SABIC Innovative Plastics LNP Thermocomp PF007 PA 6 (Asia Pacific)
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | EXW, FOB, CFR, CIF |
| Payment Terms | L/C, T/T, PayPal |
| Download PDF | SABIC Innovative Plastics LNP Thermocomp PF007 PA 6 (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Thermocomp* PF007 is a compound based on Nylon 6 resin containing Glass Fiber.This data was supplied by SABIC-IP for the Asia Pacific region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.43 g/cc | 0.0517 lb/in³ | ASTM D 792 |
| Linear Mold Shrinkage, Flow | 0.0080 cm/cm <br>@Time 86400 sec |
0.0080 in/in <br>@Time 24.0 hour |
ASTM D 955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 173 MPa | 25100 psi | ASTM D 638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D 638 |
| Tensile Modulus | 11.96 GPa | 1735 ksi | 50 mm/min; ASTM D 638 |
| Flexural Strength | 255 MPa | 37000 psi | ASTM D 790 |
| Flexural Modulus | 9.14 GPa | 1330 ksi | ASTM D 790 |
| Izod Impact, Notched | 1.44 J/cm <br>@Temperature 23.0 °C |
2.70 ft-lb/in <br>@Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 12.22 J/cm <br>@Temperature 23.0 °C |
22.89 ft-lb/in <br>@Temperature 73.4 °F |
ASTM D 4812 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C <br>@Thickness 3.20 mm |
401 °F <br>@Thickness 0.126 in |
unannealed; ASTM D 648 |
Users viewing this material also viewed the following:
- Premix Premi-Glas® 1240-20 Fiberglass Reinforced Thermoset Thick Molding Compound
- Polimeri Europa Flexirene® MS 40 A Linear Low Density Polyethylene
- PEAK Werkstoff DISPAL S263 Aluminum Alloy, AlSi25Cu3Fe3Ni3MgCoTi, Condition F
- Grupo Repol Dinalon® B1S25 M404 PA6 40% Mineral Charge
- Momentive Performance Materials RTV109 Aluminum Adhesive Sealant, High Strength Paste
- Teknor Apex APEX® 3310-90 Polyvinyl Chloride, Flexible
- Teknor Apex Monprene® MP 1093L Thermoplastic Elastomer
- Tipco Tipcolene® FPT 20 FR VO LTHA - UL94-V0 Flame Retardant, 20% Talc Polypropylene Homopolymer, Long Term Heat Stability
- Fainplast Compounds GA 85 Flexible PVC, Flame Retardant Sheathing
- Solvay RHODAFAC® RS-710 E Surfactant
Copyright © lookpolymers.com All Rights Reserved