Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 150 MPa | 21800 psi | ISO 527, ASTM D638 |
Nilit Nilamid A3 H G4 General Purpose 20% Glass Reinforced PA66 Description: Nilamid A3 H G4 is a general purpose, 20% glass fiber reinforced NYLON 66. This product combine good overall mechanical performance and impact strength with ease of processing.Key chara.. |
|||
Tensile Strength, Yield | 150 MPa | 21800 psi | ISO 527-2/1A/5 |
Solvay Specialty Polymers KetaSpire® KT-820 SL30 Polyetheretherketone (PEEK)
(Unverified Data**) Ketaspire KT-820 SL30 is a polyetheretherketone (PEEK) compound designed to provide a balance of excellent mechanical properties, wear resistance and low coefficient of friction in both dry and exte.. |
|||
Tensile Strength, Yield | 150 - 240 MPa | 21800 - 34800 psi | Average value: 202 MPa Grade Count:48 |
Overview of materials for Nylon 6, 50% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, 50% Glass Fiber Filled". Specific grades with glass content between 45% and 54% are included. E.. |
|||
Tensile Strength, Yield | 150 MPa @Temperature 22.0 °C |
21800 psi @Temperature 71.6 °F |
25mm flat samples, compression moulded; ISO 527-4 |
Menzolit Menzolit® SMC 1100 Unsaturated Polyester UP SMC 1100 is a special vinylester SMC for high strength applications. The reinforcement has been put to a level that combines mouldability with high strength and stiffness properties. The specific re.. |
|||
Tensile Strength, Yield | 150 MPa | 21800 psi | ISO 527 |
Solvay Technyl® A 218 V35 Nylon 66, 35% Glass Fiber, EH50 Polyamides PA66, reinforced with 35% of glass fiber, heat stabilized, for injection molding.Technyl A 218 V35 is used in all sectors of industry, offering an excellent combination between thermal an.. |
|||
Tensile Strength, Yield | 150 MPa | 21800 psi | 5 mm/min, Type 1A; ISO 527-2 |
Solvay Specialty Polymers KetaSpire® KT-820 SL30 Polyetheretherketone (PEEK) KetaSpire® KT-820 SL30 is a polyetheretherketone (PEEK) compound designed to provide a balance of excellent mechanical properties, wear resistance and low coefficient of friction in both dry and .. |
|||
Tensile Strength, Yield | 150 MPa | 21800 psi | ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP QF0069 PA6.10 LNP* THERMOCOMP* QF0069 is a compound based on Nylon 6/10 resin containing 30% Glass Fiber. Added features of this material include: Flame Retardant. |
|||
Tensile Strength, Yield | 150 MPa | 21800 psi | ISO 527-2/1A |
Suzhou Hipro Polymers Hiprolon® 70 MC HLS G30 Nylon 610, 30% glass fiber filled Hiprolon® 70 MC HLS G30 polyamide 6.10 compound reinforced with 30% chopped glass fiber for injection molding. Features: high heat resistance, dimension stability, impact resistance, good flow ab.. |
|||
Tensile Strength, Yield | 150 MPa | 21800 psi | ASTM-D638 |
Polyram PB302G50 Nylon 6, 50% Glass Fiber 50% glass fiber reinforced, UV and heat stabilized polyamide approved and listed by W.R.C potable water and NSF/ANSI61 internationalInformation provided by Polyram Ram On Ind. |
|||
Tensile Strength, Yield | 150 MPa | 21800 psi | ASTM-D638 |
Polyram PlusTek PA320G6 Nylon 6.6, 30% Glass Fiber, Flame Retardant 30% glass fiber reinforced, flame retardant polyamide 6.6 for injection molding applicationsInformation provided by Polyram Ram On Ind. |
|||
Tensile Strength, Yield | 150 MPa | 21800 psi | ASTM-D638 |
Polyram PlusTek PA323G6 Nylon 6.6, 30% Glass Fiber, Flame Retardant 30% glass fiber reinforced, flame retardant polyamide 6.6 for injection molding applicationsInformation provided by Polyram Ram On Ind. |
|||
Tensile Strength, Yield | 150 MPa | 21800 psi | ISO 527 |
Polyram PlusTek RA325G6 Nylon 66 for Injection Molding, 30% Glass-Fiber Reinforced, Flame Retardant, Halogen Free 30% Glass-fiber reinforced, flame retardant halogen free Nylon 66 for injection molding applications.Information provided by Polyram. |
|||
Tensile Strength, Yield | >= 150 MPa | >= 21800 psi | ASTM-D638 |
Polyram PlusTek RA334G6 Nylon 6.6, 30% Glass Fiber 30% glass fiber reinforced polyamide 6.6 for injection molding applicationsInformation provided by Polyram Ram On Ind. |
|||
Tensile Strength, Yield | 150 MPa | 21800 psi | ISO 527-2 |
Tisan TISESTER® 30% Glass Fiber Reinforced, Flame Retardant (V0). Heat Stabilized. Polybutylene Terephthalate TISESTER has a wide area of application in automotive, electric/electronics and durable goods industries. General Specifications include: Excellent surface appearanceHigh corrosion and abrasion resi.. |
|||
Tensile Strength, Yield | 150 MPa | 21800 psi | ISO 527-2 |
Tisan TISLAMID® 66 20% Glass Fiber Reinforced Nylon 66 TISLAMID has a wide area of application in electric/electronic, automotive, durable goods and telecommunications industries. It demonstrates characteristics such as Excellent chemical resistanceElec.. |
|||
Tensile Strength, Yield | 150 MPa | 21800 psi | ASTM-D638 |
Polyram Polytron P60B11 Homopolymer Polypropylene, Chemically Coupled 60% LGF A chemically coupled 60% LGF reinforced black PP, heat stabilized for injection molding applications.Information provided by Polyram Ram On Ind. |
|||
Tensile Strength, Yield | 150 MPa | 21800 psi | ISO 527 |
Polyram PlusTek PB300G4 Nylon 6 for Injection Molding, 20% Glass-Fiber Reinforced 20% Glass fiber reinforced, heat stabilized Nylon 6 for injection molding applications.Information provided by Polyram. |
|||
Tensile Strength, Yield | 150 MPa | 21800 psi | ASTM-D638 |
Polyram PlusTek RA301G6 Nylon 6.6, 30% Glass Fiber 30% glass fiber reinforced, heat stabilized polyamide 6.6 for injection molding applicationsInformation provided by Polyram Ram On Ind. |
|||
Tensile Strength, Yield | 150 MPa | 21800 psi | ISO 527 |
Polyram RamSter PF300G9 PBT, 45% Glass Fiber 45% Glass fiber reinforced PBT for injection molding applications.Information provided by Polyram. |
|||
Tensile Strength, Yield | >= 150 MPa @Strain 0.200 % |
>= 21800 psi @Strain 0.200 % |
|
CLAL-MSX NICLAL 1300 0 Annealed Copper Alloy, Free Cutting Nickel-Silver Main Characteristics: Good ductilityGood corrosion resistanceTypical Applications:High volume turned partsKeysInformation provided by CLAL-MSX |
|||
Tensile Strength, Yield | 150 MPa | 21800 psi | ASTM D638 |
E-Polymers Tekaster® F615GFR , Flame Retardant, 30% Glass Reinforced PET 30% Glass Fiber Reinforced, Flame RetardantInformation provided by E-Polymers Co. Ltd. |
|||
Tensile Strength, Yield | 150 MPa | 21800 psi | ISO 527-2 |
Ascend Performance Materials Vydyne® R535 Nylon 66, 35% Glass Reinforced, Conditioned Vydyne® R535 is general-purpose, hydrolysis-resistant, 35% glass-fiber reinforced PA66 resin. This product is lubricated for improved flow and offers superior surface appearance. Glass-reinforced V.. |
|||
Tensile Strength, Yield | 150 MPa | 21800 psi | 50mm/min; ISO 527 |
BASF Ultramid® B3ZG6 30% Glass Filled PA6 (Dry) Ultramid B3ZG6 is an impact-modified, 30% glass fiber reinforced injection molding PA6 grade for industrial items having very high impact strength and rigidity. |
|||
Tensile Strength, Yield | 150 MPa | 21800 psi | 50 mm/min; ISO 527-1/-2 |
BASF Ultramid® KR 4365 G5 35% Glass Filled PA6/6T FR (Dry) Description: Partially aromatic polyamide; flame retardant based on red phosphorus; low water absorption, high melting point (295°C); low tendency to form deposits on electrical contacts, very resi.. |
|||
Tensile Strength, Yield | 150 MPa @Temperature 700 °C |
21800 psi @Temperature 1290 °F |
R<sub>p</sub>02 |
Assab Steels 8407 2M Hot Work Steel ASSAB 8407 is a chromium-molybdenum-vanadium-alloyed steel which is characterized by: Good resistance to abrasion at both low and high temperatures. High level of toughness and ductility Uniform .. |
|||
Tensile Strength, Yield | 150 MPa | 21800 psi | 50mm/min; ISO 527 |
BASF Ultramid® A3EG7 35% Glass Filled PA66 (Conditioned) Ultramid A3EG6 is a 35% glass fiber reinforced injection molding PA66 grade for machinery components and housings of high stiffness and dimensional stability. |
|||
Tensile Strength, Yield | 150 MPa | 21800 psi | ASTM D638 |
LNP Thermocomp® QF-1006 Polyamide 6/10 Copolymer, Glass Fiber Reinforcement
(discontinued **) Forms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP grades are still active under new names.. |