SABIC Innovative Plastics LNP LUBRICOMP RFP38 PA6.6
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP RFP38 PA6.6.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* LUBRICOMP* RFP38 is a compound based on Nylon 66 containing 40% Glass Fiber, 15% PTFE/Silicone. Added feature of this grade is: Wear Resistant.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.50 g/cc | 1.50 g/cc | ASTM D792 |
| Density | 1.60 g/cc | 0.0578 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.570 % | 0.570 % | 50% RH, 24 hrs; ASTM D570 |
| 0.860 % | 0.860 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0070 - 0.0090 cm/cm @Time 86400 sec |
0.0070 - 0.0090 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.030 cm/cm @Time 86400 sec |
0.010 - 0.030 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 173 MPa | 25100 psi | Type I, 5 mm/min; ASTM D638 |
| 174 MPa | 25200 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 2.4 % | 2.4 % | Type I, 5 mm/min; ASTM D638 |
| 2.5 % | 2.5 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 13.14 GPa | 1906 ksi | 1 mm/min; ISO 527 |
| 13.38 GPa | 1941 ksi | 5 mm/min; ASTM D638 | |
| Flexural Strength | 263 MPa | 38100 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 263 MPa | 38100 psi | ISO 178 | |
| Flexural Modulus | 11.6 GPa | 1680 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 11.94 GPa | 1732 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 1.21 J/cm | 2.27 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 9.11 J/cm | 17.1 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 12.0 kJ/m² | 5.71 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 58.0 kJ/m² | 27.6 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 8.00 J @Temperature 23.0 °C |
5.90 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 3.00 J | 2.21 ft-lb | Multiaxial Impact; ISO 6603 |
| Coefficient of Friction, Dynamic | 0.65 | 0.65 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.61 | 0.61 | ASTM D3702 Modified |
| K (wear) Factor | 28.2 x 10-8 mm³/N-M | 14.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 25.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
13.9 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 33.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
18.3 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 257 °C | 495 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 257 °C @Thickness 3.20 mm |
495 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 243 °C | 469 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 248 °C @Thickness 3.20 mm |
478 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Polymax® Maxelast® P3862 TPE, PP Overmold or Standalone use
- Polymax® Maxelast® P3980H TPE, PP Overmold or Standalone use
- SABIC Innovative Plastics Lexan® DMX1214 PC Copolymer (Europe-Africa-Middle East)
- LG Chemical KEYFLEX BT GN7142F Ester Type TPE
- Solvay Specialty Polymers Amodel® AS-4133 HS Polyphthalamide (PPA), 33% Glass Fiber (Dry)
- Techmer ES HiFill FR® PA6 FR-N HS
- Borealis PC0787 Polyethylene Insulation Compound, Crosslinkable
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane, Hardness 93A
- DSM Akulon® F-X9183 PA6
- Buckeye Polymers BP RPP 4008 TR BLK Polypropylene, Talc Filled
Copyright © lookpolymers.com All Rights Reserved