Multibase Multi-Flex® A 8502 LC UV RXF/YYWA Black TPE Thermoplastic Elastomer
| Category | Polymer , Thermoplastic , Elastomer, TPE |
| Manufacturer | Multibase |
| Trade Name | Multi-Flex® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Multibase Multi-Flex® A 8502 LC UV RXF/YYWA Black TPE Thermoplastic Elastomer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Forms: PelletsProcessing Methods:Injection Molding Information provided by Multibase
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.03 g/cc | 1.03 g/cc | ASTM 792 |
| Linear Mold Shrinkage | 0.013 cm/cm | 0.013 in/in | ASTM D955 |
| Melt Flow | 1.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
1.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 83 | 83 | 10 seconds; ASTM D2240 |
| Tensile Strength, Yield | 11.0 MPa | 1600 psi | Elastic; ASTM D412 |
| 4.55 MPa @Strain 100 % |
660 psi @Strain 100 % |
ASTM D412 | |
| Elongation at Break | 500 % | 500 % | Elastic; ASTM D412 |
| Flexural Strength | 3.59 MPa | 520 psi | ASTM D790 |
| Flexural Modulus | 0.0586 GPa | 8.50 ksi | 1% Secant; ASTM D790 |
| Tear Strength | 43.8 kN/m | 250 pli | ASTM D624 |
| Compression Set | 25 % | 25 % | 73°F, 70 hours; ASTM D395 |
| 51 % | 51 % | 158°F, 70 hours; ASTM D395 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Middle Barrel Temperature | 210 °C | 410 °F | |
| Front Barrel Temperature | 227 °C | 440 °F | |
| Nozzle Temperature | 235 °C | 455 °F | |
| Mold Temperature | 51.7 °C | 125 °F |
Users viewing this material also viewed the following:
- Multibase Multi-Flex® TPE A 9007 BLK
- Kolon KOCETAL® CB301 Conductive Grade Acetal Resin
- Momentive Performance Materials RTV8262 Red General Purpose Potting/Encapsulating Compound
- SPS Guang Zhou SAMATâ„¢ EP 5001(f1) Flame-retarded Polypropylene
- A. Schulman POLYBATCH™ U-0294-L Blowing Agent Concentrate Based In PE
- Arlon 19586R025 0.025" (0.635 mm) Uncured Silicone Rubber with Fiberglass Substrate
- 3M FM15B Indoor UL Recognized Computer Imprintable Silver Polyester Label Product
- Akzo Nobel Expancel® 950 DU 120 Dry unexpanded microspheres
Copyright © lookpolymers.com All Rights Reserved