Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 15.9 MPa | 2310 psi | Type IV, 510 mm/min; ASTM D638 |
PolyOne Geon™ Vinyl Wire & Cable JJC32A Polyvinyl Chloride, Flexible (PVC, Flexible) Typical Properties of Molded Slab (0.075); Not to be Construed as Specifications.Information provided by PolyOne |
|||
Tensile Strength at Break | 15.9 MPa | 2310 psi | Type IV, 510 mm/min; ASTM D638 |
PolyOne Geon™ Vinyl Wire & Cable W2402L Polyvinyl Chloride, Flexible (PVC, Flexible) Typical Properties of Molded Slab (0.075); Not to be Construed as Specifications.Information provided by PolyOne |
|||
Tensile Strength at Break | 15.9 MPa | 2310 psi | Type IV, 510 mm/min; ASTM D638 |
PolyOne Geon™ Vinyl Wire & Cable WJJC31L Polyvinyl Chloride, Flexible (PVC, Flexible) Typical Properties of Molded Slab (0.075); Not to be Construed as Specifications. Provisional Product Information - Physical and Mechanical properties based on initial production.Information provide.. |
|||
Tensile Strength at Break | 15.9 MPa | 2310 psi | 510 mm/minTensile and elongation values are largely determined by processing parameters of the end user.; ASTM D412 |
PolyOne Maxxam™ FR WC 0587-21 R2 RoHS Polypropylene, Unspecified (PP, Unspecified) Maxxam FR WC 0587-21 R2 RoHS is a flame retardant polyolefin compound characterized by low flame spread and good processability. Designed for thin wall primary wire applications.UL Yellow Card appro.. |
|||
Tensile Strength at Break | 15.9 MPa | 2310 psi | 510 mm/min; ASTM D638 |
PolyOne Geon™ Vinyl Flexible B8000 Polyvinyl Chloride, Flexible (PVC, Flexible) Information provided by PolyOne |
|||
Tensile Strength at Break | 15.9 MPa | 2310 psi | 510 mm/min; ASTM D638 |
PolyOne Geon™ Vinyl Flexible B90T0 Polyvinyl Chloride, Flexible (PVC, Flexible) Information provided by PolyOne |
|||
Tensile Strength at Break | 15.9 MPa | 2310 psi | 510 mm/min; ASTM D638 |
PolyOne Geon™ Vinyl Flexible BP90W2 Polyvinyl Chloride, Flexible (PVC, Flexible) Information provided by PolyOne |
|||
Tensile Strength at Break | 15.9 MPa | 2310 psi | 510 mm/min; ASTM D638 |
PolyOne Geon™ Vinyl Flexible C90A0 Polyvinyl Chloride, Flexible (PVC, Flexible) Information provided by PolyOne |
|||
Tensile Strength at Break | 15.9 MPa | 2310 psi | 510 mm/min; ASTM D638 |
PolyOne Geon™ Vinyl Flexible FC900 Polyvinyl Chloride, Flexible (PVC, Flexible) Information provided by PolyOne |
|||
Tensile Strength at Break | 15.9 MPa | 2310 psi | Type IV, 510 mm/min; ASTM D638 |
PolyOne Geon™ Vinyl Flexible XV 3450 Polyvinyl Chloride, Flexible (PVC, Flexible) NOTE: All ingredients used in the formulation of this compound are listed in the United States FDA Code of Federal Regulations, Title 21. The only restriction is that the plasticizer is For foods of.. |
|||
Tensile Strength at Break | 15.9 MPa | 2310 psi | Type IV, 510 mm/min; ASTM D638 |
PolyOne Geon™ Vinyl Flexible XV3772 Polyvinyl Chloride, Flexible (PVC, Flexible) All ingredients used in the formulation of this compound are listed in the United States FDA Code of Federal Regulations, Title 21. The only restriction is that the plasticizer is For foods of high .. |
|||
Tensile Strength at Break | 15.9 MPa | 2310 psi | Type IV, 510 mm/min; ASTM D638 |
PolyOne Geon™ HC 2170 Polyvinyl Chloride, Flexible (PVC, Flexible) Geon HC 2170 is a 70 Shore A non-phthalate flexible vinyl compound made from FDA sanctioned ingredients. HC 2170 can be used for extrusion and injection molding healthcare applications.NOTE: All ing.. |
|||
Tensile Strength at Break | 15.9 MPa | 2310 psi | Type IV, 510 mm/min; ASTM D638 |
PolyOne Geon™ HC 2170G Polyvinyl Chloride, Flexible (PVC, Flexible) Geon HC 2170G is a 70 Shore A non-phthalate, gamma-stable flexible vinyl compound made from FDA sanctioned ingredients. HC 2170G can be used for extrusion and injection molding healthcare applicatio.. |
|||
Tensile Strength at Break | 15.9 MPa | 2310 psi | 510 mm/min; ASTM D638 |
PolyOne Geon™ Vinyl Flexible B4DC1 Polyvinyl Chloride, Flexible (PVC, Flexible) Information provided by PolyOne |
|||
Tensile Strength at Break | 15.9 MPa | 2310 psi | Type IV, 510 mm/min; ASTM D638 |
PolyOne Geon™ Vinyl Flexible F80E Polyvinyl Chloride, Flexible (PVC, Flexible) Information provided by PolyOne |
|||
Tensile Strength at Break | 15.9 MPa | 2310 psi | Type IV, 510 mm/min; ASTM D638 |
PolyOne Geon™ Vinyl Flexible R252AE Polyvinyl Chloride + NBR (PVC+NBR) Information provided by PolyOne |
|||
Tensile Strength at Break | 15.9 MPa | 2310 psi | Type IV, 510 mm/min; ASTM D638 |
PolyOne Geon™ Vinyl Flexible R252BE Polyvinyl Chloride + NBR (PVC+NBR) Information provided by PolyOne |
|||
Tensile Strength at Break | 15.9 MPa | 2310 psi | Type IV, 510 mm/min; ASTM D638 |
PolyOne Geon™ Vinyl Flexible R312AE Polyvinyl Chloride, Flexible (PVC, Flexible) Information provided by PolyOne |
|||
Tensile Strength at Break | 15.9 MPa | 2310 psi | Type IV, 510 mm/min; ASTM D638 |
PolyOne Geon™ Vinyl Flexible R336AE Polyvinyl Chloride, Flexible (PVC, Flexible) Information provided by PolyOne |
|||
Tensile Strength at Break | 15.9 MPa | 2310 psi | Type IV, 510 mm/min; ASTM D638 |
PolyOne Geon™ Vinyl Flexible R352AE Polyvinyl Chloride, Flexible (PVC, Flexible) Information provided by PolyOne |
|||
Tensile Strength at Break | 15.9 MPa | 2310 psi | ISO R 527 |
Stir SpA AF 80 3 IK (PVC) Application: Insulation CEI 20-11 type R 2 low acid fumes emissionInformation provided by STIR SpA |
|||
Tensile Strength at Break | 15.9 MPa | 2310 psi | ISO R 527 |
Stir SpA Z 74 AT 1 (PVC) Application: Molding for beach footwearInformation provided by STIR SpA |
|||
Tensile Strength at Break | 15.9 MPa | 2310 psi | 20in/min; ASTM D638 |
Borealis LE4212L Polyethylene Insulation Compound, Crosslinkable LE4212L is a natural low-density crosslinkable polyethylene compound. Specifications: IEC 60502-1; and ANSI/ICEA S-66-524.Information provided by Borealis AG |
|||
Tensile Strength at Break | 15.9 MPa | 2310 psi | PVC (80)/CP80AS2(20) |
Lubrizol Estane® CP80AS2 Thermoplastic Polyurethane Type: Estane® CP80AS2 is a soft, polyester based thermoplastic polyurethane resin.Features: Outstanding compatibility with flexible PVC allowing easy dispersion without pre-compounding.Uses: Tube/H.. |
|||
Tensile Strength at Break | 15.9 MPa @Temperature 23.0 °C |
2310 psi @Temperature 73.4 °F |
ASTM D638, ISO 527-2 |
DuPont™ Surlyn® 9320 Zinc Ionomer Surlyn® 9320 is a zinc ionomer thermoplastic resin. It is available for use in conventional extrusion and injection equipment, to create various sheets or shapes. Surlyn® 9320 thermoplastic resin .. |
|||
Tensile Strength at Break | 15.9 MPa | 2310 psi | |
Daikin DAI-EL G-551 Fluoroelastomer Terpolymer, Bisphenol Curable Grade, 69% Fluorine Content Offers minimal compression set and excellent sealing. The terpolymer type is able to withstand polarized solvents to realize a wide range of application.Features: Products with excellent balance of.. |
|||
Tensile Strength at Break | 15.9 MPa | 2310 psi | Press Cure 10 Minutes @ 188°C, Post Cure 16 Hours @ 250°C |
3M Dyneon™ 131TZ High Temperature Perfluoroelastomer 3M™ Dyneon™ 131TZ is a technically advanced high temperature perfluoroelastomer (HT PFE). It is designed to meet the challenges of higher temperature applications. It is classified as FFKM per AST.. |
|||
Tensile Strength at Break | 15.9 MPa | 2310 psi | 2 in/min; ASTM D638 |
Ineos H20E-00 Polypropylene Homopolymer This is a homopolymer containing antistatic designed for injection molding. This material meets the requirements of the U.S. Food and Drug Administration as specified in 21 CFR 177.1520.Application.. |