Polymer Property : Tensile Strength, Yield = 30.0 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	30.0 MPa	4350 psi	IV 2 in/min; ASTM D638
Solvay Engineered Polymers INDURE™ E1500 HG TPO (discontinued **) Description: INDURE™ E1500 HG is a thermoplastic olefinic elastomer (TPO) designed for high-gloss thermoformed applications where excellent gloss retention after forming is required. This material..
Tensile Strength, Yield	30.0 MPa	4350 psi	ISO 527
Total Finathene® SR 572 HDPE blow molding (discontinued **) FINATHENE® SR 572 is a high density polyethylene produced by the slurry loop low pressure polymerization process. FINATHENE® SR 572 has been developed for the manufacturing of blow molded bottles ..
Tensile Strength, Yield	30.0 MPa	4350 psi	50 mm/min test speed; ASTM D 638
NOVA Chemicals Sclair® 2906 HDPE Injection Molding Resin NOVA Chemicals' polyethylene resins are chemically and biologically inert.Features: Excellent toughness and impact resistance, High stiffness, Excellent processing stability, High GlossAdditives: ..
Tensile Strength, Yield	30.0 MPa	4350 psi	50 mm/min; ASTM D638
Solvay Specialty Polymers HalarÂ® 500LC Ethylene Chlorotrifluoroethylene Copolymer (ECTFE) Low ViscosityUses: Wire & Cable ApplicationsAdditional Properties: Crystallization Heat - ASTM D3418 40.0 J/g; Heat of Fusion - ASTM D3418 42.0 J/g; Thermal Stability - TGA 405 Â°CInformation prov..
Tensile Strength, Yield	30.0 MPa	4350 psi	ASTM D638
A. Schulman POLYFORT™ PP 2268UX Heat Resistant Polypropylene DescriptionPolyfort® PP 2268UX is a UV stabilized, extra high flow unique high modulus, heat resistant polypropylene.Information provided by A. Schulman.
Tensile Strength, Yield	30.0 MPa	4350 psi	2" (50mm) per min; ASTM D638
Formosa Plastics Formolene® 2306N Impact Copolymer Polypropylene Impact Copolymer for Compression and Injection Molded Caps and Closures Formolene® 2306N is a polypropylene copolymer formulated for compression and injection molded cap applications. It was create..
Tensile Strength, Yield	30.0 MPa	4350 psi	ASTM D638
Total PPH 3576 BB Polypropylene Homopolymer, Cast Film Polypropylene 3576 BB is recommended for use in non-oriented cast films processes. It contains an optimized level of slip and anti-block additives.3576 BB is intended for food, magazine or textile ..
Tensile Strength, Yield	30.0 MPa	4350 psi	ISO 527-2
Total PPH 7089 Polypropylene Homopolymer, Fiber Polypropylene PPH 7089 is a narrow molecular weight distribution homopolymer polypropylene, with anti-gas fading stabilization.Polypropylene PPH 7089 is intended for the extrusion of fibers with the..
Tensile Strength, Yield	30.0 MPa	4350 psi	ASTM D638
Total PPR 6827MZ Polypropylene, Random Copolymer - High Flow Clarified - for Injection Molding Clarity. TOTAL Polypropylene 6827MZ exhibits superior clarity and produces molded parts with improved impact compared with parts molded from homopolymer polypropylene.Antistat. 6827MZ contains an a..
Tensile Strength, Yield	30.0 MPa	4350 psi	ASTM D638
A. Schulman POLYFLAM™ RPP 1058 General Purpose Homopolymer Polypropylene (30% Fiberglass) DescriptionPolyflam® RPP 1058 is a general purpose homopolymer polypropylene flame retardant with a UL-V2 flammability rating and 105°C temperature index at 0.030 in.Information provided by A. Sch..
Tensile Strength, Yield	30.0 MPa	4350 psi	ASTM D638
A. Schulman POLYFORT™ FXP 2600-3120 CaC02 Filled Homopolymer Polypropylene DescriptionPolyfort® FXP 2600-3120 is a 20% GAC02 filled homopolymer polypropylene compound.Information provided by A. Schulman.
Tensile Strength, Yield	30.0 MPa	4350 psi
TSE Industries Millathane® E34 Millable Polyether Polyurethane Rubber with 2.0 PHR MBTS MILLATHANE E34 is a high performance polyether polyurethane rubber for applications requiring: high abrasion resistance, low temperature flexibility, ozone resistance, oil and fuel resistance, outst..
Tensile Strength, Yield	30.0 MPa	4350 psi	ASTM D638
UBE UMERIT 613A Metallocene LLDPE Description: UBE Super Polyethylene Umerit® is an ethylene-olefin copolymer made by UBE using the metallocene catalytic method. The metallocene catalytic method results in superior physical propert..
Tensile Strength, Yield	30.0 MPa	4350 psi	dry; ISO 527-1/-2
EMS-Grivory Grivory® AZ 3 PA66 Product description: Grilon AZ 3 is a normal viscosity, high impact modified PA66 injection molding grade. Grilon AZ 3 has the following important properties: Excellent toughness at low temperatures..
Tensile Strength, Yield	30.0 MPa	4350 psi	ASTM D638
Entec Hypro™ PPH-CC10 Natural Homopolymer Polypropylene, 10% Calcium Carbonate Filled Information provided by Entec
Tensile Strength, Yield	30.0 MPa	4350 psi	50 mm/min
Arkema Group Rilsan® AMN P30 LD Nylon 12, Flexible, Injection Grade (Dry) Designation ISO 1874-PA12-P,MLR,12-004Flexible grade for injection molding. Available color: black. Light stabilized. Mold-release agent.Good impact strength. Flexibility and dynamic properties. Eas..
Tensile Strength, Yield	30.0 MPa	4350 psi	ASTM D638
Aclo Accutech Polypropylene Homopolymer HP0334T40L Talc Reinforced
Tensile Strength, Yield	30.0 MPa	4350 psi	ASTM D638
Aclo Accutech Polypropylene Homopolymer HP0336C30L Calcium Reinforced
Tensile Strength, Yield	30.0 MPa @Temperature 120 °C	4350 psi @Temperature 248 °F	ISO Data
BASF Ultramid® 8202C PA6 (Dry) Ultramid 8202C is a modified crystalline and low viscosity, nylon 6 injection molding homopolymer. It is also available in heat stabilized (Ultamid 8202C HS) and/or pigmented versions. Its unique ..
Tensile Strength, Yield	30.0 MPa	4350 psi	ASTM D638
Aclo Accutech Polypropylene Homopolymer HP0339T40L Talc Reinforced
Tensile Strength, Yield	30.0 - 35.0 MPa	4350 - 5080 psi	50 mm/min; ASTM D638
Solvay Specialty Polymers Solef® 11008 PVDF Copolymer (discontinued **) Key features of this grade: Low Viscosity, Wire & Cable, Plenum, Formulated. Recommended processing is extrusion. Available as powder & granules.General information about SOLEF® PVDF: SOLEF® PVD..
Tensile Strength, Yield	30.0 MPa	4350 psi	ASTM value at 50 mm/min.
BASF Capron® 8253 Impact Modified Nylon 6 (Conditioned) (discontinued **) Capron 8253 is an unfilled type 6 graft copolymer developed for both injection molding and extrusion applications. It is also available in heat stabilized (Capron 8253 HS) and/or pigmented versions..
Tensile Strength, Yield	30.0 MPa @Temperature 23.0 °C	4350 psi @Temperature 73.4 °F	50mm/min; ISO 527-2/1A/50
SYNTHOS Krasten® 552M High Impact Polystyrene High impact grade with a wide range of Applications. Processed mainly by injection moulding. Production of consumer goods and technical parts subjected to increased mechanical stress. Good results i..
Tensile Strength, Yield	30.0 MPa	4350 psi	ASTM D638
A. Schulman POLYFORT™ FPP 1068-32 Black40% Mineral Filled Polypropylene DescriptionPolyfort® FPP 1068-32 Black is a 40% mineral filled polypropylene designed for use when improved heat resistance, dimensional stability and high stiffness is needed. ApplicationApplicati..