- Entec Hypro™ PPH-CC10 Natural Homopolymer Polypropylene, 10% Calcium Carbonate Filled
Entec Hypro™ PPH-CC10 Natural Homopolymer Polypropylene, 10% Calcium Carbonate Filled
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 10% Calcium Carbonate (CaCO3) Filler |
| Manufacturer | Entec Engineered Resins |
| Trade Name | Hypro™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Entec Hypro™ PPH-CC10 Natural Homopolymer Polypropylene, 10% Calcium Carbonate Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Entec
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.980 g/cc | 0.0354 lb/in³ | ASTM D792 |
| Melt Flow | 10.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
10.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 30.0 MPa | 4350 psi | ASTM D638 |
| Elongation at Break | 30.0 % | 30.0 % | ASTM D638 |
| Elongation at Yield | 8.00 % | 8.00 % | ASTM D638 |
| Flexural Strength | 37.0 MPa | 5370 psi | ASTM D790 |
| Flexural Modulus | 1.586 GPa | 230.0 ksi | tangent; ASTM D790 |
| Izod Impact, Notched | 0.370 J/cm @Thickness 3.17 mm |
0.693 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 93.0 °C | 199 °F | ASTM D648 |
Users viewing this material also viewed the following:
- Ravago Manufacturing Americas Hylex® P1018FRVNHE Polycarbonate
- ExxonMobil Escorene® LD-752 EVA Copolymer for Specialty Applications (discontinued **)
- Lucas-Milhaupt Silvaloy® A50 Brazing Alloy
- Special Metals INCONEL® 690 Nickel Superalloy, Hot Rolled Flat, 2.0 inch (51 mm) Diameter
- Polyram PlusTek PA340S8 Nylon 6.6 for Injection Molding, 40% Glass-beads Reinforced
- Westlake EB502 12.5% EVA Copolymer
- A. Schulman PP 1329H-01 Polypropylene Medium Impact Polypropylene
- 3M Scotch-Weld™ AC77 Instant Adhesive Primer
- Eastman Tenite 550E3V45510 Butyrate Water Clear, Trsp (discontinued **)
Copyright © lookpolymers.com All Rights Reserved