Fujipoly Industries SarconÂ® 30T Thin-Film TR

Category	Polymer , Thermoset , Silicone
Manufacturer	Fujipoly Industries
Trade Name	Sarcon®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Fujipoly Industries SarconÂ® 30T Thin-Film TR.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Sarcon TR is Fujipolys originally developed High Heat Conductive Silicone Rubber. Fine, high heat conductive ceramic particles are mixed with insulative silicone rubber.Sarcon GTR is a composite of Heat Conductive Silicone Rubber and fiberglass.Information provided by Fujipoly Industries

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	73	73	60Â°C for 500 hrs; ASTM D2240
	75	75	ASTM D2240
	83	83	150Â°C for 1,000 hrs; ASTM D2240
	90	90	200Â°C for 1,000 hrs; ASTM D2240
Tensile Strength, Yield	5.66 MPa	821 psi
	6.00 MPa	870 psi	150Â°C for 1,000 hrs
	7.00 MPa	1020 psi	200Â°C for 1,000 hrs
Elongation at Yield	30 %	30 %	200Â°C for 1,000 hrs
	50 %	50 %	150Â°C for 1,000 hrs
	100 %	100 %
Tear Strength	0.300 kN/m	1.71 pli

Thermal Properties	Metric	English
Maximum Service Temperature, Air	182 Â°C	360 Â°F
Minimum Service Temperature, Air	-60.0 Â°C	-76.0 Â°F
Flammability, UL94	V-0	V-0

Electrical Properties	Metric	English	Comments
Volume Resistivity	6.10e+13 ohm-cm	6.10e+13 ohm-cm	60Â°C for 500 hrs
	1.00e+15 ohm-cm	1.00e+15 ohm-cm
	5.60e+15 ohm-cm	5.60e+15 ohm-cm	150Â°C for 1,000 hrs
	7.20e+15 ohm-cm	7.20e+15 ohm-cm	200Â°C for 1,000 hrs
Dielectric Constant	4.2 @Frequency 50 Hz	4.2 @Frequency 50 Hz	After 1000 hrs at 150Â°C
	4.2 @Frequency 50 Hz	4.2 @Frequency 50 Hz	After 1000 hrs at 200Â°C
	4.2 @Frequency 1000 Hz	4.2 @Frequency 1000 Hz	After 1000 hrs at 200Â°C
	4.2 @Frequency 1e+6 Hz	4.2 @Frequency 1e+6 Hz	After 1000 hrs at 200Â°C
	4.3 @Frequency 1e+6 Hz	4.3 @Frequency 1e+6 Hz	After 1000 hrs at 150Â°C
	4.3 @Frequency 1000 Hz	4.3 @Frequency 1000 Hz	After 1000 hrs at 150Â°C
	4.5 @Frequency 1e+6 Hz	4.5 @Frequency 1e+6 Hz	After 500 hrs at 60Â°C
	4.6 @Frequency 1000 Hz	4.6 @Frequency 1000 Hz	After 500 hrs at 60Â°C
	4.8 @Frequency 50 Hz	4.8 @Frequency 50 Hz	After 500 hrs at 60Â°C
Dielectric Strength	6.00 kV/mm	152 kV/in	60Â°C for 500 hrs
	8.00 kV/mm	203 kV/in	AC 60 Hz; 200Â°C for 1,000 hrs
	8.40 kV/mm	213 kV/in	AC 60 Hz; 150Â°C for 1,000 hrs
	10.0 kV/mm	254 kV/in	AC 60 Hz
Dielectric Breakdown	7000 V	7000 V	Withstand Voltage [V/min]; AC 60 Hz
Dissipation Factor	0.0020 @Frequency 1000 Hz	0.0020 @Frequency 1000 Hz	After 1000 hrs at 150Â°C
	0.0020 @Frequency 1000 Hz	0.0020 @Frequency 1000 Hz	After 1000 hrs at 200Â°C
	0.0020 @Frequency 1000 Hz	0.0020 @Frequency 1000 Hz
	0.0030 @Frequency 1e+6 Hz	0.0030 @Frequency 1e+6 Hz
	0.0030 @Frequency 1e+6 Hz	0.0030 @Frequency 1e+6 Hz	After 1000 hrs at 200Â°C
	0.0030 @Frequency 1e+6 Hz	0.0030 @Frequency 1e+6 Hz	After 1000 hrs at 150Â°C
	0.0040 @Frequency 50 Hz	0.0040 @Frequency 50 Hz	After 1000 hrs at 200Â°C
	0.0040 @Frequency 50 Hz	0.0040 @Frequency 50 Hz	After 1000 hrs at 150Â°C
	0.0040 @Frequency 50 Hz	0.0040 @Frequency 50 Hz
	0.0060 @Frequency 1e+6 Hz	0.0060 @Frequency 1e+6 Hz	After 500 hrs at 60Â°C
	0.014 @Frequency 1000 Hz	0.014 @Frequency 1000 Hz	After 500 hrs at 60Â°C
	0.030 @Frequency 50 Hz	0.030 @Frequency 50 Hz	After 500 hrs at 60Â°C

Descriptive Properties	Value	Comments
Color	Gray-Green
Thermal Impedance	0.62Â°C/W	FTM P-3010; ASTM D5470