Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Film Tensile Strength at Break, MD | 24.0 MPa | 3480 psi | ISO 527-3 |
Polimeri Europa Riblene® FH 10 Low Density Polyethylene - Blown Film Extrusion Riblene FH 10 is a low density polyethylene (LDPE) suitable for blown film extrusion. Riblene FH 10 is characterized by a good balance between processability and mechanical properties.Films manufac.. |
|||
Film Tensile Strength at Break, MD | 24.0 MPa | 3480 psi | ISO 527-3 |
Polimeri Europa Riblene® FL 23 Low Density Polyethylene - Blown Film Extrusion Riblene FL 23 is a low density polyethylene (LDPE) with added slip agent, suitable for blown film extrusion. Riblene FL 23 is characterized by a good balance between processability and mechanical p.. |
|||
Film Tensile Strength at Break, MD | 24.0 MPa | 3480 psi | ISO 527 |
Premix Thermoplastics PRE-ELEC® PE 1271 PRE-ELEC PE 1271 is a conductive thermoplastic compound based on a blend of PE-LD/PE-LLD. Conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivi.. |
|||
Film Tensile Strength at Break, MD | 24.0 MPa | 3480 psi | ISO 527 |
Premix Thermoplastics PRE-ELEC® PE 1308
(discontinued **) PRE-ELEC PE 1308 is a conductive thermoplastic compound based on a blend of PE-LD/PE-LLD. Conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivi.. |
|||
Film Tensile Strength at Break, MD | 24.0 MPa | 3480 psi | ASTM D882 |
Eastman E6838-997F Polyethylene
(discontinued **) E6838-997F natural is a low density formulation with no slip or antiblock. Outstanding optical properties make this material an excellent choice for calendering and as a clarity filler in co-extrud.. |
|||
Film Tensile Strength at Break, MD | 24.0 MPa | 3480 psi | ASTM D882 |
ExxonMobil Escorene® LD-133 LDPE Packaging Film Resin
(discontinued **) Data provided by the manufacturer, Exxon Chemical.A homopolymer film resin with good clarity. It is suitable for processing in blown film equipment and can be drawn down to 1.0 mil.Applications: Fo.. |
|||
Film Tensile Strength at Break, MD | 24.0 MPa | 3480 psi | ASTM D882 |
NOVA Chemicals Novapol® LF-Y824-C LDPE Clarity Film Resin
(discontinued **) Features: High optical clarityExcellent processabilityExcellent shrink film characteristics Applications: High clarity shrink filmProduce and bakery filmTextile packaging filmInformation provided by.. |
|||
Film Tensile Strength at Break, MD | 24.0 MPa | 3480 psi | ASTM D882 |
ExxonMobil Escorene® CR-5810 EVA Resin, for High Cling Stretch Film
(discontinued **) Data provided by the manufacturer, Exxon Chemical.A tackified Ethylene Vinyl Acetate resin for blown or cast stretch film.Applications: Packing films (cling). Data for film properties below based o.. |
|||
Film Tensile Strength at Break, MD | 24.0 MPa | 3480 psi | ASTM D882 |
ExxonMobil Escorene® LD-144 EVA Film Resin
(discontinued **) Data provided by the manufacturer, Exxon Chemical.A 2% vinyl acetate copolymer packaging film resin. Film made from LD-144 offers improved impact strength and heat sealability compared to homopolym.. |
|||
Film Tensile Strength at Break, MD | 24.0 MPa | 3480 psi | ASTM D882 |
ExxonMobil Escorene® LD-307 EVA Film Resin, Clarity, High Impact
(discontinued **) Data provided by the manufacturer, Exxon Chemical.A 5.0% vinyl acetate copolymer, clarity film resin. Film made from this resin has superior impact strength and heat sealability.Applications: Froze.. |
|||
Film Tensile Strength at Break, MD | 24.0 MPa | 3480 psi | ASTM D882 |
ExxonMobil Escorene® LD-314 EVA Packaging Film Resin
(discontinued **) Data provided by the manufacturer, Exxon Chemical.A 3.5% vinyl acetate copolymer resin for higher clarity films. Film made from LD-314 offers good impact strength, heat sealability, and low tempera.. |
|||
Film Tensile Strength at Break, MD | 24.0 MPa | 3480 psi | ASTM D882 |
Huntsman PE1503 EVA Film Extrusion
(discontinued **) 5% Vinyl Acetate EVA copolymer and FDA compliantFeatures: Excellent balance of optical and strength, toughness and flexibility at low temperatures, and good heat seal characteristic.Applications: Fi.. |
|||
Film Tensile Strength at Break, MD | 24.0 MPa | 3480 psi | ASTM D882 |
Huntsman PE1504 EVA Film Extrusion
(discontinued **) 5% Vinyl Acetate EVA copolymer and FDA compliantFeatures: Excellent balance of optical and strength, toughness and flexibility at low temperatures, and good heat seal characteristic.Applications: Fi.. |
|||
Film Tensile Strength at Break, MD | 24.0 MPa | 3480 psi | ASTM D882 |
Huntsman PE1753 EVA Film Extrusion
(discontinued **) 7.5% Vinyl Acetate EVA copolymer and FDA compliantFeatures: Yields film with good clarity and excellent impact strength.Applications: Film extrusion: icebags, liquid packaging, lamination film, and .. |
|||
Film Tensile Strength at Break, MD | 24.0 MPa | 3480 psi | ISO 1184 |
Carmel Olefins IPETHENE® 214 Low Density Polyethylene
(discontinued **) IPETHENE® 214 is a general purpose low density polyethylene film extrusion grade. It contains a high level of anti-blocking and slip additives. It is BHT free. APPLICATIONS IPETHENE® 214 is main.. |
|||
Film Tensile Strength at Break, MD | 24.0 MPa | 3480 psi | ASTM D882 |
SCG Chemicals EL-Leneâ„¢ LD2305F Low Density Polyethylene Film Key Characteristics:Excellent clarity and glossGood zip formationContains 1000 ppm slip agent and 500 ppm antiblocking agentRecommended Applications:Zip bagsGeneral purpose film for food packagingIn.. |
|||
Film Tensile Strength at Break, MD | 24.0 MPa | 3480 psi | ISO 527-3 |
Borealis FA7220 Low Density Polyethylene FA7220 is a Low Density Polyethylene for Film Extrusion. Includes Antioxidant. This grade is developed for production of blown film or cast film with good optical properties. When cast on a polish.. |
|||
Film Tensile Strength at Break, MD | 24.0 MPa | 3480 psi | ISO 527-3 |
Borealis Himod™ FT6273 LDPE for Film Himod FT6273 is a tubular, low-density polyethylene grade for the production of packaging films. Compared to standard LDPE grades, the Himod products provide a combination of higher stiffness and i.. |
|||
Film Tensile Strength at Break, MD | 24.0 MPa | 3480 psi | ISO 527-3 |
Borealis Himod™ FT6274 LDPE for Film Himod FT6274 is a tubular, low-density polyethylene grade for the production of packaging films. Compared to standard LDPE grades, the Himod products provide a combination of higher stiffness and i.. |
|||
Film Tensile Strength at Break, MD | 24.0 MPa | 3480 psi | 50 µm (2 mil) film; ASTM D882 |
DuPont Elvax® 3165 Ethylene-Vinyl Acetate Copolymer Resin for Coextrusion, Blown Film 18 wt% Vinyl Acetate.Elvax® 3165 is an extrudable ethylene-vinyl acetate copolymer resin available in pellet form for use in conventional extrusion equipment designed to process polyethylene resins.. |
|||
Film Tensile Strength at Break, MD | 24.0 MPa | 3480 psi | ASTM D882 |
Westlake Elevate™ EF437 2.5% Ethylene Vinyl Acetate Copolymer Westlake EF437 resin is a 2.5% EVA copolymer designed for films that require excellent optical and strength properties. This Kosher compliant resin has excellent heat sealing characteristics and low.. |
|||
Film Tensile Strength at Break, MD | 24.0 MPa | 3480 psi | ASTM D882 |
DuPont™ Surlyn® 1652 Zinc Ionomer Resin for Flexible Packaging Surlyn® 1652 is an ionomer resin available for use in blown/cast film and extrusion coating operations. It can be used in both extrusion and coextrusion equipment designed to process polyethylene .. |
|||
Film Tensile Strength at Break, MD | 24.0 MPa | 3480 psi | ASTM D882 |
ExxonMobil LD 316.19 High Clarity, High Impact Film Resin LD 316.19 has improved impact strength and heat sealability versus homopolymer clarity film resins. Applications include frozen and other food packaging, as well as profile extrusion.Information pr.. |
|||
Film Tensile Strength at Break, MD | 24.0 MPa | 3480 psi | ASTM-D882 |
Braskem TN2020 EVA General Film Copolymer TN2020 is an Ethylene-Vinyl Acetate (EVA) copolymer developed to mostly meet the needs of the multi-layer packaging segment produced by coextrusion and/or lamination processes. Multilayer structures.. |
|||
Film Tensile Strength at Break, MD | 24.0 MPa | 3480 psi | ASTM D-882 |
Bapolene® 200B Polyethylene, Film Extrusion Bapolene 200B is a low density polyethylene for blown film applications requiring superior clarity. It complies with US FDA 21CFR177.1520.Applications: General purpose, bakery, flexible, medical an.. |
|||
Film Tensile Strength at Break, MD | 24.0 MPa | 3480 psi | ISO 1184 |
Carmel Olefins IPETHENE® 213 Low Density Polyethylene IPETHENE® 213 is a general purpose low density polyethylene film extrusion grade. It contains a medium level of anti-blocking and slip additives. It is BHT free. It exhibits a good balance between .. |
|||
Film Tensile Strength at Break, MD | 24.0 - 41.0 MPa | 3480 - 5950 psi | Average value: 32.0 MPa Grade Count:17 |
Overview of materials for Ionomer, Film Grade This property data is a summary of similar materials in the MatWeb database for the category "Ionomer, Film Grade". Each property range of values reported is minimum and maximum values of appropriat.. |
|||
Film Tensile Strength at Break, MD | 24.0 MPa | 3480 psi | 500 mm/min; ISO 527-3 |
DuPont Elvaloy® 3107 AC Ethylene and 7% Butyl Acrylate Copolymer
(discontinued **) Elvaloy® 3107 AC contains antioxidant, slip and antiblock additives.Elvaloy® 3107 AC is developed to give films with good sealing properties, impact strength at lower temperature, and low shrinkag.. |
|||
Film Tensile Strength at Break, MD | 24.0 - 25.0 MPa | 3480 - 3630 psi | Average value: 24.3 MPa Grade Count:3 |
Overview of materials for Ethylene Butyl Acrylate This property data is a summary of similar materials in the MatWeb database for the category "Ethylene Butyl Acrylate". Each property range of values reported is minimum and maximum values of approp.. |
|||
Film Tensile Strength at Break, MD | 24.0 MPa | 3480 psi | 500 mm/min; ISO 527-3 |
DuPont Elvaloy® 3108 AC Ethylene and 7% Butyl Acrylate Copolymer
(discontinued **) Elvaloy® 3108 AC contains antioxidant, slip and antiblock additives.Elvaloy® 3108 AC is developed to give films with good sealing properties, impact strength at lower temperature, and low shrinkag.. |