ExxonMobil LD 316.19 High Clarity, High Impact Film Resin

Category Polymer , Film , Thermoplastic , Ethylene Vinyl Acetate , Ethylene Vinyl Acetate Copolymer (EVA), Film Grade
Manufacturer Exxon Chemical
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil LD 316.19 High Clarity, High Impact Film Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LD 316.19 has improved impact strength and heat sealability versus homopolymer clarity film resins. Applications include frozen and other food packaging, as well as profile extrusion.Information provided by ExxonMobil Chemical
Physical Properties Metric English Comments
Density 0.924 g/cc
0.0334 lb/in³
ExxonMobil Method
Vinyl Acetate Content 2.0 %
2.0 %
ExxonMobil Method
Melt Flow 2.2 g/10 min
2.2 g/10 min
ExxonMobil Method
Antiblock Level 2100 ppm
2100 ppm
Slip Level 700 ppm
700 ppm
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 9.79 MPa
1420 psi
at 2% offset; ASTM D882
Film Tensile Strength at Yield, TD 9.72 MPa
1410 psi
at 2% offset; ASTM D882
Film Elongation at Break, MD 200 %
200 %
ASTM D882
Film Elongation at Break, TD 560 %
560 %
ASTM D882
Film Elongation at Yield, MD 6.4 %
6.4 %
ASTM D882
Film Elongation at Yield, TD 5.4 %
5.4 %
ASTM D882
Elmendorf Tear Strength MD 290 g
290 g
ASTM D1922
Elmendorf Tear Strength TD 150 g
150 g
ASTM D1922
Dart Drop Test 120 g
0.265 lb
ASTM D1709
Film Tensile Strength at Break, MD 24.0 MPa
3480 psi
ASTM D882
Film Tensile Strength at Break, TD 20.4 MPa
2960 psi
ASTM D882
1% Secant Modulus, MD 183 MPa
26600 psi
ASTM D882
1% Secant Modulus, TD 215 MPa
31200 psi
ASTM D882
Thermal Properties Metric English Comments
Melting Point 108 °C
227 °F
Peak Melting Temperature; ExxonMobil Method
Crystallization Temperature 96.0 °C
205 °F
ExxonMobil Method
Vicat Softening Point 93.9 °C
201 °F
ASTM D1525
Optical Properties Metric English Comments
Haze 5.2 %
5.2 %
ASTM D1003
Gloss 77 %
77 %
45°; ASTM D2457
Transmission, Visible 90 %
90 %
clear; thickness not quantified
Descriptive Properties Value Comments
Features Thermal Stabilizer