Polymer Property : Tensile Strength, Yield = 1520 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	10.5 MPa	1520 psi	ASTM D412
Polymax® Maxelast® F02-081A-6C TPE, Halogen Free Extrusion Grade Characteristics: Good melt strengthSoft touchSmooth surface with dry feelGood weather and heat resistanceWide range of hardnessEasy processing Halogen FreeLow smoke emissionRoHs compliantDesigned to..
Tensile Strength, Yield	10.5 MPa	1520 psi	ASTM D412
Precision Polymer Engineering E60E Ethylene Propylene Rubber Ethylene Propylene Terpolymer, 56-65 °IRHD. Terpolymer of ethylene, propylene and diene monomers. To meet Aerospace Specification DTD5597A Grade 60.Applications: For sealing applications where goo..
Tensile Strength, Yield	10.5 MPa	1520 psi	5% change after 70 hours @ 100°C; ASTM D412
Precision Polymer Engineering E70B Ethylene Propylene Rubber General purpose, Ethylene Propylene Rubber, 65-75 °IRHD. Terpolymer of ethylene, propylene and diene monomers.Applications: Excellent water and steam resistance with good compression set propertie..
Tensile Strength, Yield	10.5 MPa	1520 psi	5% change after 70 hours @ 100°C; ASTM D412
Precision Polymer Engineering N70H Nitrile Rubber Nitrile Butadiene Rubber (NBR), 65-75 °IRHD. High acrylonitrile (ACN) content. Copolymer of acrylonitrile and butadiene.Applications: The high acrylonitrile content of this rubber increases resist..
Tensile Strength, Yield	10.5 MPa	1520 psi	ASTM D412
Precision Polymer Engineering N70N Nitrile Rubber Nitrile Butadiene Rubber (NBR) 66-75 °IRHD. Copolymer of acrylonitrile and butadiene. To meet Aerospace Material Specification DTD5595A Grade 70.Applications: Synthetic rubber resistant to petrole..
Tensile Strength, Yield	10.5 MPa	1520 psi	-25% change after 72 hours @ 250°C; ASTM D412
Precision Polymer Engineering V75F Fluoroelastomer Compound Special steam resistant, Fluoroelastomer Rubber, 70-80 °IRHD. Tetrapolymer of vinylidene fluoride, hexafluoropropylene and tetrafluoroethylene and cure site monomer (CSM). To meet ASTM D2000 line..
Tensile Strength, Yield	10.5 MPa	1520 psi	ASTM D412
Precision Polymer Engineering V75L Fluoroelastomer Compound Special, steam-resistant Fluoroelastomer Rubber, 70-80 °IRHD. Copolymer of vinylidene fluoride and hexafluoropropylene. To meet ASTM D2000 line call-out:- M2HK710, A1-10, B38, EF31, EO78, F15, Z1...
Tensile Strength, Yield	10.5 MPa	1520 psi	-25% change after 72 hours @ 250°C; ASTM D412
Precision Polymer Engineering V80B Fluoroelastomer Compound Fluoroelastomer Rubber, 76-85 °IRHD. Copolymer of vinylidene fluoride and hexafluoropropylene. To meet ASTM D2000 line call-out: M2HK814, A1-10, B37, B38, EF31, EO78, F15, Z1. Where Z1 = compressi..
Tensile Strength, Yield	10.5 MPa	1520 psi	-25% change after 72 hours @ 250°C; ASTM D412
Precision Polymer Engineering V85F Fluoroelastomer Compound Special steam resistant, Fluoroelastomer Rubber, 80-90 °IRHD. Tetrapolymer of vinylidene fluoride, hexafluoropropylene and tetrafluoroethylene and cure site monomer (CSM). To meet ASTM D2000 line c..
Tensile Strength, Yield	10.5 MPa	1520 psi	-25% change after 72 hours @ 250°C; ASTM D412
Precision Polymer Engineering V90G Fluoroelastomer Compound Green Fluoroelastomer Rubber, 85-95 °IRHD. Copolymer of vinylidene fluoride and hexafluoropropylene. To meet ASTM D2000 line call-out: M3HK914, A1-10, B38, EF31, EO78, Z1, Z2. Z1 = colour green, ..
Tensile Strength, Yield	10.5 MPa	1520 psi	-25% change after 72 hours @ 250°C; ASTM D412
Precision Polymer Engineering V90M Fluoroelastomer Compound Brown Fluoroelastomer Rubber, 85-95 °IRHD. Copolymer of vinylidene fluoride and hexafluoropropylene. To meet ASTM D2000 line call-out: M3HK914, A1-10, B38, EF31, EO78, Z1, Z2, where Z1 = Brown and..
Tensile Strength, Yield	10.5 MPa	1520 psi	-25% change after 70 hours @ 150°C; ASTM D412
Precision Polymer Engineering Z60B Hydrogenated NBR Compound Hydrogenated Nitrile Rubber, 55-65 °IRHD. Medium acrylonitrile (ACN) content. ASTM designation = HNBR. ASTM D2000 line call-out 2MDH614, A26, B36, EO16, EO36, F14.Applications: High strength and ..
Tensile Strength, Yield	10.5 MPa	1520 psi	ASTM D412
Polymax® Maxelast® P1890 TPE, PP Overmold or Standalone use Polymax's TPE material complies with UL, VDE, FDA, RoHS and PAH's standards.Uses:Consumer ProductsToys & NoveltiesAuto PartsTool Hand GripsSporting GoodsWire & Cable ElectronicsMedical DevicesPlasti..
Tensile Strength, Yield	>= 10.5 MPa	>= 1520 psi
Kazanorgsintez M 115 SV Polymer Composition for Rotary Molding Production Method: Composition is produced on the basis of 11503-070 grade low density polyethylene and 276-03 grade high density polyethylene composition. Application: Compositions are designed..
Tensile Strength, Yield	>= 10.5 MPa	>= 1520 psi	Cable at 100°C, 10 days; ASTM D638
Borealis Casico™ FR4803 Non-Halogen Flame Retardant Compound for Low Voltage Insulation and Jacketing Borstar FR4803 is a natural, thermoplastic polyolefin compound designed for flame retardant low voltage wire insulation and jacketing. As such, FR4803 offers a unique combination of good extrusion p..
Tensile Strength, Yield	10.5 MPa	1520 psi
Trelleborg P600 Epichlorohydrin There are three types of epichlorohydrin:1. Homopolymers of epichlorohydrin. Designated CO.2. Chopolymers of epichlorohydrin and etylene oxide. Designated ECO.Terpolymers of epichlorohydrin, etylene..
Tensile Strength, Yield	10.5 MPa	1520 psi
Trelleborg P650 Epichlorohydrin There are three types of epichlorohydrin:1. Homopolymers of epichlorohydrin. Designated CO.2. Chopolymers of epichlorohydrin and etylene oxide. Designated ECO.Terpolymers of epichlorohydrin, etylene..
Tensile Strength, Yield	>= 10.5 MPa	>= 1520 psi	Cable at 100°C, 10 days; ASTM D638
Borealis Casico™ FR4802 Non-Halogen Flame Retardant Insulation/Jacketing Compound Borstar FR4802 is a natural, thermoplastic polyolefin compound designed for flame retardant low voltage wire insulation and jacketing. As such, FR4802 offers a unique combination of good extrusion p..
Tensile Strength, Yield	10.5 MPa	1520 psi
Dow DOWLEX™ 2507 Linear Low Density Polyethylene, Narrow MW Distribution DOWLEX® 2507 Polyethylene resin is a narrow molecular weight distribution copolymer designed for fast injection molding of thin wall lids without warping. It has demonstrated excellent processabili..
Tensile Strength, Yield	10.5 MPa @Strain 300 %	1520 psi @Strain 300 %	ASTM D412
Dow SE SLR-4630 Solution polymerized Styrene Butadiene Rubber (S-SBR) SE SLR-4630 is manufactured by anionic solution polymerization using lithium initiator and is extended with 37.5 parts of TDAE oil in relation to solid rubber. It is a product with medium styrene a..
Tensile Strength, Yield	10.5 MPa	1520 psi	ISO 527-2
Carmel Olefins IPETHENE® 670 Low Density Polyethylene IPETHENE® 670 is a low density polyethylene extrusion coating and lamination grade. This grade can be processed at high coating temperatures and coating speeds. It exhibits low neck-in and stable w..
Tensile Strength, Yield	10.5 MPa	1520 psi	ISO 527-2
Carmel Olefins IPETHENE® 810 Low Density Polyethylene IPETHENE® 810 is a low density polyethylene injection molding grade. It exhibits high melt flow rate, high gloss, and high stiffness. APPLICATIONS IPETHENE® 810 is used to produce lids, containe..
Tensile Strength, Yield	10.5 MPa	1520 psi	ISO 527-2
Carmel Olefins IPETHENE® 470 Low Density Polyethylene IPETHENE® 470 is a low density polyethylene extrusion coating and lamination grade. This grade can be processed at high coating temperatures and coating speeds. It exhibits low neck-in and stable w..
Tensile Strength, Yield	10.5 MPa	1520 psi	ASTM D638
Reliance Industries Reclair M24300 Polyethylene High flow Linear Low Density Polyethylene grade. Reclair M24300 is butene comonomer based, with optimum levels of antioxidants.Characteristics:narrow molecular weight distribution, good fluidity, ..