molding, PBT+GF30%, Flame Retardant, Anti-Hydrolysis Application: IT/OA, E&E (Connector)CAS No. 68928-70-1, 65997-17-3, 24968-12-5 and 1309-64-4Information provided by LG Chem.. |
|||
Flexural Yield Strength | 186 MPa | 27000 psi | ASTM D570 |
LG Chemical Lupox® PBT-GP-2306F 30% GFR Flame Retardant PBT Information provided by US distributor Polymer Technology and Services, LLC (PTS). |
|||
Flexural Yield Strength | 186 MPa | 27000 psi | DIN 53455; ASTM D790 |
Kolon KOPA® KN133G15 G/F Reinforced Nylon 6 KOPA® is a thermoplastic resin with excellent mechanical, thermal and electrical properties and is widely used in automobile and industrial parts.Good mechanical properties, outstanding self-lubr.. |
|||
Flexural Yield Strength | 186 MPa | 27000 psi | ASTM D790 |
Techmer ES HiFill® PA4/6 GF30 HS BK 30% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 30% Filler by WeightAdditive: Heat StabilizerFeatures: Heat StabilizedUL File Number: E157318Appearance: Bla.. |
|||
Flexural Yield Strength | 186 MPa | 27000 psi | ASTM D790 |
Shinkong Synthetic Fibers Shinite® T102G30 PET, 30% Glass Filled, Fire Retardant Information from Shinkong Synthetic Fibers Corp. |
|||
Flexural Yield Strength | 186 MPa | 27000 psi | ASTM D790 |
Techmer ES HiFill® PVDF CF15 BK 15% Carbon Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Carbon Fiber Reinforcement, 15% Filler by WeightAppearance: BlackInformation provided by TP Composites, Inc. |
|||
Flexural Yield Strength | 186 MPa | 27000 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP DF006 PC (Europe-Africa-Middle East) LNP* Thermocomp* DF1006 is a compound based on Polycarbonate resin containing Glass Fiber. |
|||
Flexural Yield Strength | 186 MPa | 27000 psi | ASTM D790 |
Techmer ES Plaslube® J-50/30/TF/10 Polycarbonate, 30% GFR, 10% PTFE Plaslube glass fiber reinforced polytetrafluorethylene (PTFE) lubricated polycarbonate grades have an excellent balance of mechanical strength characteristics, dimensional stability and wear and fri.. |
|||
Flexural Yield Strength | 186 MPa | 27000 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP RFB53XXZ PA 66 LNP* THERMOCOMP* RFB53XXZ is a compound based on Nylon 66 resin containing 15% Glass Fiber, 25% Glass Bead. |
|||
Flexural Yield Strength | 186 MPa | 27000 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP WF007 PBT LNP THERMOCOMP WF007 is a compound based on PBT resin containing 35% Glass Fiber. |
|||
Flexural Yield Strength | 186 MPa | 27000 psi | ASTM D790 |
Techmer ES HiFill® PA4/6 GF30 HS NAT 30% Glass Filled (Conditioned) Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 30% Filler by WeightAdditive: Heat StabilizerFeatures: Heat StabilizedAppearance: Natural ColorInformation p.. |
|||
Flexural Yield Strength | 186 MPa | 27000 psi | ASTM D790 |
Westlake Plastics Zelux® 40% GF Polycarbonate 40% Glass Filled Zelux polycarbonate is a transparent engineering plastic with excellent dimensional stability and good mechanical and electrical properties. It is used for structural applications when clarity and .. |