Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 32.4 MPa | 4700 psi | 2 in/min; ASTM D638 |
RheTech Products M15P100-01A 15% Mica Reinforced Polypropylene, Black Applications: Fan shroudsAir ductsElectronicsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Tensile Strength at Break | 32.4 MPa | 4700 psi | 2 in/min; ASTM D638 |
RheTech Products P107-00 Polypropylene Homopolymer, Natural Applications: Wire harnessesTrim componentsUnderhood componentsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Tensile Strength at Break | 32.4 MPa | 4700 psi | 2 in/min; ASTM D638 |
RheTech Products T15P100-00 12% Talc Reinforced Polypropylene, Natural Applications: Component housingConsumer goodsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Tensile Strength at Break | 32.4 MPa | 4700 psi | |
Indium Corp. Indalloy 153 Tin-Lead Solder Alloy Information Provided by Indium Corporation |
|||
Tensile Strength at Break | 32.4 MPa | 4700 psi | 5 mm/min; ASTM D638 |
Samsung Cheil Industries Starex® HF-0690M ABS, Unreinforced Information provided by Samsung Cheil Industries. |
|||
Tensile Strength at Break | 32.4 MPa | 4700 psi | 50 mm/min; ASTM D638 |
Samsung Cheil Industries Starex® LX-0981 ABS, Unreinforced Metallic-Look Luminous Grade - gives aesthetics of a painted surface without painting. Reduces time, cost, and environmental hazards (such as soilvents).Information provided by Samsung Cheil Industries. |
|||
Tensile Strength at Break | 32.4 MPa | 4700 psi | 5 mm/min; ASTM D638 |
Samsung Cheil Industries Starex® SF-0505HWR MABS, Unreinforced Scratch Resistant Information provided by Samsung Cheil Industries. |
|||
Tensile Strength at Break | 32.4 MPa | 4700 psi | 5 mm/min; ASTM D638 |
Samsung Cheil Industries Starex® SR-0315 V ABS, Unreinforced Heat Resistant Information provided by Samsung Cheil Industries. |
|||
Tensile Strength at Break | 32.4 MPa | 4700 psi | 5 mm/min; ASTM D638 |
Samsung Cheil Industries Starex® HF-0690M ABS, Unreinforced Information provided by Samsung Cheil Industries. |
|||
Tensile Strength at Break | 32.4 MPa | 4700 psi | 50 mm/min; ASTM D638 |
Samsung Cheil Industries Starex® LX-0981 ABS, Unreinforced Metallic-Look Luminous Grade - gives aesthetics of a painted surface without painting. Reduces time, cost, and environmental hazards (such as soilvents).Information provided by Samsung Cheil Industries. |
|||
Tensile Strength at Break | 32.4 MPa | 4700 psi | 5 mm/min; ASTM D638 |
Samsung Cheil Industries Starex® SF-0505HWR MABS, Unreinforced Scratch Resistant Information provided by Samsung Cheil Industries. |
|||
Tensile Strength at Break | 32.4 MPa | 4700 psi | 5 mm/min; ASTM D638 |
Samsung Cheil Industries Starex® SR-0315 V ABS, Unreinforced Heat Resistant Information provided by Samsung Cheil Industries. |
|||
Tensile Strength at Break | 32.4 MPa | 4700 psi | ASTM D638 |
Chase Plastics CP Pryme® NN300STL (COND, 50% RH) Nylon 66 (Utility Grade), Super Toughened, Internally Lubricated Information provided by Chase Plastics. |
|||
Tensile Strength at Break | 32.4 MPa @Temperature 22.8 °C |
4700 psi @Temperature 73.0 °F |
ASTM D638 |
Ensinger TECAFINE™ PP Polypropylene (PP) TECAFINE™ PP is an anti-stated, polypropylene, random copolymer polyolefin engineering plastic providing excellent chemical resistance and high purity. FDA compliant with better mechanical propert.. |
|||
Tensile Strength at Break | 32.4 MPa | 4700 psi | vs. steel; 90 s set time |
Elmer's Products Aron Alpha® 403T Cyanoacrylate Adhesive (Industrial Krazy Glue™) Extra tough adhesives with highest heat, peeling, impact and thermal shock resistance.High gap fill. Ethyl base monomer. Excellent on rubber/plastic substrates. Excellent on metal substrates. Fa.. |
|||
Tensile Strength at Break | 32.4 MPa | 4700 psi | ASTM D638 |
Plastics Group Polifil® T-30 30% Talc-Reinforced Polypropylene Polifil® T series compounds are homopolymer polypropylene resins reinforced with asbestos-free talc. They possess high flex modulus, high deflection temperature, good chemical resistance and colora.. |
|||
Tensile Strength at Break | 32.4 MPa | 4700 psi | 2 in/min; ASTM D638 |
RheTech Products HP501-01 High Performance Polypropylene Copolymer, Non-UV Stabilized, Black Applications: Battery traysInterior TrimInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Tensile Strength at Break | 32.4 MPa | 4700 psi | ASTM D638 |
PlastxWorld CEVIAN® A1300 PA/ABS Alloy, Conditioned Property data is for samples at equilibrium moisture (2.0%)Information provided by PlastxWorld Inc. |
|||
Tensile Strength at Break | 32.4 MPa @Thickness 2.00 mm |
4700 psi @Thickness 0.0787 in |
50mm/min; ASTM D638 |
LG Chemical KEYFLEX BT S5035 Ester Type TPE Description: Injection Molding, TPC-ET, Airbag Cover Deployment, Medium Modulus, Black ColorApplication: Airbag Cover (DAB, PAB, KAB, SAB)CAS: 37282-12-5, 24968-12-5 and 1333-86-4Information provide.. |
|||
Tensile Strength at Break | 32.4 MPa | 4700 psi | ASTM D638 |
Chase Plastics CP Pryme® PPH100-18M Polypropylene Homopolymer, 18 Melt Flow Information provided by Chase Plastics. |
|||
Tensile Strength at Break | 32.4 MPa | 4700 psi | 2 in/min; ASTM D638 |
RheTech Products HP501-00 High Performance Polypropylene Copolymer, Non-UV Stabilized, Natural Applications: Battery traysInterior TrimInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Tensile Strength at Break | 32.4 MPa | 4700 psi | 2 in/min; ASTM D638 |
RheTech Products M20P100-01A 20% Mica Reinforced Polypropylene, Black Applications: Fan shroudsFiller panelsAir ductsInjection molding conditions reported in table.Information provided by RheTech Products. |