- Inno-Comp INNOPOL® CS 2-2120 17TOP BU UV-Stabilized 17% Talc-Filled Polypropylene Block-Copolymer
Inno-Comp INNOPOL® CS 2-2120 17TOP BU UV-Stabilized 17% Talc-Filled Polypropylene Block-Copolymer
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 20% Talc Filler |
| Manufacturer | Inno-Comp Ltd |
| Trade Name | INNOPOL® CS |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Inno-Comp INNOPOL® CS 2-2120 17TOP BU UV-Stabilized 17% Talc-Filled Polypropylene Block-Copolymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
INNOPOL® CS 2-2120 17TOP BU is a black colored, 17% talc-filled, UV stabilized compound based on polypropylene block-copolymer.INNOPOL® CS 2-2120 17TOP BU is developed for producing injection molded automotive components.All information provided by INNO-COMP.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.01 g/cc @Temperature 23.0 °C |
0.0365 lb/in³ @Temperature 73.4 °F |
ISO 1183 |
| Melt Flow | 22 g/10 min @Load 2.16 kg, Temperature 230 °C |
22 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
| Ash | 15 - 17 % @Temperature 600 °C |
15 - 17 % @Temperature 1110 °F |
ISO 3451-1/A |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 20.0 MPa | 2900 psi | 50 mm/min; ISO 527-1,-2 |
| Elongation at Yield | 5.5 % | 5.5 % | 50 mm/min; ISO 527-1,-2 |
| Tensile Modulus | 1.45 GPa | 210 ksi | 1 mm/min; ISO 527-1,-2 |
| Flexural Modulus | 1.55 GPa | 225 ksi | 2 mm/min; ISO 178 |
| Charpy Impact Unnotched | 12.0 J/cm² @Temperature -20.0 °C |
57.1 ft-lb/in² @Temperature -4.00 °F |
ISO 179/1eU |
| NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 0.650 J/cm² @Temperature -20.0 °C |
3.09 ft-lb/in² @Temperature -4.00 °F |
ISO 179/1eA |
| 3.00 J/cm² @Temperature 23.0 °C |
14.3 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 100 °C | 212 °F | ISO 75-1,-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 62.0 °C | 144 °F | ISO 75-1,-2 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Black |
Users viewing this material also viewed the following:
- MV Labs TB400 TbCl3·6H2O Terbium chloride hexahydrate
- Niche Polymer PA66HIN Nylon 66, High Impact
- NOVA Chemicals Sclair® 2315 LLDPE Injection Molding Resin (discontinued **)
- NOVA Chemicals Novapol® LF-Y819-A LDPE Film Resin
- Lord Adhesives Thermosetâ„¢ EP-809 Ignition Coil Impregnating and Encapsulation Epoxy
- Sylvin Technologies 8980-90 Natural PVC Extrusion Compound
- Shin-Etsu Silicones MK15H Fluid
- EMS-Grivory Grivory® XE 4101 black 9225 PA*-GF40
- Eagle Brass 304 Austenitic Stainless Steel, Full Hardened
- Abatron AboWeld 48-8/AboCure 48-8 Adhesive/Casting Resin
Copyright © lookpolymers.com All Rights Reserved