Daikin DAI-EL G-551 Fluoroelastomer Terpolymer, Bisphenol Curable Grade, 69% Fluorine Content

Category Polymer , Thermoset , Fluoropolymer, TS , Thermoset Fluoroelastomer , Rubber or Thermoset Elastomer (TSE)
Manufacturer Daikin Industries
Trade Name DAI-EL
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Daikin DAI-EL G-551 Fluoroelastomer Terpolymer, Bisphenol Curable Grade, 69% Fluorine Content.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Offers minimal compression set and excellent sealing. The terpolymer type is able to withstand polarized solvents to realize a wide range of application.Features: Products with excellent balance of methanol and low temperature resistance.Information provided by Daikin Industries.
Physical Properties Metric English Comments
Specific Gravity 1.89 g/cc
1.89 g/cc
at 25°C
Mooney Viscosity 48

@Temperature 121 °C
48

@Temperature 250 °F
ML 1+10
Mechanical Properties Metric English Comments
Hardness, Shore A 74
74
Peak value, at 25°C
Tensile Strength at Break 15.9 MPa
2310 psi
Tensile Strength, Yield 4.40 MPa

@Strain 100 %
638 psi

@Strain 100 %
Elongation at Break 210 %
210 %
Tear Strength 20.6 kN/m
118 pli
at 25°C
Compression Set 13 %
13 %
70 hours at 25°C
9.0 %

@Temperature 100 °C
9.0 %

@Temperature 212 °F
70 hours
18 %

@Temperature 175 °C
18 %

@Temperature 347 °F
70 hours
25 %

@Temperature 200 °C
25 %

@Temperature 392 °F
70 hours
Thermal Properties Metric English Comments
Minimum Service Temperature, Air -14.0 °C
6.80 °F
TR test, TR10
-12.0 °C
10.4 °F
Gehman torsion test, T10
-8.00 °C
17.6 °F
TR test, TR70
-7.00 °C
19.4 °F
Gehman torsion test, T2
Brittleness Temperature -21.0 °C
-5.80 °F
Processing Properties Metric English Comments
Processing Temperature 170 °C
338 °F
Cure Measuring Temperature
Cure Time 2.40 min
0.0400 hour
Curelastmeter