SABIC Innovative Plastics LNP THERMOCOMP AX04518 ABS
| Category | Polymer , Thermoplastic , ABS Polymer |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP AX04518 ABS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* AX04518 is a compound based on ABS resin containing proprietary filler(s).
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.21 g/cc | 0.0437 lb/in³ | ASTM D792 |
| 1.21 g/cc | 0.0437 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.400 % | 0.400 % | 23°C / 50% RH; ISO 62 |
| 0.670 % | 0.670 % | 50% RH, 24 hrs; ASTM D570 | |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0060 cm/cm @Time 86400 sec |
0.0040 - 0.0060 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0060 - 0.0080 cm/cm @Time 86400 sec |
0.0060 - 0.0080 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 74.0 MPa | 10700 psi | 5 mm/min; ISO 527 |
| 78.0 MPa | 11300 psi | Type I, 5 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 74.0 MPa | 10700 psi | 5 mm/min; ISO 527 |
| 78.0 MPa | 11300 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 1.7 % | 1.7 % | 5 mm/min; ISO 527 |
| 1.8 % | 1.8 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 1.7 % | 1.7 % | 5 mm/min; ISO 527 |
| 1.8 % | 1.8 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 6.33 GPa | 918 ksi | 1 mm/min; ISO 527 |
| 6.75 GPa | 979 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 98.0 MPa | 14200 psi | ISO 178 |
| 110 MPa | 16000 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Yield Strength | 112 MPa | 16200 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 5.99 GPa | 869 ksi | 2 mm/min; ISO 178 |
| 6.26 GPa | 908 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.510 J/cm | 0.955 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 2.69 J/cm | 5.04 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 15.0 kJ/m² | 7.14 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 8.00 J @Temperature 23.0 °C |
5.90 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 60.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
33.3 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 69.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
38.3 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 120 °C | 248 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 119 °C @Thickness 3.20 mm |
246 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 115 °C | 239 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 114 °C @Thickness 3.20 mm |
237 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- MV Labs ZN100 Zn(OAC)2·xH2O Zinc acetate hydrate
- Nye Lubricants 874 (FG) Synthetic Oil
- Fainplast Compounds RKS 205/K Rigid PVC, Antishock Extrusion Lead Free
- Styron CALIBREâ„¢ 200-3 Polycarbonate Resin
- Borealis BorPURE™ MB6562 High Density Polyethylene for Injection Molding
- Arkema Group Rilsamid® PA 12 AESNO MED Nylon 12
- Arlon 51576W015 0.0155" (0.394 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate
- Plenco 2000 Phenolic, Granular, Transfer Molded
- Materion Beryllium Copper Alloy 3 Tube; HT (TH04) Temper; up to 76 mm o.d. (UNS C17510)
Copyright © lookpolymers.com All Rights Reserved