Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 152 MPa | 22000 psi | Type I, 5.1 mm/min; ASTM D638 |
PolyOne Nymax™ ND 1233 GF Natural Polyamide 66 (Nylon 66) The Nymax® GF 1200 Series of glass fiber-reinforced nylon 6/6 compounds have been specifically formulated for applications requiring high stiffness, tensile properties, heat resistance, and durabil.. |
|||
Tensile Strength at Break | 152 MPa | 22000 psi | ASTM D638 |
Ravago Manufacturing Americas Hylon® N1043HL Nylon 6/6 (Cond) Information provided by Ravago. |
|||
Tensile Strength at Break | 152 MPa | 22000 psi | Type I, 5.1 mm/min; ASTM D638 |
PolyOne Nymax™ ND633 GF Natural Polyamide 6 (Nylon 6) The Nymax® GF 600 Series of glass fiber-reinforced nylon 6 compounds have been specifically engineered for applications requiring high stiffness, tensile strength, and toughness, while providing en.. |
|||
Tensile Strength at Break | 152 MPa | 22000 psi | ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP HFG25Z PA 11 LNP* Lubricomp* HFG25Z is a compound based on Nylon 11 resin containing 25% Glass Fiber, 10% Graphite. Added features of this material include: Internally Lubricated. |
|||
Tensile Strength at Break | 152 MPa | 22000 psi | ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP HFG25Z PA 11 (Asia Pacific) LNP* Lubricomp* HFG25Z is a compound based on Nylon 11 resin containing Glass Fiber, Graphite Powder. Added features of this material include: Internally Lubricated. |
|||
Tensile Strength at Break | 152 MPa | 22000 psi | ISO 527 Type 1A |
Solvay TECHNYL® eXten D218 V30 Nylon 6.10, 30% glass fiber, DRY Description: TECHNYL® eXten D 218 V30 is a 30% Glass Fiber reinforced and heat stabilized product suitable to the manufacturing of all injection molded parts. This material is available in black... |
|||
Tensile Strength at Break | 152 MPa | 22000 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP STAT-KON Valox_VCF2020 PET LNP* Stat-kon* Valox_VCF2020 compound is a 20% carbon fiber reinforced PET. Conductive applications. |
|||
Tensile Strength at Break | 152 MPa | 22000 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP DX10313 PC (Asia Pacific) DX10313 is high modulus polycarbonate, 50% glass filled, with balanced flow and impact strength |
|||
Tensile Strength at Break | 152 MPa | 22000 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP RX96592 PA 66 LNP* Thermocomp* RX96592 is a compound based on Nylon 6/6 containing Proprietary Fillers. |
|||
Tensile Strength at Break | 152 MPa | 22000 psi | ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP PF008QS PA 6 LNP THERMOCOMP* PF008QS is a compound based on Nylon 6 resin containing 40% Glass Fiber. Added features of this material include: Heat Stabilized, Reduced Moisture. |
|||
Tensile Strength at Break | 152 MPa | 22000 psi | ISO 527-2 |
Tisan TISESTER® 30% Glass Fiber Reinforced and heat Stabilized Polybutylene Terephthalate TISESTER has a wide area of application in automotive, electric/electronics and durable goods industries. General Specifications include: Excellent surface appearanceHigh corrosion and abrasion resi.. |
|||
Tensile Strength at Break | 152 MPa | 22000 psi | ASTM D638 |
Toyobo VYLOPET® EMC333 Injection Molding Polyester Resin, Hydrolysis Resistant Applications: Electric rice cooker partsBathroom appliancesFeatures: Good hydrolysis resistanceInformation provided by Toyobo. |
|||
Tensile Strength at Break | 152 MPa | 22000 psi | ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP SF008 PA 12 (Asia Pacific) LNP* Thermocomp* SF008 is a compound based on Nylon 12 resin containing Glass Fiber. |