Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | <= 175 MPa | <= 25400 psi | ISO/R527 |
Polykemi AB SCANAMID 66 A13^ F30 Nylon 66, Glass Fiber Reinforced Information provided by Polykemi AB |
|||
Tensile Strength at Break | <= 175 MPa | <= 25400 psi | ISO/R527 |
Polykemi AB SCANAMID 66.6 C12^F30 Nylon 66/6, Glass Fiber, Reinforced Information provided by Polykemi AB |
|||
Tensile Strength at Break | 175 MPa | 25400 psi | ASTM D638 |
LNP Lubricomp® EFL-4036 Polyetherimide, Glass Fiber Reinforcement, PTFE Lubricant
(discontinued **) Features: LubricatedForms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP grades are still ac.. |
|||
Tensile Strength at Break | 175 MPa | 25400 psi | ISO 527-1/-2 |
DSM Akulon® K-FHG6 (Dry) 30% Glass Reinforced Nylon 6 (North America)
(discontinued **) Description: The Akulon portfolio is engineered for optimum performance to suit different processing techniques and end use markets.Unfilled Extrusion ResinsAkulon resins are available with melt vis.. |
|||
Tensile Strength at Break | 175 MPa | 25400 psi | ISO 527 |
Grupo Repol Dinalon® A1S25 G25 PA66 25% Glass Fiber Mechanical properties for Dry As Molded samplesInformation provided by Grupo Repol |
|||
Tensile Strength at Break | 175 MPa | 25400 psi | ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP EFL36 PEI (Asia Pacific) LNP LUBRICOMP* EFL36 is a compound based on Polyetherimide resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated. |
|||
Tensile Strength at Break | 175 MPa | 25400 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP EFL36XXC PEI LNP* Lubricomp* EFL36XXC is a compound based on Polyetherimide containing 30% Glass Fiber, 155 PTFE. Characteristics of this grade are: Internally Lubricated. |
|||
Tensile Strength at Break | 175 MPa | 25400 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP OCL36AXP PPS (Europe-Africa-Middle East) LNP* LUBRICOMP* OCL36AXP is a compound based on PPS-Branched resin containing Carbon Fiber, PTFE. Added features include: Electrically Conductive, Internally Lubricated. |
|||
Tensile Strength at Break | 175 MPa | 25400 psi | ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP EC004XXC PEI (Asia Pacific) LNP* Thermocomp* EC004XXC is a compound based on Polyetherimide resin containing Carbon Fiber. Added features of this material include: Electrically Conductive. |
|||
Tensile Strength at Break | 175 MPa | 25400 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP Thermocomp RF006XXP PA 66 (Europe-Africa-Middle East) 30% glass fibre reinforced Polyamide 66 injection moulding resin.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region. |
|||
Tensile Strength at Break | 175 MPa | 25400 psi | ISO 527-93 |
Wellman Wellamid® GF1750-BK2 50% Glass Fiber Reinforced Nylon 6 Description: Glass Fiber Reinforced Nylon 6Information provided by Wellman. |
|||
Tensile Strength at Break | 175 MPa | 25400 psi | ISO 527-1/-2 |
DSM Akulon® Ultraflow™ K-FG6 Nylon 6-30% Glass Reinforced (European Grade) (Dry) The Akulon® product portfolio is engineered for optimum performance to suit different processing techniques and end use markets. Akulon Nylon 6 is used for extrusion applications including barrier .. |
|||
Tensile Strength at Break | 175 MPa | 25400 psi | ISO 527-1/-2 |
DuPont Performance Polymers Rynite® 545 BK504 Polyethylene Terephthalate (PET)
(Unverified Data**) 45% Glass Reinforced Polyethylene Terephthalate Rynite 545 BK504 is a 45% glass reinforced modified polyethylene terephthalate with good strength and stiffness excellent dimensional stability and cr.. |
|||
Tensile Strength at Break | 175 MPa | 25400 psi | DAM; ISO 527-1/-2 |
DuPont Performance Polymers Zytel® PLS 95G40DH1T BK261 Nylon 6
(Unverified Data**) 40% Glass Reinforced Heat Stabilized Polyamide Zytel PLS95G40DH1T is a 40% GR impact modified PA made with SHIELD technology its superior heatInformation provided by DuPont Performance Polymers |
|||
Tensile Strength at Break | 175 MPa | 25400 psi | ISO 527 |
Eurotec® Tecomid® NB40 GR30 NL PA 6 30% glass fiber reinforced Excellent stiffness/toughness balanceHigh mechanical strengthVery good thermal stabilityExcellent flammability characteristicsGood electrical propertiesHigh wear resistance and low frictionVery good.. |
|||
Tensile Strength at Break | 175 MPa | 25400 psi | 5 mm/min; ISO 527 |
CP-Polymer-Technik Wellamid® 6000 GV 30 HWCP 30% Glass Fiber Nylon 6, Heat Stabilized, Dry Information provided by CP-Polymer-Technik GmbH & Co. KG |
|||
Tensile Strength at Break | 175 MPa | 25400 psi | 5 mm/min; ISO 527 |
Eurostar Staramide RF006XXP PA66, 30% Glass Fiber Filled, Injection Molded Staramide RF006XXP is a 30% Glass Fiber Reinforced Polyamide 66 Injection Molding Resin (also known as RF1006)Information provided by Eurostar. |
|||
Tensile Strength at Break | 175 MPa | 25400 psi | ISO 527 |
Eurotec® Tecomid® NA40 GR25 NL PA 6.6 25% glass fiber reinforced Excellent stiffness/toughness balanceHigh mechanical strengthVery good thermal stabilityExcellent flammability characteristicsGood electrical propertiesHigh wear resistance and low frictionVery good.. |
|||
Tensile Strength at Break | 175 MPa | 25400 psi | ISO 527 |
Eurotec® Tecomid® NB40 GR30 NL HW PA6, 30% glass fiber reinforced, hydrolysis stabilized, natural Information provided by Eurotec® |
|||
Tensile Strength at Break | 175 MPa | 25400 psi | ISO 527 |
BASF Ultramid® 66 H2 G/35-V0KB NAT 0046 35% Glass Filled PA66 (Dry) Description: Ultramid 66 H2 G/35-V0KB NAT0046 is a 35% glass reinforced, heat stabilized injection molding grade. It is a V-0 self-extinguishing grade, with phosphorous. It offers good flowability a.. |
|||
Tensile Strength at Break | 175 MPa | 25400 psi | ASTM D638 |
BASF Ultramid® HPN 9233G HS BK 102 33% Glass Filled PA6 (Dry) Description: Ultramid HPN 9233G HS BK-102 is a heat stabilized, pigmented black, 33% glass reinforced PA6 injection molding grade resin in the High Productivity Nylon Series developed for improved c.. |
|||
Tensile Strength at Break | 175 MPa | 25400 psi | ISO R 527 |
Addiplast Addinyl C2 V30 Nylon 66/6, 30% Glass Filled Glass fiber reinforced, high strengthInformation provided by Addiplast. |
|||
Tensile Strength at Break | 175 MPa @Temperature -40.0 °C |
25400 psi @Temperature -40.0 °F |
ISO Data |
BASF Ultramid® SEGM35 H1 BK-126 15/25% Glass/Mineral Filled PA6 (Dry) Ultramid SEGM35 H1 BK-126 is a 40% glass/mineral reinforced injection molding grade. It offers enhanced surface appearance, it also exhibits similar UV weathering characteristics compared to 8267G .. |
|||
Tensile Strength at Break | 175 MPa | 25400 psi | ISO 527-2 |
Pasargad Polymer Peyvand Pasamid 3P-H2145B Nylon 66, 45% Glass Fiber Reinforced Form: PelletsProcessing Method: Injection MoldingUses: Automotive Application Furniture Appliance Components Electrical PartsFastenerHousingInformation provided by Pasargad Polymer Peyvand Co |