SABIC Innovative Plastics LNP THERMOCOMP RX96592 PA 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP RX96592 PA 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Thermocomp* RX96592 is a compound based on Nylon 6/6 containing Proprietary Fillers.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.39 g/cc | 0.0502 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.850 % | 0.850 % | 50% RH, 24 hrs; ASTM D570 |
| 1.40 % | 1.40 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0060 cm/cm @Time 86400 sec |
0.0030 - 0.0060 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.040 cm/cm @Time 86400 sec |
0.010 - 0.040 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 152 MPa | 22000 psi | 5 mm/min; ISO 527 |
| 154 MPa | 22300 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 2.2 % | 2.2 % | Type I, 5 mm/min; ASTM D638 |
| 2.2 % | 2.2 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 10.21 GPa | 1481 ksi | 1 mm/min; ISO 527 |
| 10.3 GPa | 1490 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 218 MPa | 31600 psi | ISO 178 |
| 221 MPa | 32100 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Yield Strength | 222 MPa | 32200 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 8.81 GPa | 1280 ksi | 2 mm/min; ISO 178 |
| 9.14 GPa | 1330 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.670 J/cm | 1.26 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 6.26 J/cm | 11.7 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² | 2.86 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 37.0 kJ/m² | 17.6 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 7.00 J @Temperature 23.0 °C |
5.16 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 1.00 J | 0.738 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 38.1 µm/m-°C @Temperature -30.0 - 30.0 °C |
21.2 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 89.6 µm/m-°C @Temperature -30.0 - 30.0 °C |
49.8 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 253 °C | 487 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 255 °C @Thickness 3.20 mm |
491 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 233 °C | 451 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 239 °C @Thickness 3.20 mm |
462 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Polimeri Europa Riblene® FM 50 Low Density Polyethylene - Blown Film Extrusion
- Osprey Metals 85/15 Cu Sn Powder (Grade 90% - 16)
- PolyOne Geon™ Vinyl Flexible XV3856 Polyvinyl Chloride, Flexible (PVC, Flexible)
- Polymax® Maxelast® P1870 TPE, PP Overmold or Standalone use
- Monmouth Rubber & Plastics Durafoamâ„¢ P97SHD Red EPDM
- SABIC Innovative Plastics NORYL PX9406 PPE+PS
- Solvay Specialty Polymers FOMBLIN® LC55 PFPE Lubricant
- SABIC Innovative Plastics LNP STAT-KON 9X08403C Liquid Crystal Polymer (LCP)
- Dow DNDB-1077 NT 7 Linear Low Density Polyethylene Resin
- Polyram RamTal PM1027 Acetal, General Purpose
Copyright © lookpolymers.com All Rights Reserved