Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 68.0 MPa | 9860 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Lexan® CFR5630 PC COPOLYMER LEXAN™ CFR5630 Polycarbonate (PC) is a non-filled resin, suitable for injection molding and extrusion. This non-chlorinated, non-brominated flame retardant PC resin meets FAR25.853 smoke density an.. |
|||
Tensile Strength, Yield | 68.0 MPa | 9860 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Lexan® CFR5630 PC COPOLYMER (Europe-Africa-Middle East) LEXAN™ CFR5630 Polycarbonate (PC) is a non-filled resin, suitable for injection molding and extrusion. This non-chlorinated, non-brominated flame retardant PC resin meets FAR25.853 smoke density an.. |
|||
Tensile Strength, Yield | 68.0 MPa | 9860 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Lexan® CFR5630D PC COPOLYMER LEXAN™ CFR5630D Polycarbonate (PC) is a non-filled resin, suitable for injection molding and extrusion. This non-chlorinated, non-brominated flame retardant PC resin meets FAR25.853 smoke density a.. |
|||
Tensile Strength, Yield | 68.0 MPa | 9860 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Lexan® CFR7630 PC COPOLYMER (Asia Pacific) Lexan* CFR7630 Polycarbonate (PC) resin is a non-filled resin, suitable for injection molding and extrusion. This non-chlorinated, non-brominated flame retardant PC has an UL-94 V0 rating at 1.0 mm .. |
|||
Tensile Strength, Yield | 68.0 MPa | 9860 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Lexan® CFR7630 PC COPOLYMER (Europe-Africa-Middle East) Lexan* CFR7630 Polycarbonate (PC) resin is a non-filled resin, suitable for injection molding and extrusion. This non-chlorinated, non-brominated flame retardant PC has an UL-94 V0 rating at 1.0 mm .. |
|||
Tensile Strength, Yield | 68.0 MPa | 9860 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics Lexan® HFD4211 PC Lexan* HFD4211 is a 10% glass filled, injection moldable grade designed for high flow and superior surface appearance. Internal mold release. |
|||
Tensile Strength, Yield | 68.0 MPa | 9860 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Lexan® HPH4704 PPC High heat specialty polycarbonate. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 or USP Class VI). EtO, steam, gamma and e-beam steril.. |
|||
Tensile Strength, Yield | 68.0 MPa | 9860 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Lexan® LUX7630C PC COPOLYMER Lexan* LUX7630C Polycarbonate (PC) resin is a non-filled resin, suitable for injection molding and extrusion. This non-chlorinated, non-brominated flame retardant PC has an UL-94 V0 rating at 1.0 mm.. |
|||
Tensile Strength, Yield | 68.0 MPa | 9860 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Lexan® LUX7636C PC COPOLYMER Lexan* LUX7636C Polycarbonate (PC) resin is a non-filled, extrudable grade. This non-chlorinated, non-brominated flame retardant PC has an UL-94 V0 rating at 1.0 mm / 5VA rating at 3.0mm and is U.. |
|||
Tensile Strength, Yield | 68.0 MPa | 9860 psi | Type I, 5 mm/min; ASTM D 638 |
SABIC Innovative Plastics Ultem ATX100F PEI+PCE (Asia Pacific) Higher impact, high flow Polyetherimide blend. ECO Conforming, UL94 HB Listing. US FDA Food Contact Compliant.This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
Tensile Strength, Yield | 68.0 MPa | 9860 psi | Type I, 5 mm/min; ASTM D 638 |
SABIC Innovative Plastics Ultem HATX100 PEI+PCE (Europe-Africa-Middle East) Higher impact, high flow Polyetherimide blend. ECO Conforming. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO 10993 or USP Class VI), food.. |
|||
Tensile Strength, Yield | 68.0 MPa | 9860 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics NORYL HNA033 PPE+HIPS Noryl* HNA033 resin is an unfilled modified polyphenylene ether resin designed to withstand several cycles in an autoclave. This resin is suitable for multiple conversion routes and is available in.. |
|||
Tensile Strength, Yield | 68.0 MPa | 9860 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics NORYL HNA033 PPE+HIPS (Europe-Africa-Middle East) Noryl* HNA033 resin is an unfilled modified polyphenylene ether resin designed to withstand several cycles in an autoclave. This resin is suitable for multiple conversion routes and is available in.. |
|||
Tensile Strength, Yield | 68.0 MPa | 9860 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics NORYL NH5120C PPE+PS Noryl* NH5120C resin is a modified PPE-PS blend that exhibits an excellent balance of nonhalogenated flame retardance, good chemical resistance, and low specifc gravity for light weight parts. The .. |
|||
Tensile Strength, Yield | 68.0 MPa | 9860 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics NORYL NH5120C PPE+PS (Asia Pacific) Noryl* NH5120C resin is a modified PPE-PS blend that exhibits an excellent balance of nonhalogenated flame retardance, good chemical resistance, and low specifc gravity for light weight parts. The .. |
|||
Tensile Strength, Yield | 68.0 MPa | 9860 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics NORYL PX1391 PPE+PS (Asia Pacific) Automotive applications, primarily. Excellent electrical properties. high heat. 305F (152C) DTUL. |
|||
Tensile Strength, Yield | 68.0 MPa | 9860 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics ULTEM STM1700 PEI Copolymer (Europe-Africa-Middle East) Siltem STM1700 is a flexible copolymer designed for wire and cable applications. It offers a halogen free (according VDE 0472) flame retardant solution that also offers low smoke emission and toxici.. |
|||
Tensile Strength, Yield | 68.0 MPa | 9860 psi | 50 mm/min; ISO 527-1,-2 |
Covestro Apec® 1697 High-Heat Polycarbonate This linear, amorphous copolycarbonate is most suitable for applications that must withstand high temperatures and exhibit toughness, impact resistance and high transparency. These properties, along.. |
|||
Tensile Strength, Yield | 68.0 MPa | 9860 psi | 50 mm/min; ISO 527 |
Chi Mei Kibisan® PN-117 SAN Injection Molding |
|||
Tensile Strength, Yield | 68.0 MPa | 9860 psi | 23°C, 50% RH; ASTM D638 |
Asahi Kasei Xyron® A0210 PPE/PA AutomotiveInformation provided by Asahi Kasei |
|||
Tensile Strength, Yield | 68.0 MPa | 9860 psi | 50 mm/min; ISO 527-2 |
BASF Ultraform® S1320 003 POM Description: Is a POM, free-flowing, rapidly solidifying grade for moldings difficult to produce by injection molding and having low wall thicknesses, higher stiffness and thermal stability.Informat.. |
|||
Tensile Strength, Yield | 68.0 MPa | 9860 psi | ASTM D638 |
Ascend Performance Materials VYDYNE® 45 Nylon, Impact Modified, Weather Stable Typical property data. VYDYNE is a registered trademark of Solutia Inc. |
|||
Tensile Strength, Yield | 68.0 MPa @Temperature 60.0 °C |
9860 psi @Temperature 140 °F |
|
BASF Ultrason S 3010 PSU Ultrason S 3010 is an unreinforced, higher viscosity injection molding and extrusion PSU grade, tougher and with improved chemical resistance. It conforms to FDA requirements of 21 CFR 177.1655. |
|||
Tensile Strength, Yield | 68.0 MPa | 9860 psi | |
Asahi Kasei Xyron® AT610 Modified Polyphenylene Ether Applications: Information provided by Asahi Kasei |
|||
Tensile Strength, Yield | 68.0 MPa | 9860 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Lexan® LUX7632C PC COPOLYMER (Asia Pacific) Lexan* LUX7632C Polycarbonate (PC) resin is a non-filled, extrudable grade. This non-chlorinated, non-brominated flame retardant PC has an UL-94 V0 rating at 1.0 mm / 5VA rating at 3.0mm and is U.. |
|||
Tensile Strength, Yield | 68.0 MPa | 9860 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Lexan® LUX7636C PC COPOLYMER (Asia Pacific) Lexan* LUX7636C Polycarbonate (PC) resin is a non-filled, extrudable grade. This non-chlorinated, non-brominated flame retardant PC has an UL-94 V0 rating at 1.0 mm / 5VA rating at 3.0mm and is U.. |
|||
Tensile Strength, Yield | 68.0 MPa | 9860 psi | ISO 527 |
Styrolution Luran® SAN C Styrene Acrylonitrile Luran SAN C is an injection molding grade of SAN with medium impact strength and high flow.Information provided by Styrolution |