Dow DNDA-1081 NT 7 Linear Low Density Polyethylene Resin

Category	Polymer , Thermoplastic , Polyethylene (PE) , LLDPE
Manufacturer	Dow Chemical
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Dow DNDA-1081 NT 7 Linear Low Density Polyethylene Resin.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

DOW DNDA-1081 NT 7 is produced using UNIPOL™ PE process technology. It is intended for high-speed injection molding of thin walled parts such as downguaged lids. Information provided by Dow

Physical Properties	Metric	English	Comments
Density	0.931 g/cc	0.0336 lb/in³	ASTM D792
Melt Index of Compound	127.5 g/10 min @Load 2.16 kg, Temperature 190 °C	127.5 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	55	55	Molded and tested in accordance with ASTM D4976; ASTM D2240
Tensile Strength at Break	8.96 MPa	1300 psi	Molded and tested in accordance with ASTM D4976; ASTM D638
Tensile Strength, Yield	11.0 MPa	1600 psi	Molded and tested in accordance with ASTM D4976; ASTM D638
Elongation at Break	60 %	60 %	Molded and tested in accordance with ASTM D4976; ASTM D638
Elongation at Yield	2.0 %	2.0 %	Molded and tested in accordance with ASTM D4976; ASTM D638
Flexural Modulus	0.524 GPa	76.0 ksi	2% Secant; Molded and tested in accordance with ASTM D4976; ASTM D790 B
Tensile Impact Strength	105 kJ/m²	50.0 ft-lb/in²	Molded and tested in accordance with ASTM D4976; ASTM D1822, Type S

Thermal Properties	Metric	English	Comments
Melting Point	126 °C	259 °F	Dow Method (DSC)
Crystallization Temperature	113 °C	235 °F	Dow Method (DSC)
Deflection Temperature at 0.46 MPa (66 psi)	51.1 °C	124 °F	Molded and tested in accordance with ASTM D4976; ASTM D648
Vicat Softening Point	97.2 °C	207 °F	ASTM D1525
Brittleness Temperature	-23.9 °C	-11.0 °F	Molded and tested in accordance with ASTM D4976; ASTM D746