Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 28.3 MPa | 4100 psi | Type I, 51 mm/min; ASTM D638 |
PolyOne Maxxam™ FR PP FR 7A11 Polypropylene, Unspecified (PP, Unspecified) Maxxam™ FR flame-retardant polyolefin compounds and masterbatches meet stringent flammability performance requirements defined by industry agencies, including Underwriters Laboratories UL 94 V-2, V.. |
|||
Tensile Strength, Yield | 28.3 MPa | 4100 psi | (2 in/min); ASTM D638 |
Phillips 66 COPYLENE® CR020CL Polypropylene Impact Copolymer COPYLENE® CR020CL is a random copolymer formulated with advanced clarifier technology and with antistat and is specially designed to excel in extrusion blowmolding processes. EBM bottles will have .. |
|||
Tensile Strength, Yield | 28.3 MPa | 4100 psi | 2 in/min; ASTM D638 |
Phillips 66 COPYLENE® CR120LN Polypropylene, Random Copolymer, Nucleated COPYLENE™ CR120LN is a random copolymer nucleated and with antistat for good mold release in injection molding applications. Applications: Containers, Closures, HousewaresInformation provided by P.. |
|||
Tensile Strength, Yield | 28.3 MPa | 4100 psi | |
TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 60 PHR N650 Filler MILLATHANE CM is a sulfur and peroxide curable polyether urethane rubber. Its outstanding property is its great resistance to abrasion, which makes it of special interest for articles that are subje.. |
|||
Tensile Strength, Yield | 28.3 MPa | 4110 psi | Crosshead speed - 2"min.; ASTM D638 |
LyondellBasell Alathon® M5370 High Density Polyethylene ApplicationsALATHON M 5370 copolymer with narrow weight distribution. This resin provides high impact strength and stress crack resistance, excellent color, low odor and good processability. Typic.. |
|||
Tensile Strength, Yield | 28.3 MPa | 4110 psi | 2"/min; ASTM D638 |
LyondellBasell Alathon® M5370PX High Density Polyethylene, Extrusion Grade ALATHON M5370PX is a copolymer with a narrow molecular weight distribution. This resin provides high impact strength and stress crack resistance, excellent color, low odor and good processability. T.. |
|||
Tensile Strength, Yield | 28.3 MPa | 4110 psi | Crosshead speed - 2"min.; ASTM D638 |
LyondellBasell Alathon® M6580 High Density Polyethylene ApplicationsALATHON M 6580 is a narrow molecular weight distribution homopolymer that enhances processability and stiffness, exhibits excellent color, low odor and good processing stability. Typica.. |
|||
Tensile Strength, Yield | 28.3 MPa | 4100 psi | 2"/min; ASTM D638 |
LyondellBasell Lupolen® 5261 Z Q 456 B High Density Polyethylene, Pipe and Sheet Extrusion Grade Lupolen 5261 Z Q 456 B is a high density polyethylene (HDPE) with high melt viscosity for ram extrusion of peroxide crosslinked pipes (PE-Xa). The product is supplied as a nominal 20 mesh (840 um) p.. |
|||
Tensile Strength, Yield | 28.3 MPa | 4100 psi | 2 in/min; ASTM D638 |
Ineos B4020N1331 Polyethylene Copolymer This is a unique high density polyethylene copolymer intended for the injection or compression molding of closures for beverages. Because of its high purity and excellent organoleptic properties, t.. |
|||
Tensile Strength, Yield | 28.3 MPa | 4100 psi | ASTM D638 |
Ineos L12Z-00 Polypropylene Impact Copolymer Grade L12Z-00 is a medium melt flow rate, high stiffness and high impact polypropylene copolymer. This material meets the requirements of the U.S. Food and Drug Administration as specified in 21 CFR.. |
|||
Tensile Strength, Yield | 28.3 MPa | 4100 psi | 2 in/min; ASTM D638 |
Ineos R01A-00 Polypropylene Random Copolymer Random copolymer R01A-00 is an antistatic polypropylene produced by a unique catalyst technology. It is designed for blow molding and extrusion applications and exhibits good stiffness and improved .. |
|||
Tensile Strength, Yield | 28.3 MPa | 4100 psi | ASTM D638 |
LyondellBasell Alathon® L5876 High Density Polyethylene, Blow Molding Grade ALATHON L5876 is designed for injection blow molding and extrusion blow molding applications where higher gloss than standard grades is required. Regulatory Status: L5876 meets the requirements of t.. |
|||
Tensile Strength, Yield | 28.3 MPa | 4100 psi | ASTM D638 |
Techmer ES HiFill FR® ABS FR AS Availability: North AmericaForms: PelletsAdditive: AntistaticFeatures: Antistatic and Flame RetardantInformation provided by TP Composites, Inc. |
|||
Tensile Strength, Yield | 28.3 MPa | 4100 psi | ASTM D 638 |
Styrolution PS 7800 HIPS Extremely high surface glossGood processabilityUL Classification 94 HBInformation provided by Styrolution |
|||
Tensile Strength, Yield | 28.3 MPa | 4100 psi | 2 in/min; ASTM Test |
Styrolution Styrolux 3G33 SBC Styrolux 3G33 is a thermoplastic styrene-butadiene block copolymer which is suitable for injection molding, extrusion and thermoforming. It offers an outstanding combination of crystal clarity and .. |
|||
Tensile Strength, Yield | 28.3 MPa | 4100 psi | 2 in/min; ASTM Test |
Styrolution Styrolux HS 70 SBC Information provided by STYROLUTION, which is a joint venture between BASF and INEOS. |
|||
Tensile Strength, Yield | 28.3 MPa | 4100 psi | ASTM D638 |
A. Schulman PP 828S-01 Polypropylene Medium Impact Molding Grade Polypropylene DescriptionPolypropylene PP 828S-01 is a medium impact molding grade created for applications needing good impact and higher H.D.T., such as tote bins, automotive ducting and housings. Information p.. |
|||
Tensile Strength, Yield | 28.3 MPa | 4100 psi | ASTM D638 |
A. Schulman PP 1116-01 Polypropylene Molding Grade Copolymer Polypropylene DescriptionPolypropylene PP 1116-01 is a molding grade copolymer polypropylene with improved low temperature toughness and good room temperature toughness. Information provided by A. Schulman. |
|||
Tensile Strength, Yield | 28.3 MPa | 4100 psi | ASTM D638 |
Westlake Plastics Clariflex® TFE/VF2/HFP Clariflex is a flexible, transparent fluoroplastic composed of tetrafluoroethylene, hexafluoro-propylene, and vinylidene fluoride. Notable properties include light transmission, chemical resistance.. |
|||
Tensile Strength, Yield | 28.3 MPa | 4100 psi | ASTM D638 |
A. Schulman PP 828S-01 Polypropylene Medium Impact Molding Grade Polypropylene DescriptionPolypropylene PP 828S-01 is a medium impact molding grade created for applications needing good impact and higher H.D.T., such as tote bins, automotive ducting and housings. Information p.. |
|||
Tensile Strength, Yield | 28.3 MPa | 4100 psi | ASTM D638 |
A. Schulman PP 1817-01 Polypropylene Utility Grade Random Co-Polymer DescriptionPolypropylene PP 1817-01 is a utility grade random co-polymer which can be used for general purpose injection molding, extrusion, or blow molding applications. It does not have a gel spe.. |
|||
Tensile Strength, Yield | 28.3 MPa | 4100 psi | |
TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 30 PHR Suprex Clay Filler MILLATHANE CM is a sulfur and peroxide curable polyether urethane rubber. Its outstanding property is its great resistance to abrasion, which makes it of special interest for articles that are subje.. |
|||
Tensile Strength, Yield | 28.3 MPa | 4100 psi | ASTM D638 |
ExxonMobil HDPE HD 7800P High Density Polyethylene Copolymer Resin Product Description: HD 7800P is a pipe extrusion grade high density polyethylene copolymer offering an excellent combination of stiffness and stress crack resistance. This material meets or exceeds.. |
|||
Tensile Strength, Yield | 28.3 MPa | 4100 psi | ASTM D638 |
ExxonMobil HDPE HYA021L High Density Polyethylene Resin Product Description: HYA021L is a molecular weight, high-density polyethylene copolymer. This resin has superior stress crack resistance, high impact strength and good rigidity.Availability: Latin A.. |
|||
Tensile Strength, Yield | 28.3 MPa | 4100 psi | chs 2.0 in/min; ASTM D638 |
Diamond Polymers Centrex® 601 Profile Extrusion Grade AES Centrex 601 resin is a very high-impact, low-gloss AES (acrylonitrile-ethylene-propylene-styrene) resin with good resistance to weather aging. It has good melt strength for profile extrusion and can.. |
|||
Tensile Strength, Yield | 28.3 MPa | 4100 psi | ASTM D638 |
Dow 560.00 Developmental Performance Polypropylene Polymer OverviewConsistent processabilityExcellent gloss before and after thermoformingUV stabilized for increased weatherabilityD 560.00 Performance Polymer is designed as a co-extrusion cap layer for extr.. |
|||
Tensile Strength, Yield | 28.3 MPa | 4100 psi | ASTM D638 |
Dow 560.01 Developmental Performance Polypropylene Polymer OverviewConsistent processabilityHigh glossGood regrind stabilityContains U.V. stabilizers for increased weatherabilityD 560.01 Performance Polymer is intended for use in extrusion blow molding, she.. |
|||
Tensile Strength, Yield | 28.3 MPa | 4100 psi | ASTM D638 |
Albis Plastics Cellulose Acetate Butyrate B900 (Base Grade), 10% Plasticizer
(discontinued **) Amorphous Cellulose Acetate Butyrate (CAB)Characteristics: Dimensional Stability, Weatherability and Low Temp Impact StrengthApplications: Pens, Ski Goggles, Auto Trim, Skylights, Tool Handles and T.. |
|||
Tensile Strength, Yield | 28.3 MPa | 4100 psi | ASTM D638 |
Albis Plastics Cellulose Acetate Butyrate B902 (UV Inhibitor Added), 10% Plasticizer
(discontinued **) Amorphous Cellulose Acetate Butyrate (CAB)Characteristics: Dimensional Stability, Weatherability and Low Temp Impact StrengthApplications: Pens, Ski Goggles, Auto Trim, Skylights, Tool Handles and T.. |
|||
Tensile Strength, Yield | 28.3 MPa | 4100 psi | ASTM D638 |
Lubrizol Stat-Rite® SIS535 Static Control System Product Description: Stat-Rite® SIS535 is a static dissipative HIPS alloy. Stat-Rite SIS535 utilizes the patented Stat-Rite inherently dissipative polymer (IDP) alloy system to provide clean, perma.. |