Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 173 MPa | 25100 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP REL22 PA 66 LNP* LUBRICOMP* REL22 is a compound based on Nylon 66 resin containing 10% Carbon Fiber, 10% PTFE. Added features of this material include: Wear Resistant, Electrically Conductive. |
|||
Tensile Strength at Break | 173 MPa | 25100 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP RFL36SXC PA 66 (Europe-Africa-Middle East) LNP* Lubricomp* RFL36SXC is a compound based on Nylon 66 resin containing Glass Fiber, PTFE. Added features of this material include: Heat Stabilized. |
|||
Tensile Strength at Break | 173 MPa | 25100 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP RFL36SXD PA 66 (Europe-Africa-Middle East) LNP* Lubricomp* RFL36SXD is a compound based on Nylon 66 resin containing Glass Fiber, PTFE. Added features of this material include: Heat Stabilized. |
|||
Tensile Strength at Break | 173 MPa | 25100 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP RFP38 PA6.6 LNP* LUBRICOMP* RFP38 is a compound based on Nylon 66 containing 40% Glass Fiber, 15% PTFE/Silicone. Added feature of this grade is: Wear Resistant. |
|||
Tensile Strength at Break | 173 MPa | 25100 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP RX05049 PA 66 (Europe-Africa-Middle East) LNP* LUBRICOMP* RX05049 is a compound based on PA 66 resin containing Glass Fiber, PTFE, Proprietary Lubricant. Added features include; Internally Lubricated. |
|||
Tensile Strength at Break | 173 MPa | 25100 psi | ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP IX95700 PA 6/12 (Asia Pacific) LNP* Thermocomp* IX95700 is a compound based on Nylon 6/12 resin containing Glass Fiber. |
|||
Tensile Strength at Break | 173 MPa | 25100 psi | ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP IX95700 PA6.12 LNP* THERMOCOMP* IX95700 is a compound based on Nylon 6/12 resin containing Glass Fiber. |
|||
Tensile Strength at Break | 173 MPa | 25100 psi | ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP PF007 PA 6 LNP* THERMOCOMP* PF007 is a compound based on Nylon 6 resin containing 35% Glass Fiber. |
|||
Tensile Strength at Break | 173 MPa | 25100 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP QCP36 PA6.10 LNP* LUBRICOMP* QCP36 is a compound based on Nylon 6/10 resin containing 15% PTFE/Silicone, 30% Carbon Fiber. Added features of this material include: Wear Resistant. Electrically Conductive |
|||
Tensile Strength at Break | 173 MPa | 25100 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP STAT-KON OE006C1 PPS - Linear LNP* STAT-KON* OE006C1 is a compound based on PPS - Linear resin containing 30% Carbon Fiber. Added features of this material include: Electrically Conductive. |
|||
Tensile Strength at Break | 173 MPa | 25100 psi | ASTM D638 |
SABIC Innovative Plastics LNP STAT-KON REF42 PA 66 LNP* STAT-KON* REF42 is a compound based on Nylon 66 resin containing 20% Glass Fiber, 10% Carbon Fiber. Added features of this material include: Electrically Conductive. |
|||
Tensile Strength at Break | 173 MPa | 25100 psi | |
Radici Radilon® A RV500 (cond.) Nylon 66 Radilon® A is a range of polyamide 66 (PA66) products obtained through the polymerization of hexamethylendiamine and adipic acid, and used for injection, extrusion and blow-molding.Information prov.. |
|||
Tensile Strength at Break | 173 MPa | 25100 psi | ASTM D638 |
SABIC Innovative Plastics LNP STAT-KON REF42 PA 66 (Asia Pacific) LNP* Stat-kon* REF42 is a compound based on Nylon 66 resin containing Glass Fiber, Carbon Fiber. |
|||
Tensile Strength at Break | 173 MPa | 25100 psi | ASTM D 638 |
SABIC Innovative Plastics LNP Thermocomp PF007 PA 6 (Asia Pacific) LNP* Thermocomp* PF007 is a compound based on Nylon 6 resin containing Glass Fiber.This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
Tensile Strength at Break | 173 MPa | 25100 psi | ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP QCP36 PA 6/10 (Asia Pacific) LNP* Lubricomp* QCP36 is a compound based on Nylon 6/10 resin containing PTFE, Flame Retardant, Carbon Fiber. Added features of this material include: Internally Lubricated, , Electrically Conducti.. |