3M Dyneon™ 131TZ High Temperature Perfluoroelastomer

Category Polymer , Thermoset , Fluoropolymer, TS , Thermoset Fluoroelastomer , Rubber or Thermoset Elastomer (TSE)
Manufacturer 3M Dyneon™
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF 3M Dyneon™ 131TZ High Temperature Perfluoroelastomer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
3M™ Dyneon™ 131TZ is a technically advanced high temperature perfluoroelastomer (HT PFE). It is designed to meet the challenges of higher temperature applications. It is classified as FFKM per ASTM D1418. Its fully fluorinated back bone structure provides a very broad chemical and thermal stability.Features and Benefits:Ideal for dry side (thermal processes) semiconductor applications including plasma, and high temperature CPI and aerospace applicationsHigh temperature FFKMLow metal ion content with low extractablesUpper use temperature of 315°CExcellent compression set resistanceCan be compounded to pass AMS 7257CInformation provided by the Dyneon division of 3M.
Physical Properties Metric English Comments
Specific Gravity 2.00 g/cc
2.00 g/cc
Mooney Viscosity 80

@Temperature 121 °C
80

@Temperature 250 °F
ML 1+ 10
Mechanical Properties Metric English Comments
Hardness, Shore A 77
77
Press Cure 10 Minutes @ 188°C, Post Cure 16 Hours @ 250°C
Tensile Strength at Break 15.9 MPa
2310 psi
Press Cure 10 Minutes @ 188°C, Post Cure 16 Hours @ 250°C
Elongation at Break 165 %
165 %
Press Cure 10 Minutes @ 188°C, Post Cure 16 Hours @ 250°C
100% Modulus 0.00910 GPa
1.32 ksi
Press Cure 10 Minutes @ 188°C, Post Cure 16 Hours @ 250°C
Compression Set 20 %

@Treatment Temp. 232 °C,
Time 252000 sec
20 %

@Treatment Temp. 450 °F,
Time 70.0 hour
Method B, -214 O-rings, Aged 70 Hours, 25% Deformation; ASTM D395
25 %

@Treatment Temp. 232 °C,
Time 605000 sec
25 %

@Treatment Temp. 450 °F,
Time 168 hour
Method B, -214 O-rings, Aged 168 Hours, 25% Deformation; ASTM D395
43 %

@Treatment Temp. 300 °C,
Time 252000 sec
43 %

@Treatment Temp. 572 °F,
Time 70.0 hour
Method B, -214 O-rings, Aged 70 Hours, 18% Deformation; ASTM D395
52 %

@Treatment Temp. 300 °C,
Time 252000 sec
52 %

@Treatment Temp. 572 °F,
Time 70.0 hour
Method B, -214 O-rings, Aged 70 Hours, 18% Deformation; ASTM D395
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 315 °C
599 °F
Brittleness Temperature -35.0 °C
-31.0 °F
Transformation Temperature -2.00 °C
28.4 °F
TR10
Descriptive Properties Value Comments
Color White
Form Crumb
MH, Maximum Toque 17.8 Inch-lb
100 cpm, 0.5° Arc, 12 Minutes @ 188°C, ASTM D5289
ML, Minimum Torque 1.2 Inch-lb
100 cpm, 0.5° Arc, 12 Minutes @ 188°C, ASTM D5289
t2, Time to 2 Inch-lb Rise from Minimum 2.4 Minutes
100 cpm, 0.5° Arc, 12 Minutes @ 188°C, ASTM D5289
t'50, Time to 50% Cure 3.6 Minutes
100 cpm, 0.5° Arc, 12 Minutes @ 188°C, ASTM D5289
t'90, Time to 90% Cure 7.0 Minutes
100 cpm, 0.5° Arc, 12 Minutes @ 188°C, ASTM D5289