- Acrylonitrile Butadiene Styrene (ABS), Heat Resistant, Molded
- Samsung Cheil Industries Starex® SR-0315 V ABS, Unreinforced Heat Resistant
Samsung Cheil Industries Starex® SR-0315 V ABS, Unreinforced Heat Resistant
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Heat Resistant, Molded |
| Manufacturer | Samsung, Cheil Industries |
| Trade Name | Starex® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samsung Cheil Industries Starex® SR-0315 V ABS, Unreinforced Heat Resistant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Samsung Cheil Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.04 g/cc | 1.04 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Transverse | 0.0020 - 0.0050 cm/cm @Thickness 3.20 mm |
0.0020 - 0.0050 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 26 g/10 min @Load 10.0 kg, Temperature 220 °C |
26 g/10 min @Load 22.0 lb, Temperature 428 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 109 | 109 | ASTM D785 |
| Tensile Strength at Break | 32.4 MPa | 4700 psi | 5 mm/min; ASTM D638 |
| Tensile Strength, Yield | 39.2 MPa | 5690 psi | 5 mm/min; ASTM D638 |
| Elongation at Break | 41 % | 41 % | 5 mm/min; ASTM D638 |
| Tensile Modulus | 2.16 GPa | 313 ksi | 5 mm/min; ASTM D638 |
| Flexural Strength | 62.8 MPa | 9110 psi | 2.8 mm/min; ASTM D790 |
| Flexural Modulus | 2.16 GPa | 313 ksi | 2.8 mm/min; ASTM D790 |
| Izod Impact, Notched | 2.06 J/cm @Thickness 6.35 mm |
3.86 ft-lb/in @Thickness 0.250 in |
ASTM D256 |
| 2.45 J/cm @Thickness 3.17 mm |
4.59 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 99.0 °C @Thickness 6.40 mm |
210 °F @Thickness 0.252 in |
ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 90.0 °C @Thickness 6.40 mm |
194 °F @Thickness 0.252 in |
ASTM D648 |
| Vicat Softening Point | 102 °C | 216 °F | B/50; ISO R306 |
| 104 °C | 219 °F | B/120; ISO R306 |
Users viewing this material also viewed the following:
- Abatron AboCast 8-22/Abocure 8-22 Epoxy (discontinued **)
- Kinlead LSS12 Low Temperature Grade Heat Sealable Film (thickness: 30 µm)
- LG Chemical LS100S PVC
- A. Schulman POLYBATCH™ White LL8425 AP Concentrate Based In LLDPE
- Polyplastics Duranex® 3405 Polybutylene Terephthalate (PBT), Standard, 45% GF filled
- BASF Procom® T40H 564 Polypropylene
- Radici Radilon® A RV300 990 (dry) Nylon 66
Copyright © lookpolymers.com All Rights Reserved