Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | <= 14.0 MPa | <= 2030 psi | ISO/R527 |
Polykemi AB POLYelast TPE Z900 Thermoplastic Elastomer, SEBS-based Information provided by Polykemi AB |
|||
Tensile Strength at Break | 14.0 MPa | 2030 psi | ISO 527 |
Total Lacqtene® FD 0270 LDPE, blown film, compounding, injection molding
(discontinued **) Low density radical polyethylene made by high pressure process. Temperature profile (°C) for injection molding: 200 to 260Information provided provided by Total Petrochemicals.Total Petrochemicals .. |
|||
Tensile Strength at Break | 14.0 MPa | 2030 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP FL003 PE LNP* LUBRICOMP* FL003 is a compound based on Polyethylene resin containing 15% PTFE. Added features include: Internally Lubricated. |
|||
Tensile Strength at Break | 14.0 MPa | 2030 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics NORYL WCD915 PPE-TPE (Asia Pacific) Flexible and non-halogenated flame retardant extrusion grade intended for evaluation in applications such as insulation materials. Flame retardant performance capable of meeting UL 1581 VW-1 require.. |
|||
Tensile Strength at Break | 14.0 MPa | 2030 psi | 50 mm/min, 1A; ISO 527 |
SABIC Innovative Plastics SABIC PPCOMPOUND 9710 PP SABIC® PPcompound 9710 is a mineral filled, impact modified polypropylene TPO. This material combines high impact resistance, scratch resistance, and heat stability with interior automotive UV st.. |
|||
Tensile Strength at Break | 14.0 MPa | 2030 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP TH0300B PU LNP* Thermocomp* Th0300B is a compound based on Polyurethane containing proprietary fillers. Characteristics of this grade are High Specific Gravity. |
|||
Tensile Strength at Break | 14.0 MPa | 2030 psi | ASTM D638 |
ELASTO UK Dryflex® 502850S SEBS Based Material, Unfilled Qualities, 85A Hardness, Black The 500-seriesis very favorable when transparency and good scratch resistance are required, as well as when there are high surface finish requirements. Unfilled grades have excellent flow and mecha.. |
|||
Tensile Strength at Break | 14.0 MPa | 2030 psi | ISO 37 |
ELASTO UK Dryflex® 9035-101 TPE, Modified Injection Molding Grade for Semi Rigid Molding The VTC TPE Group have developed endless formulations to fulfill different properties and application requirements to optimize the finished component. VTC Dryflex® 9035-101 is specifically designe.. |
|||
Tensile Strength at Break | 14.0 MPa | 2030 psi | ISO 527-1/-2 |
DSM Arnitel® PL380 Polyether Ester Elastomer (European and Asian Grade) Product description: Arnitel® combines the advantages of engineering thermoplastics, being easy to process with excellent mechanical properties, at the same time with the flexibility of rubbers.Arn.. |
|||
Tensile Strength at Break | >= 14.0 MPa | >= 2030 psi | ISO R 527 |
Fainplast Compounds CL 75 Flexible PVC, Sheathing General purposes |
|||
Tensile Strength at Break | >= 14.0 MPa | >= 2030 psi | ISO R 527 |
Fainplast Compounds CL 78 Flexible PVC, Sheathing General purposes |
|||
Tensile Strength at Break | >= 14.0 MPa | >= 2030 psi | ISO R 527 |
Fainplast Compounds CL 82/2 Flexible PVC, Sheathing General purposes |
|||
Tensile Strength at Break | >= 14.0 MPa | >= 2030 psi | ISO R 527 |
Fainplast Compounds CL 83/1 Flexible PVC, Sheathing Sheath coaxial TV Cable |
|||
Tensile Strength at Break | >= 14.0 MPa | >= 2030 psi | ISO R 527 |
Fainplast Compounds CL 87/T Flexible PVC, Sheathing Sheath antiroditor - antitermite |
|||
Tensile Strength at Break | >= 14.0 MPa | >= 2030 psi | ISO R 527 |
Fainplast Compounds GA 80 Flexible PVC, Flame Retardant Sheathing General purposes |
|||
Tensile Strength at Break | >= 14.0 MPa | >= 2030 psi | ISO R 527 |
Fainplast Compounds GA 83 Flexible PVC, Flame Retardant Sheathing General purposes |
|||
Tensile Strength at Break | >= 14.0 MPa | >= 2030 psi | ISO R 527 |
Fainplast Compounds GA 85 Flexible PVC, Flame Retardant Sheathing General purposes |
|||
Tensile Strength at Break | >= 14.0 MPa | >= 2030 psi | ISO R 527 |
Fainplast Compounds GK 85 Flexible PVC, Flame Retardant Sheathing Lead Free General purposes |
|||
Tensile Strength at Break | 14.0 MPa | 2030 psi | ISO R 527 |
Fainplast Compounds GS 70/T Flexible PVC, Injection Molding for Footwear Soles |
|||
Tensile Strength at Break | >= 14.0 MPa | >= 2030 psi | ISO R 527 |
Fainplast Compounds HGK 82 Flexible PVC, Sheathing for High Temperatures Lead Free Operating temperature 90°C |
|||
Tensile Strength at Break | 14.0 MPa | 2030 psi | ISO R 527 |
Fainplast Compounds MPH 69 Medical Flexible PVC, Extrusion Tubolar apparatus |
|||
Tensile Strength at Break | 14.0 MPa | 2030 psi | ASTM D638 |
Aclo Accutech Polypropylene Copolymer CP0437T20L1 Talc Reinforced |
|||
Tensile Strength at Break | 14.0 MPa | 2030 psi | ASTM D638 |
Arkema Group EVATANE® 28-25 Copolymer Ethylene - Vinyl Acetate EVATANE® 28-25 is a random copolymer of Ethylene and Vinyl Acetate made by high-pressure radicalar polymerisation process. EVATANE® 28-25 is stabilized with antioxidants. The High Vinyl Acetate co.. |
|||
Tensile Strength at Break | 14.0 - 30.0 MPa @Thickness 2.00 mm, Temperature 23.0 °C |
2030 - 4350 psi @Thickness 0.0787 in, Temperature 73.4 °F |
Type IV, 50 mm/min; ASTM D638 |
Solvay Specialty Polymers Solef® 31508 Polyvinylidene Fluoride (PVDF)
(Unverified Data**) Solef® 31508 PVDF copolymer is a low viscosity and very flexible grade for Wire & Cable applications.Information provided by Solvay Specialty Polymers. |
|||
Tensile Strength at Break | 14.0 MPa | 2030 psi | 500 mm/min; ASTM D638 - ISO 527-2 |
DuPont Elvaloy® 1126 AC Ethylene and 25% Methyl Acrylate Copolymer
(discontinued **) Elvaloy® 1126 AC is intended for coextrusion and molding. It can be recommended for blow molding of parts requiring permanent flexibility, stress cracking resistance and softness. Excellent fill.. |