Polymer Property : Tensile Strength, Yield = 1600 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	11.0 MPa	1600 psi	ASTM D638
S&E Specialty Polymers TufGuard E™ GTPO8102ROHS Olefin-based, Flame Retardant Application: The GTPO8102ROHS compound is an FR, UV, olefin-based insulation and jacketing compound for appliance, flat ribbon and heat trace wire applications. It is formulated to meet CSA test C22..
Tensile Strength, Yield	11.0 MPa	1600 psi	ISO 527
Polimeri Europa Riblene® GM 30 Low Density Polyethylene - Coating Grade Riblene GM 30 is a medium fluidity low density polyethylene resin (LDPE).Main Applications: Riblene GM 30 is suitable for coating applications where low neck-in and high manufacturing speed are req..
Tensile Strength, Yield	11.0 MPa	1600 psi	ISO 527
Polimeri Europa Riblene® MM 20 Low Density Polyethylene - Injection Molding Riblene MM 20 is a medium fluidity low density polyethylene resin (LDPE).Parts made by Riblene MM 20 are characterized by a high flexibility.Main Applications: Riblene MM 20 is suitable for injecti..
Tensile Strength, Yield	11.0 MPa	1600 psi	ASTM D638
Petroquimica Triunfo Trithene® TS 7001 LDPE - Heavy Duty Low Friction Film The Trithene TS 7001 resin is a low-density polyethylene (LDPE) with high molecular weight, designed to satisfy those applications that require high mechanical strength and low coefficient of fricti..
Tensile Strength, Yield	11.0 MPa	1600 psi	ASTM D638
Petroquimica Triunfo Trithene® TX 7001 LDPE - High Molecular Weight The Trithene TX 7001 resin is a low-density polyethylene (LDPE) with high molecular weight, designed to satisfy those applications that require high mechanical strength and environmental stress crac..
Tensile Strength, Yield	11.0 MPa	1600 psi	at 100%; ASTM D412
2095A Polyurethane-based Biomedical Elastomer
Tensile Strength, Yield	11.0 MPa @Strain 100 %	1600 psi @Strain 100 %	across flow; ASTM D412
ExxonMobil Santoprene® 8203-45 Thermoplastic Rubber (discontinued **) Description: A colorable thermoplastic general purpose non-hygroscopic elastomer with good fluid resistance, formulated to replace thermoset elastomers such as EPDM, polychloroprene, and chlorosulfo..
Tensile Strength, Yield	11.0 MPa	1600 psi	500 mm/min (20 in./min.); Type IV Specimen; ASTM D638
Eastman 18DOA Polyethylene (discontinued **) Polyethylene 18DOA is a low density formulation suggested for the production of closures where a high melt index material is needed to meet shrinkage requirements and fast molding cycles. It molds ..
Tensile Strength, Yield	11.0 MPa	1600 psi	ASTM D638
Petroquimica Triunfo Trithene® TU 3001 LDPE - Agricultural Film The Trithene TU 3001 resin is a low-density polyethylene (LDPE) with high molecular weight, designed to satisfy those applications that require high mechanical properties, good processability and bu..
Tensile Strength, Yield	11.0 MPa	1600 psi	ASTM D638
Petroquimica Triunfo Trithene® TU 8091 LDPE - Agricultural Film Trithene TU 8091 is a low-density polyethylene (LDPE) with high molecular weight, with excellent mechanical properties and good processability. These qualities ensure the production of very wide fil..
Tensile Strength, Yield	11.0 MPa	1600 psi	ASTM D638
Petroquimica Triunfo Trithene® TX 7003 LDPE - Heavy Duty and Industrial Film The Trithene® TX 7003 resin is a low-density, high molecular-weight polyethylene that offers high mechanical strength and environmental stress cracking resistance (ESCR). Additionally, this product..
Tensile Strength, Yield	11.0 MPa @Strain 0.200 %, Temperature 1204 Â°C	1600 psi @Strain 0.200 %, Temperature 2199 Â°F
Haynes HR-160Â® alloy, hot rolled and solution annealed plate Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an..
Tensile Strength, Yield	11.0 MPa	1600 psi	Elastic; ASTM D638
Multibase Multi-FlexÂ® A 8502 LC TPE Thermoplastic Elastomer Features: Chemical Resistance, Good Thermal Stability, GoodOzone Resistant Forms:PelletsProcessing Method:Injection MoldingExtrusion Uses: Automotive Interior PartsInformation provided by Multiba..
Tensile Strength, Yield	11.0 MPa	1600 psi	Elastic; ASTM D412
Multibase Multi-FlexÂ® A 8502 LC UV RXF/YYWA Black TPE Thermoplastic Elastomer Forms: PelletsProcessing Methods:Injection Molding Information provided by Multibase
Tensile Strength, Yield	11.0 MPa	1600 psi	100%; ASTM D412
Teknor Apex APEXÂ® 3211-85 Polyvinyl Chloride, Flexible Material Status-Commercial: ActiveAvailability-North AmericaTest Standards Available-ASTMUses-Automotive Applications, Non-specific Food Applications, General Purpose, Medical Applications, Modeling..
Tensile Strength, Yield	11.0 MPa	1600 psi	ASTM D412
Teknor Apex APEXÂ® 90-A472R-65-NT Polyvinyl Chloride, Flexible Material Status-Commercial: ActiveAvailability-North AmericaTest Standards Available-ASTMUses-Medical Applications, Caps, Closures, Valves/Valve Parts Appearance-ClearForms-PelletsProcessing Method-..
Tensile Strength, Yield	11.0 MPa	1600 psi	ASTM D412
Teknor Apex FlexalloyÂ® 3501-50-NT Polyvinyl Chloride Elastomer Material Status-Commercial: ActiveAvailability-North AmericaTest Standards Available-ASTM Features: Ultra High MW, Ethylene Oxide SterilizableForms-PelletsProcessing-Extrusion, Injection MoldingAppe..
Tensile Strength, Yield	11.0 MPa	1600 psi	TD; ISO 527-3
Borealis FG5199 Linear Low Density Polyethylene FG5199 is a Butene Linear Low Density Polyethylene for Film Extrusion. Includes antioxidant, anti-Fog and cling additives. The grade is developed for blown cling film. Film made from FG5199 is suit..
Tensile Strength, Yield	11.0 MPa	1600 psi	2"/min; ASTM D638
A. Schulman CP814-01 Linear, Low-Density Polyethylene DescriptionCP 814-01 is a linear low-density polyethylene resin with excellent molding characteristics and good low temperature impact. ApplicationCP814-01 meets the specifications contained in FDA ..
Tensile Strength, Yield	11.0 MPa	1600 psi	2"/min; ASTM D638
A. Schulman CP814-01 Linear, Low-Density Polyethylene DescriptionCP 814-01 is a linear low-density polyethylene resin with excellent molding characteristics and good low temperature impact. ApplicationCP814-01 meets the specifications contained in FDA ..
Tensile Strength, Yield	11.0 MPa	1600 psi	machine direction; ASTM D882
A. Schulman CP878-01 Natural Linear, Low-Density Polyethylene DescriptionCP 878-01 Natural is a linear low-density polyethylene having good tensile, stiffness, and toughness properties. ApplicationCP 878-01 meets FDA Regulation 21 CFR 177.1520(c)3.1 and 3.2.In..
Tensile Strength, Yield	11.0 MPa	1600 psi	ASTM D638
Trelleborg Horda Cable E8413 Easy Strippable Semiconductive Shielding E8413 is a vulcanizable, strippable semiconductive compound, designed for both XLPE and EPDM rubber insulated cables and use in both dry and steam curing processes.E8413 meets the requirements as be..
Tensile Strength, Yield	11.0 MPa	1600 psi	ASTM D638
ExxonMobil LDPE LD 617.LN Low Density Polyethylene Resin Product Description: LD 617.LN is a high flow, low density polyethylene homopolymer resin designed to provide excellent processability, flexibility and surface appearance. This multipurpose resin is..
Tensile Strength, Yield	11.0 MPa	1600 psi	Molded and tested in accordance with ASTM D4976; ASTM D638
Dow DNDA-1081 NT 7 Linear Low Density Polyethylene Resin DOW DNDA-1081 NT 7 is produced using UNIPOL™ PE process technology. It is intended for high-speed injection molding of thin walled parts such as downguaged lids. Information provided by Dow
Tensile Strength, Yield	11.0 MPa	1600 psi	ASTM D-638
Axiall 8640 Moldings & Extrusions Flexible PVC General purpose extrusion compound for weatherstrips and tubings.Information provided by Georgia GulfGeorgia Gulf became Axiall Corporation in 2013.
Tensile Strength, Yield	11.0 MPa	1600 psi	ASTM D-638
Axiall 8700 Moldings & Extrusions Flexible PVC General purpose, matte-finish extrusion compound.Information provided by Georgia GulfGeorgia Gulf became Axiall Corporation in 2013.
Tensile Strength, Yield	11.0 MPa	1600 psi	ASTM D-638
Axiall 8651 Moldings & Extrusions Flexible PVC A quality, low gravity extrusion compound with excellent low temperature properties. Designed for use in weatherstrips, flexible gaskets and extruded shapes.Information provided by Georgia GulfGeor..
Tensile Strength, Yield	11.0 MPa	1600 psi	ASTM D638
Huntsman PE2060 Injection Molding Polyethylene (discontinued **) Homopolymer and FDA compliant.Features: High flow characteristics, good processability.Applications: Injection molding: general purpose molding, large moldings including housewares and toys.FDA Note..
Tensile Strength, Yield	11.0 - 22.0 MPa	1600 - 3190 psi	Average value: 18.1 MPa Grade Count:66
Overview of materials for Linear Medium Density Polyethylene (LMDPE), Rotational Molded This property data is a summary of similar materials in the MatWeb database for the category "Linear Medium Density Polyethylene (LMDPE), Rotational Molded". Each property range of values reported i..
Tensile Strength, Yield	11.0 MPa	1600 psi	ASTM D638
Huntsman PE8020 Specialty Polyethylene (discontinued **) Homopolymer and FDA compliant.Features: Yields film with excellent draw down and machinability.Applications: Film extrusion: gel free film applications.FDA Notes: Conforms to FDA regulation 21 CFR 1..