Lucent Polymers TPO-1015 Thermoplastic Polyolefin
| Category | Polymer , Thermoplastic , Polyolefin |
| Manufacturer | Lucent Polymers |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lucent Polymers TPO-1015 Thermoplastic Polyolefin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Melt Flow Adjustable for ApplicationAdd "U" for UV StabilizedAdd "H" for Heat StabilizedInformation provided by Lucent Polymers, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.910 g/cc | 0.910 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.016 cm/cm @Thickness 3.17 mm |
0.016 in/in @Thickness 0.125 in |
1/8" Section |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 20.0 MPa | 2900 psi | ASTM D638 |
| Elongation at Break | >= 100 % | >= 100 % | ASTM D638 |
| Flexural Strength | 28.0 MPa | 4060 psi | ASTM D790 |
| Flexural Modulus | 0.621 GPa | 90.1 ksi | ASTM D790 |
| Izod Impact, Notched | 9.99 J/cm @Thickness 3.17 mm |
18.7 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 38.0 °C | 100 °F | ASTM D648 |
Users viewing this material also viewed the following:
- DuPont Performance Polymers Hypalon® 45 Chlorosulfonated Polyethylene Rubber, Mineral Filled Compound (discon
- Eastman 9921P PET Injection Molded (discontinued **)
- Kingfa JH960 6300 Non-halogenated Flame Retardant PC/ABS Alloy
- Supreme Petrochem SP 515 Flame Retardant Polystyrene
- UBE UBESTA® 3030U Nylon 12 (After Methyl Ethyl Ketone for 500 hours)
- ExxonMobil LD 306.38 High Clarity, High Impact Film Resin
- 3M 5498 PTFE Film Tape
- Haynes Hastelloy® G-35® Nickel Alloy Bar, Annealed at 2075°F (1135°C)
Copyright © lookpolymers.com All Rights Reserved