Physical Properties | Metric | English | Comments |
---|---|---|---|
Density | 0.930 g/cc | 0.0336 lb/in³ | |
Viscosity | 23000 cP @Shear Rate 5000 1/s, Temperature 190 °C |
23000 cP @Shear Rate 5000 1/s, Temperature 374 °F |
Apparent Dynamic Viscosity |
50000 cP @Shear Rate 1000 1/s, Temperature 190 °C |
50000 cP @Shear Rate 1000 1/s, Temperature 374 °F |
Apparent Dynamic Viscosity | |
77000 cP @Shear Rate 300 1/s, Temperature 190 °C |
77000 cP @Shear Rate 300 1/s, Temperature 374 °F |
Apparent Dynamic Viscosity | |
Melt Flow | 150 g/10 min @Load 2.16 kg |
150 g/10 min @Load 4.76 lb |
Melt flow ratio I10/I2 is 6.5. |
Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 8.60 MPa | 1250 psi | |
Tensile Strength, Yield | 10.5 MPa | 1520 psi | |
Elongation at Break | 460 % | 460 % | |
Modulus of Elasticity | 0.268 GPa | 38.9 ksi | Molded Sample 2% Secant Modulus |
Flexural Modulus | 0.455 GPa | 66.0 ksi | |
Izod Impact, Notched (ISO) | 29.4 kJ/m² @Temperature -50.0 °C |
14.0 ft-lb/in² @Temperature -58.0 °F |
Thermal Properties | Metric | English | Comments |
---|---|---|---|
Vicat Softening Point | 96.0 °C | 205 °F |