- Polymer Property : Tensile Strength at Break = 4640 psi
Polymer Property : Tensile Strength at Break = 4640 psi Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 32.0 MPa | 4640 psi | 50 mm/min; ASTM D638 |
| Ovation Polymers Nemcon™ H ABS DP116P ABS ABS-Thermally conducting, electrically insulating grade with high HDT and improved processability.Information provided by Ovation Polymers |
|||
| Tensile Strength at Break | 32.0 MPa | 4640 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics LNP Faradex AS0039 ABS (Europe-Africa-Middle East) LNP* Faradex* AS0039 is a compound based on Acrylonitrile Butadiene Styrene resin containing Flame Retardant, Stainless Steel Fiber. Added features of this material include: EMI/RFI Shielding.This .. |
|||
| Tensile Strength at Break | <= 32.0 MPa | <= 4640 psi | ISO/R527 |
| Polykemi AB POLYfill PPC 200 E20 Polypropylene Copolymer, Elastomer Modified Information provided by Polykemi AB |
|||
| Tensile Strength at Break | 32.0 MPa | 4640 psi | ISO 527 |
| SABIC Innovative Plastics LNP LUBRICOMP AL002 ABS LNP LUBRICOMP* AL002 is a compound based on Acrylonitrile Butadiene Styrene resin containing 10% PTFE. Added features of this material include: Internally Lubricated. |
|||
| Tensile Strength at Break | 32.0 MPa | 4640 psi | ASTM D638 |
| SABIC Innovative Plastics LNP LUBRICOMP AL002 ABS (Europe-Africa-Middle East) LNP* LUBRICOMP* AL002 is a compound based on Acrylonitrile Butadiene Styrene resin containing PTFE. Added features of this material include: Internally Lubricated. |
|||
| Tensile Strength at Break | 32.0 MPa | 4640 psi | ASTM D638 |
| Braskem BS 002J HDPE Blow Molding Polyethylene
(discontinued **) Applications: Bottles up to 60 liters with high ESCR; bottles for surface-active agents. Information provided by Braskem |
|||
| Tensile Strength at Break | 32.0 MPa | 4640 psi | ASTM D638 |
| 3M Dyneon™ PFA 6505N Perfluoroalkoxy Fluorothermoplastic
(discontinued **) The excellent chemical temperature resistance of Dyneon™ 6500N PFA is available across a range of melt flow indices, for optimal processability. Dyneon™ PFA 6502N, the highest molecular weight gra.. |
|||
| Tensile Strength at Break | 32.0 MPa | 4640 psi | ISO R 527 |
| Fainplast Compounds RE 325/2 Rigid PVC, Extrusion Building profiles |
|||
| Tensile Strength at Break | 32.0 MPa | 4640 psi | ASTM D638 |
| LG Chemical HI855HS PMMA, Impact Resistant Grade Molding granule designed for greater impact strength combined with the outstanding properties of conventional acrylic materialsFeatures: Excellent transparency and eleganceWeather resistance and che.. |
|||
| Tensile Strength at Break | 32.0 MPa | 4640 psi | ASTM-D638 |
| Ineos ABS Lustran® Guardian™ 682 ABS, Injection Molding Grade Lustran® ABS 682 is a high performance, HCFC-141b resistant grade of ABS for injection molded refrigerator and freezer components. |
|||
| Tensile Strength at Break | 32.0 MPa @Temperature 23.0 °C |
4640 psi @Temperature 73.4 °F |
50mm/min; ISO 527-2/1A/50 |
| SYNTHOS Forsan® 449 Acrylonitrile Butadiene Styrene (ABS) High flow, high gloss, suitable for electroplating.Applications: General purpose, intricate and thin-walled productsHousehold appliances, vacuum cleaners, heels, toys, fan grilles, etc.Synthos was f.. |
|||
| Tensile Strength at Break | 32.0 MPa | 4640 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics LNP STAT-KON FX98501 PE LNP* STAT-KON* FX98501 is a compound based on Polyethylene resin containing Proprietary Fillers. Added feature of this material is: Electrically Conductive. |
|||
| Tensile Strength at Break | >= 32.0 MPa | >= 4640 psi | ISO R 527 |
| Stir SpA Giesse RSA/12 (PVC) Application: Blow molding very high shock resistanceInformation provided by STIR SpA |
|||
| Tensile Strength at Break | 32.0 MPa | 4640 psi | |
| UBE B (Low-Cis) HIPS (n-DM = 0.03 wt % and PH-3H = 0.03 wt %) Description: UBE high impact polystyrene (HIPS).Information provided by UBE. |
|||
| Tensile Strength at Break | 32.0 MPa | 4640 psi | |
| UBE UBEPOL B -B HIPS (Low-cis) Description: UBE high impact polystyrene (HIPS).Information provided by UBE. |
|||
| Tensile Strength at Break | 32.0 MPa | 4640 psi | DIN EN ISO 527 |
| Wolf Kunststoff ZEDEX® ZX-530CD3 031 Polymer Alloy, Fiber Reinforced and PTFE Modified Main Characteristics: Dimensionally stable and rigid; Stress resistant; Extremely low wear to 100 ° CApplications: Chemical Engineering; Laboratory Technology; Automitve Technology; Machine ToolsIn.. |
|||
| Tensile Strength at Break | 32.0 MPa | 4640 psi | ASTM D 638 |
| Cossa Polimeri ESTABLEND CR Polycarbonate ABS Blend Polycarbonate and Acrylonitrile Butadiene Styrene blend for chromium plating, painting and metallizationGood impact resistance, good thermal resistanceInformation provided by Cossa Polimeri S.r.l. |
|||
| Tensile Strength at Break | 32.0 MPa | 4640 psi | ASTM D 638 |
| Cossa Polimeri ESTADIENE 3015 MT Acrylonitrile Butadiene Styrene ABSMedium thermal resistance, high impact resistance at low temperature, good melt flow rate, high gloss, excellent processabilityInformation provided by Cossa Polimeri S.r.l. |
|||
| Tensile Strength at Break | 32.0 MPa | 4640 psi | 50mm/min; ASTM D638 |
| Denka TE-30 Transparent Resin Polymer (MABS resin) ABS "TX Polymer" (methyl methacrylate styrene), MS resins as an alternative to acrylic resins, with low density, low moisture absorption, and good moldability, "TH Polymer/TP Polymer," MBS resins with a.. |
|||
| Tensile Strength at Break | 32.0 MPa | 4640 psi | Conditioned 15 days at 23°C - 50% RH; ASTM D638 |
| Arkema Group Pebax® 2533 SA 01 MED Polyether Block Amide (PEBA) Polyether block amide PEBAX® 2533 SA 01 MED is a thermoplastic elastomer made of flexible polyether and rigid polyamide. This grade offers the highest quality and it is specially designed to meet t.. |
|||
| Tensile Strength at Break | 32.0 MPa | 4640 psi | ASTM D638 |
| Aclo Accutech Polypropylene Homopolymer HP0334T40L1 Talc Reinforced |
|||
| Tensile Strength at Break | 32.0 MPa | 4640 psi | Conditioned; ISO R 527 |
| Addiplast Addilene H 490 M10S Flame Retardant Polypropylene Flame retardant, mineral filled, with halogensInformation provided by Addiplast. |
|||
| Tensile Strength at Break | 32.0 MPa | 4640 psi | Conditioned; ISO R 527 |
| Addiplast Addilene H 490 S Flame Retardant Polypropylene Flame retardant, unreinforced, with halogensInformation provided by Addiplast. |
|||
| Tensile Strength at Break | 32.0 - 34.0 MPa | 4640 - 4930 psi | ASTM D4745-97 |
| Adamas Adalon® 508 PTFE, 1% MoS2 Information provided by Adamas, HPM |
|||
| Tensile Strength at Break | 32.0 MPa | 4640 psi | ASTM D638 |
| Asahi Glass Fluon® P-63P PFA Perfluoropolymer Fluon® PFA is a copolymer of tetrafluoroethylene (C2F4) and perfluoroalkoxyethylene, which has excellent chemical, electrical, mechanical and surface properties. PFA retains many inherent character.. |
|||
| Tensile Strength at Break | 32.0 MPa | 4640 psi | ASTM D638 |
| Asahi Glass Fluon® P-830UP PFA Perfluoropolymer Fluon® PFA is a copolymer of tetrafluoroethylene (C2F4) and perfluoroalkoxyethylene, which has excellent chemical, electrical, mechanical and surface properties. PFA retains many inherent character.. |
|||
| Tensile Strength at Break | 32.0 MPa | 4640 psi | |
| Plastcom SLOVALEN PH 82 T 20 PP, 20% mineral filling FeaturesModified homopolymer PP for injection moulding with the content of 20% mineral filling. Increased rigidity, strength and thermal use up to 130°C depending on the talc conte nt. Decreased sh.. |
|||
| Tensile Strength at Break | <= 32.0 MPa | <= 4640 psi | ISO/R527 |
| Polykemi AB POLYfill PPH TS15010 H VTUV1 Polypropylene Homopolymer, Mineral Reinforced Information provided by Polykemi AB |
|||
| Tensile Strength at Break | 32.0 MPa | 4640 psi | ISO R 527 |
| Fainplast Compounds RE 430 Rigid PVC, Extrusion Electric channels |
|||
| Tensile Strength at Break | 32.0 MPa | 4640 psi | ASTM D638 |
| Braskem BU 004 HDPE Blow Molding Polyethylene Applications: Bottles for food products, lubricating and cooking oil; toys; bottler for surface-active agents; sheets. Information provided by Braskem |
|||