- Polymer Property : Tensile Strength, Yield = 7.00 MPa
Polymer Property : Tensile Strength, Yield = 7.00 MPa Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 7.00 MPa | 1020 psi | ISO 527 |
| Polimeri Europa Greenflex® MP 34 Ethylene Vinyl Acetate Copolymer - Injection Molding & Compounding Greenflex MP 34 is an ethylene vinyl acetate copolymer (EVA) for injection molding and compounding applications. Greenflex MP 34 combines high fluidity with high elasticity.Main Applications: Gree.. |
|||
| Tensile Strength, Yield | 7.00 MPa | 1020 psi | ASTM D412 |
| Precision Polymer Engineering F60A Fluorosilicone Rubber Blue Fluorosilicone, 56-65 °IRHD. Fluorosilicone rubber having methyl, vinyl and fluorine substituent groups on the polymer chain. To meet Aerospace Specification Mil-R-25988B, Class 1, Grade 60... |
|||
| Tensile Strength, Yield | 7.00 MPa | 1020 psi | ASTM D412 |
| Precision Polymer Engineering H80B Epichlorohydrin Peroxide Cured, Epichlorohydrin Rubber, 75-85 °IRHD. Terpolymer of epichlorohydrin, ethylene oxide and an unsaturated monomer. To ASTM D2000 line call-out: M3CH608, A25, B14, EO16, EO36, F17. AS.. |
|||
| Tensile Strength, Yield | 7.00 MPa | 1020 psi | ASTM D412 |
| Precision Polymer Engineering N65H Nitrile Rubber Nitrile Butadiene Rubber (NBR), 65-75 °IRHD. High acrylonitrile (ACN) content = 40% plus. Copolymer of acrylonitrile and butadiene.Applications: The high acrylonitrile content of this compound inc.. |
|||
| Tensile Strength, Yield | 7.00 MPa | 1020 psi | ASTM D412 |
| Precision Polymer Engineering S40R Silicone Rubber Red Silicone Rubber, 35-45 °IRHD. Silicone rubber having both methyl and vinyl substituent groups on the polymer chain. ASTM & ISO designation = VMQ.Applications: Excellent heat resistance and lo.. |
|||
| Tensile Strength, Yield | 7.00 - 13.0 MPa | 1020 - 1890 psi | ±30% change after 72 hours @ 250°C; ASTM D412 |
| Precision Polymer Engineering V71H Fluoroelastomer Compound Green Fluoroelastomer Rubber, 70-75 °IRHD. Copolymer of vinylidene fluoride and hexafluoropropylene. Formulated using only those ingredients determined by the United States Federal Food and Drug Ad.. |
|||
| Tensile Strength, Yield | 7.00 MPa | 1020 psi | ASTM D412 |
| Precision Polymer Engineering V75V Fluoroelastomer Compound Special steam resistant, Fluoroelastomer Rubber, 70-80 °IRHD. Terpolymer of vinylidene fluoride, hexafluoropropylene and tetrafluoroethylene. To meet ASTM D2000 line call-out MHK707, A1-10, B37, E.. |
|||
| Tensile Strength, Yield | 7.00 MPa | 1020 psi | |
| LyondellBasell Lupolen® V 3510 K Ethylene Vinyl Acetate, lnjection Molding Grade Injection moldingsData was collected by ISO methods and originally provided by BASF. The Lupolen® product line is now produced by Basell. |
|||
| Tensile Strength, Yield | 7.00 MPa | 1020 psi | 60°C for 1,000 hrs with 90% RH; JIS-K-6251 |
| Fujipoly Industries Sarcon® 25G-Td Thin-Film GR-TD Sarcon 25G-Td is a highly conformable, thermally conductive material in areas where space between surfaces is uneven and surface textures vary.Information provided by Fujipoly Industries |
|||
| Tensile Strength, Yield | 7.00 MPa | 1020 psi | 200°C for 1,000 hrs |
| Fujipoly Industries Sarcon® 30T Thin-Film TR Sarcon TR is Fujipolys originally developed High Heat Conductive Silicone Rubber. Fine, high heat conductive ceramic particles are mixed with insulative silicone rubber.Sarcon GTR is a composite of .. |
|||
| Tensile Strength, Yield | 7.00 MPa | 1020 psi | ASTM D638 |
| LyondellBasell Adflexâ„¢ KS-021P TPO Resin Primary Processing Method: Blown Film/Impact ModificationKey Features: excellent low temperature impact resistance, excellent chemical and environmental stress-cracking resistance, FDA acceptable, n.. |
|||
| Tensile Strength, Yield | >= 7.00 MPa | >= 1020 psi | |
| Mikro-Technik Reproflon G25 PTFE Available Forms: Rods, Tubes. Special Characteristics:Higher resistance to abrasionHigher resistance to compression compared to virgin PTFE and unfilled ReproflonReduced plastic flowInformation prov.. |
|||
| Tensile Strength, Yield | >= 7.00 MPa | >= 1020 psi | |
| Sibur BK-1675M Butyl Rubber (IIR) EXXON Butyl 268, PB 301 Bayer. For general and medical goods. |
|||
| Tensile Strength, Yield | >= 7.00 MPa | >= 1020 psi | |
| Sibur BK-1675N Butyl Rubber (IIR) EXXON Butyl 268, PB 301 Bayer. For production of automobile inner tubes, heating tubes, sharper vulcanizer diaphragms, and rubber fabrics. |
|||
| Tensile Strength, Yield | 7.00 MPa | 1020 psi | |
| Trelleborg Commercial Neoprene® C653 Chloroprene CR or Chloroprene is a homopolymer of chloroprene or chlorobutadiene. NEOPRENE®PropertiesExcellent mechanical and abrasion properties even without reinforcing fillers.Reasonable resilience in grade.. |
|||
| Tensile Strength, Yield | 7.00 MPa | 1020 psi | |
| Trelleborg Hypalon® H511 Chlorosulphonated Polyethylene PropertiesExcellent resistance to oxidation and has outstanding resistance to atmospheric conditions and in particular strong sunlight and ozone.CSM compounds resist fire and are self extinguishing .. |
|||
| Tensile Strength, Yield | 7.00 MPa | 1020 psi | |
| Trelleborg Hypalon® H608 Chlorosulphonated Polyethylene PropertiesExcellent resistance to oxidation and has outstanding resistance to atmospheric conditions and in particular strong sunlight and ozone.CSM compounds resist fire and are self extinguishing .. |
|||
| Tensile Strength, Yield | 7.00 MPa | 1020 psi | |
| Trelleborg T528 Butyl Rubber Butyl rubber is a copolymer of isobutylene and a small percentage of isoprene.PropertiesWith careful compounding Butyl has really good tensile strength.Butyl has very low permeability to air and oth.. |
|||
| Tensile Strength, Yield | 7.00 MPa | 1020 psi | |
| Trelleborg E701 EPDM Rubber EPM -- EPDM or Ethylene -- Propylene Rubber. EPM can only be vulcanized by peroxides or radiation; whereas EPDM can be vulcanized conventionally using sulphur.Properties:Excellent inherent high and .. |
|||
| Tensile Strength, Yield | 7.00 MPa | 1020 psi | |
| Trelleborg Hypalon® H606 Chlorosulphonated Polyethylene PropertiesExcellent resistance to oxidation and has outstanding resistance to atmospheric conditions and in particular strong sunlight and ozone.CSM compounds resist fire and are self extinguishing .. |
|||
| Tensile Strength, Yield | 7.00 MPa @Strain 100 % |
1020 psi @Strain 100 % |
ISO 527-1/-2 |
| Covestro Desmopan® 786 S Polyurethane injection molding gradevery good hydrolysis and microbial resistancehigh mechanical strengthgood low-temperature flexibilityApplicationToysTechnical partsAs of 1 September 2015, Bayer MaterialScienc.. |
|||
| Tensile Strength, Yield | 7.00 MPa @Strain 100 % |
1020 psi @Strain 100 % |
ISO 527-1/-2 |
| Covestro Desmopan® W DP89085A Polyurethane PreprocessingMax. Water content |
|||
| Tensile Strength, Yield | 7.00 MPa @Strain 50.0 % |
1020 psi @Strain 50.0 % |
50 mm/min |
| Arkema Group Nakan® FKS 810 R PVC, Soft Extrusion Grade NAKAN FKS 810 R is a soft polyvinyl chloride compound developed for insulation and sheathing.ISO data provided by the manufacturer, Arkema. |
|||
| Tensile Strength, Yield | 7.00 MPa @Strain 50.0 % |
1020 psi @Strain 50.0 % |
50 mm/min |
| Arkema Group Nakan® FMM 871 N PVC, Soft Injection Molding Grade NAKAN FMM 871 N is a soft polyvinyl chloride compound developed for injection molding of drip chambers for perfusion and transfusion.ISO data provided by the manufacturer, Arkema. |
|||
| Tensile Strength, Yield | 7.00 MPa | 1020 psi | ISO 527-2 |
| Arkema Group OREVAC® 18302N Maleic Anhydride Modified Linear Low Density Polyethylene OREVAC® 18365 is anhydride modified polyethylene. It is available in pellet form for use in conventional extrusion and coextrusion equipment designed to process polyethylene (PE) resins. OREVAC® 1.. |
|||
| Tensile Strength, Yield | 7.00 MPa | 1020 psi | 50 mm/min |
| Arkema Group Evatane® 1003 VL 4C Ethylene Vinyl Acetate EVA copolymer made by high pressure tubular process. Anti-UV stabilized grade. Applications Thermal and colorless agricultural film to 180 at 200 µ for greenhouse coverage.ISO data provided by the .. |
|||
| Tensile Strength, Yield | 7.00 MPa | 1020 psi | 50 mm/min |
| Arkema Group Evatane® 1004 VL 4E Ethylene Vinyl Acetate EVA copolymer made by high pressure tubular process. Anti-UV stabilized grade. Applications Thermal and colorless agricultural film to 180 at 200 µ for greenhouse coverage.ISO data provided by the .. |
|||
| Tensile Strength, Yield | 7.00 MPa | 1020 psi | 50 mm/min |
| Arkema Group Evatane® 1010 VN 3 Ethylene Vinyl Acetate EVA copolymer made by high pressure tubular process. Applications Grade for flexible, transparent films with high mechanical properties. Examples: stretch film, food packaging.ISO data provided by t.. |
|||
| Tensile Strength, Yield | 7.00 MPa @Strain 50.0 % |
1020 psi @Strain 50.0 % |
50 mm/min |
| Arkema Group Nakan® FKS 902 R PVC, Soft Extrusion Grade NAKAN FKS 902 R is a soft polyvinyl chloride compound developed for medium voltage hard insulation.ISO data provided by the manufacturer, Arkema. |
|||