Total PPC 4280W Polypropylene, Impact Copolymer

Category	Polymer , Thermoplastic , Polypropylene (PP)
Manufacturer	Total Atofina
Trade Name	PPC
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Total PPC 4280W Polypropylene, Impact Copolymer.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

ATOFINA 4280W polypropylene is a nucleated impact copolymer. 4280W has a low fluidity providing melt strength with excellent impact properties. It is nucleated for added stiffness and surface hardness. ApplicationATOFINA 4280W is designed to be particularly suited for profile and sheet extrusion, extrusion-thermoforming and heavy-duty injection molded applications. Information provided provided by Total Petrochemicals.Total Petrochemicals acquired former Fina and Atofina plastics product lines.

Physical Properties	Metric	English	Comments
Density	0.905 g/cc	0.0327 lb/in³	ASTM D1505
Melt Flow	1.3 g/10 min	1.3 g/10 min	ASTM D1238

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	24.8 MPa	3600 psi	ASTM D638
Elongation at Yield	7.0 %	7.0 %	ASTM D638
Flexural Modulus	1.31 GPa	190 ksi	ASTM D 790
Izod Impact, Notched	NB	NB	ASTM D256
	0.700 J/cm @Temperature -20.0 °C	1.31 ft-lb/in @Temperature -4.00 °F	ASTM D256
Charpy Impact Unnotched	0.800 J/cm² @Temperature -20.0 °C	3.81 ft-lb/in² @Temperature -4.00 °F	ASTM DIN53453
	NB @Temperature 23.0 °C	NB @Temperature 73.4 °F	ASTM DIN53453

Thermal Properties	Metric	English	Comments
Melting Point	160 - 165 °C	320 - 329 °F	ATOFINA Method
Deflection Temperature at 0.46 MPa (66 psi)	93.0 °C	199 °F	ASTM D648
Vicat Softening Point	152 °C	306 °F	ASTM D1525