Material Notes:

Introduction: AVALON 92 AE is a general purpose polyester based thermoplastic polyurethane for injection molding. AVALON 92 AE is part of the AVALON Perform Range and offers a premium soiling material for sports footwear and top-pieces. The features offered include:DurabilityExcellent surface definitionAbrasion resistanceFlex resistancePhthalate free TPU Information provided by Alliance Polymers

Physical Properties	Metric	English	Comments
Density	1.23 g/cc	0.0444 lb/inÂ³	ISO 2781

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	92	92	ISO 868
Hardness, Shore D	46	46	ISO 868
Tensile Strength at Break	32.0 MPa	4640 psi	ISO 37
Elongation at Break	450 %	450 %	ISO 37
100% Modulus	0.00900 GPa	1.31 ksi	ISO 37
300% Modulus	0.0150 GPa	2.18 ksi	ISO 37
Tear Strength	110 kN/m	628 pli	ISO 34B
Abrasion	35	35	mm<sup>3</sup>; ISO 4649
Compression Set	20 %	20 %	ISO 815

Processing Properties	Metric	English
Feed Temperature	25.0 - 35.0 Â°C	77.0 - 95.0 Â°F
Rear Barrel Temperature	185 - 195 Â°C	365 - 383 Â°F
Middle Barrel Temperature	190 - 200 Â°C	374 - 392 Â°F
Front Barrel Temperature	195 - 205 Â°C	383 - 401 Â°F
Nozzle Temperature	180 - 190 Â°C	356 - 374 Â°F
Mold Temperature	25.0 - 50.0 Â°C	77.0 - 122 Â°F
Injection Pressure	2.00 - 10.0 MPa	290 - 1450 psi
Hold Pressure	1.00 - 5.00 MPa	145 - 725 psi
Back Pressure	0.0300 - 0.300 MPa	4.35 - 43.5 psi
Screw Speed	20 - 80 rpm	20 - 80 rpm

Descriptive Properties	Value	Comments
Compression Ratio	2-3:1
L/D Ratio	20-25:1
Ross Flex	-10Â°C, BS 5131
Typical Screw Diameter	40-120 nm