Plastics Group Polifil® T-30 30% Talc-Reinforced Polypropylene

Category	Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 30% Talc Filler
Manufacturer	The Plastics Group of America
Trade Name	Polifil®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Plastics Group Polifil® T-30 30% Talc-Reinforced Polypropylene.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Polifil® T series compounds are homopolymer polypropylene resins reinforced with asbestos-free talc. They possess high flex modulus, high deflection temperature, good chemical resistance and colorability, low shrinkage and yield maximum stiffness combined with characteristic impact.Applications: Automotive (underhood) applicationsMajor appliancesElectrical goodsHousewaresStandard processing techniques are applicable. Information provided by The Plastics Group.

Physical Properties	Metric	English	Comments
Density	1.15 g/cc	0.0415 lb/in³	ASTM D792
Filler Content	30 %	30 %	ASTM D2584
Linear Mold Shrinkage	0.0090 cm/cm @Thickness 1.59 mm	0.0090 in/in @Thickness 0.0625 in	ASTM D955
Melt Flow	8.0 - 12 g/10 min	8.0 - 12 g/10 min	230/2.16; May be specified; ASTM D1238

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	97	97	ASTM D785
Tensile Strength at Break	32.4 MPa	4700 psi	ASTM D638
Flexural Modulus	2.41 GPa	350 ksi	Tangent; ASTM D790
Izod Impact, Notched	0.267 J/cm	0.500 ft-lb/in	At 73°F; ASTM D256
Izod Impact, Unnotched	2.72 J/cm	5.10 ft-lb/in	At 73°F; ASTM D256
Gardner Impact	0.565 J	0.417 ft-lb	ASTM D3029

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	132 °C	270 °F	ASTM D648