Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	220 MPa	31900 psi	Type I, 50 mm/min; ASTM D638
SABIC Innovative Plastics Lexan® ML7687 PC (Europe-Africa-Middle East) ML7687 is an optical quality, high purity PC resin optimized for use in optical applications such as light guide panels
Tensile Strength at Break	220 MPa	31900 psi	ISO 527
Nilit FRIANYL B63 GV50 Nylon 6 for injection molding, 50% glass fiber reinforced Nylon 6 for injection molding.Information provided by Frisetta Polymer, which merged into Nilit Plastics
Tensile Strength at Break	220 MPa	31900 psi	ISO 527-1,-2
Lanxess DurethanÂ® AKV 50 H3.0 000000 Nylon 66, 50% Glass Fibers PA 66, 50% glass fibers, injection molding, heat-ageing stabilized
Tensile Strength at Break	220 MPa	31900 psi	ISO 527-1,-2
Lanxess DurethanÂ® BKV 50 H3.0 000000 Nylon 6, 50% Glass Fibers PA 6, 50% glass fibers, injection molding, heat-ageing stabilized
Tensile Strength at Break	220 MPa	31900 psi	d.a.m.; ISO 527-1, -2; 5 mm/min
Lanxess DurethanÂ® AKV 40 H3.0 000000 Nylon 66, Glass Fiber Reinforced PA 66, 40% glass fibers, injection molding, heat-aging stabilizedInformation provided by LANXESS.
Tensile Strength at Break	220 MPa	31900 psi	ISO 527-1/-2
Lanxess DurethanÂ® BKV 50 H2.0 901510 Nylon 6, 50% Glass Fiber PA 6, injection molding grade, 50% glass fibers, good heat-ageing resistance
Tensile Strength at Break	220 MPa	31900 psi	ASTM D638
Solvay TECHNYLÂ® A 218 V50 PA66, 50% glass fiber, DRY Description: TECHNYLÂ® A 218 V50 is a polyamide 66, reinforced with 50% of glass fiber, heat stabilized, for injection molding. This product is available in natural and black colors.Benefits: The ..
Tensile Strength at Break	220 MPa	31900 psi	ASTM D638
SABIC Innovative Plastics LNP VERTON UX03320 PPA LNP* VERTON* UX03320 is a compound based on Polyphthalamide resin containing proprietary fillers. Added feature of this grade is: Structural.
Tensile Strength at Break	220 MPa	31900 psi	ISO R 527
Solvay TECHNYLÂ® A 118L V50 PA66, 50% glass fiber, Eh 0 Description: TECHNYL A 118L V50 is a polyamide 6.6 reinforced with 50% of glass fiber, with thermal stability, UV protection and modified viscosity that provides better superficial appearance. Color..
Tensile Strength at Break	220 MPa	31900 psi	conditioned; ISO 527-1/-2
EMS-Grivory Grivory® GV-5 FWA black 9225 PA*-GF50 Product description: Grivory GV-5 FWA black 9225 is a 50% glass fiber reinforced engineering thermoplastic material based on a combination of semicrystalline Polyamide with partially aromatic copoly..
Tensile Strength at Break	220 MPa	31900 psi	conditioned; ISO 527-1/-2
EMS-Grivory Grivory® GV-5H EF nat PA*-GF50 Product description: Grivory GV-5H EF natural is a 50% glass-fiber reinforced engineering thermoplastic material based on a combination of semi-crystalline Polyamide with partially aromatic copolyam..
Tensile Strength at Break	220 MPa	31900 psi	dry; ISO 527-1/-2
EMS-Grivory Grivory® TSG-60 PA666-GF60 Product description: Grilon TSG-60 is a heat stabilized, normal viscosity PA66 + PA6 injection molding grade with 60% glass fibers. Grilon TSG-60 has the following important properties: Very high st..
Tensile Strength at Break	220 MPa	31900 psi	dry; ISO 527-1/-2
EMS-Grivory Grivory® TSGL-40/4 FA black 9840 PA666-GF40 Product description: Grilon TSGL-40/4 FA black 9840 is based on a heat stabilized semi-crystalline Polyamide PA66+PA6 and 40% long glass fibers. Grilon TSGL-40/4 FA black 9840 is characterized by th..
Tensile Strength at Break	220 MPa	31900 psi	dry; ISO 527-1/-2
EMS-Grivory Grivory® XE 4095 black 9225 PA*-GF50 Product description: Grivory XE 4095 is a 50% glass-fiber reinforced engineering thermoplastic material based on a semi-crystalline, partially aromatic copolyamide. This Grivory HT product is partia..
Tensile Strength at Break	220 MPa	31900 psi	DAM; ISO 527-1/-2
DuPont Performance Polymers Zytel® HTN 51G35EF BK083 Polyphthalamide (PPA) (Unverified Data**) 35% Glass Reinforced PPA High Performance Polyamide Developed for Electrical and Electronics Applications Zytel HTN51G35EF BK083 is a 35% glass reinforced heat stabilized lubricated high performance..
Tensile Strength at Break	220 MPa	31900 psi	dry; ISO 527-1/-2
EMS-Grivory Grivory® GVN-5H black 9915 PA*-GF50 Product description: Grivory GVN-5H is a 50 % glass-fiber reinforced, impact-modified engineering thermoplastic material based on a combination of semicrystalline polyamide with partially aromatic c..
Tensile Strength at Break	220 MPa	31900 psi	conditioned; ISO 527-1/-2
EMS-Grivory Grivory® GVS-5H black 9915 PA*-GF50 Product description: Grivory GVS-5H black 9915 is a 50% glass fiber reinforced engineering thermoplastic material based on a combination of semicrystalline polyamide with partially aromatic copolyam..
Tensile Strength at Break	220 MPa	31900 psi	ISO R 527
Addiplast Addinyl B2 ZV 50 Nylon 6, 50% Glass Filled Glass fiber reinforced, increased thermal aging stabilityInformation provided by Addiplast.
Tensile Strength at Break	220 MPa	31900 psi	5 [mm/min]; ISO 527-1/2
Akro-Plastic Akroloy® PA GF 50 (2706) PA 6.6 & PA6I/6T Conditioned, 50% Glass Filled One of the most characteristic properties of polyamide (PA 6.6) is the absorption of moisture. This essentially leads to increased toughness and elongation at break, to name the most important param..
Tensile Strength at Break	220 MPa	31900 psi	5 [mm/min]; ISO 527-1/2
Akro-Plastic Akromid® T1 GF 40 9 (3499) PPA Conditioned, 40% Glass Filled The new AKROMID® T is characterized primarily by high heat resistance and the lowest moisture absorption of the three PA grades, making it particularly well-suited in the automotive sector for high..
Tensile Strength at Break	220 MPa	31900 psi	ISO 527
BASF Ultramid® HMG14 HS BK 102 60% Glass Filled PA66 (Conditioned) Description: Ultramid HMG14 HS BK-102 is a 60% glass reinforced, injection molding grade of PA66 offering high strength and stiffness. Due to inherently lower moisture absorption, Ultramid HMG14 HS ..
Tensile Strength at Break	220 MPa	31900 psi	50% RH
3M PN8017 Marine Grade Silicone Sealant A mildew resistant, non-sagging, moisture curing silicone rubber sealant for above the waterline applications which remains flexible with excellent resistance to the marine environment. Adheres to b..
Tensile Strength at Break	220 MPa	31900 psi	dry; ISO 527-1/-2
EMS-Grivory Grivory® HT1V-4 FWA nat PA6T/6I-GF40 Product description: Grivory HT1V-4 FWA natural is a 40 wt.-% glass fiber reinforced engineering thermoplastic material based on a semi-crystalline, partially aromatic copolyamide. Acc. to ISO: PA 6..
Tensile Strength at Break	220 MPa	31900 psi	dry; ISO 527-1/-2
EMS-Grivory Grivory® HT1V-4 HY black 9205 PA6T/6I-GF40 Product description: Grivory HT1V-4 HY black 9205 is a 40% glass fiber reinforced engineering thermoplastic material based on a semi-crystalline, partially aromatic copolyamide. Grivory HT1V-4 HY bl..
Tensile Strength at Break	220 MPa	31900 psi
Radici Radilon® A RV500 (dry) Nylon 66 Radilon® A is a range of polyamide 66 (PA66) products obtained through the polymerization of hexamethylendiamine and adipic acid, and used for injection, extrusion and blow-molding.Information prov..
Tensile Strength at Break	220 MPa	31900 psi	5 mm/min; ISO 527
SABIC Innovative Plastics LNP Verton RX93407D PA 66 LNP* Verton* RX93407D is a compound based on Nylon 66 resin.This data was supplied by SABIC-IP for the Americas region.