Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | <= 12.0 MPa | <= 1740 psi | ISO/R527 |
Polykemi AB POLYelast TPE S902A Thermoplastic Elastomer, SBS-based Information provided by Polykemi AB |
|||
Tensile Strength at Break | 12.0 MPa | 1740 psi | ASTM D638 |
Petroquimica Triunfo Trithene® TS 9022 MDPE - Overwrap Packaging The Trithene TS 9022 resin is a medium-density polyethylene (MDPE) with good optical properties, excellent stiffness and processability, that warrants the production of thin films with good appearan.. |
|||
Tensile Strength at Break | 12.0 MPa | 1740 psi | ISO 527 |
Polimeri Europa Flexirene® MS 40 A Linear Low Density Polyethylene Flexirene MS 40 A is a linear low density polyethylene (LLDPE), with antioxidants, suitable for injection molding application.Parts made with Flexirene MS 40 A are characterized by a good balance be.. |
|||
Tensile Strength at Break | 12.0 MPa | 1740 psi | ASTM D638 |
SABIC M200024 Linear Low Density Polyethylene for Injection Molding Product Description: M200024 is a Linear Low Density Polyethylene grade with a narrow molecular weight distribution suitable for injection molding applications. It has been designed to give good f.. |
|||
Tensile Strength at Break | 12.0 MPa | 1740 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP FL004 PE LNP* Lubricomp* FL004 is a compound based on Polyethylene resin containing 20% PTFE. Added features of this material include: Internally Lubricated. |
|||
Tensile Strength at Break | 12.0 MPa | 1740 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics NORYL WCD801A PPE-TPE Flexible, migration-improved, halogen free extrusion grade intended for evaluation in applications such as wire insulation and cable jacket. Flame performance capable of meeting UL VW1 requirements.. |
|||
Tensile Strength at Break | 12.0 MPa | 1740 psi | 500mm/min; ASTM D638 Type IV Specimen |
Westlake EM800AA Low Density Polyethylene WESTLAKE low-density polyethylene EM800 is a general-purpose low-density formulation used for injection molding applications that require good stress-crack resistance.Application/UsesCosmetics/perso.. |
|||
Tensile Strength at Break | 12.0 MPa | 1740 psi | ISO 527-2/50 |
ExxonMobil Exxtral™ BMT222 Performance Polyolefin Product Description: A specialty thermoplastic polyolefin resin characterized by good stiffness/toughness balance and designed for automotive interior applications in which good surface finish and g.. |
|||
Tensile Strength at Break | >= 12.0 MPa | >= 1740 psi | ISO R 527 |
Fainplast Compounds AP 80 Flexible PVC, Flame Retardant Insulation General purposes |
|||
Tensile Strength at Break | >= 12.0 MPa | >= 1740 psi | 50 mm/min; ISO 527 |
Fainplast Compounds Ethylplus 600 Polyethylene Cable Compound Polyethelene, halogen-free cable compound with superior thermo-mechanical properties, outstanding heat resistance, and high electrical propertiesSolid LDPEInformation provided by Fainplast Compounds.. |
|||
Tensile Strength at Break | >= 12.0 MPa | >= 1740 psi | ISO R 527 |
Fainplast Compounds FR 70 Flexible PVC, Insulation Good flexibility cables |
|||
Tensile Strength at Break | >= 12.0 MPa | >= 1740 psi | ISO R 527 |
Fainplast Compounds FR 75 Flexible PVC, Insulation General purposes |
|||
Tensile Strength at Break | >= 12.0 MPa | >= 1740 psi | ISO R 527 |
Fainplast Compounds GA 75/1 Flexible PVC, Flame Retardant Sheathing General purposes |
|||
Tensile Strength at Break | 12.0 MPa | 1740 psi | ISO R 527 |
Fainplast Compounds GS 65/T Flexible PVC, Injection Molding for Footwear Crystal soles and sandals |
|||
Tensile Strength at Break | 12.0 MPa | 1740 psi | ISO R 527 |
Fainplast Compounds GS 70/AT Flexible PVC, Injection Molding for Transparent Technical Items Toys |
|||
Tensile Strength at Break | 12.0 MPa | 1740 psi | ISO R 527 |
Fainplast Compounds GS 7303 Flexible PVC, Injection Molding for Footwear Soles |
|||
Tensile Strength at Break | 12.0 MPa | 1740 psi | IEC 60811 |
Fainplast Compounds HAX HF 20 Halogen Free PVC Sheathing; Insulation, low cost for general purpose |
|||
Tensile Strength at Break | >= 12.0 MPa | >= 1740 psi | ISO R 527 |
Fainplast Compounds HGK 83/1 Flexible PVC, Sheathing for High Temperatures Lead Free Operating temperature 105°C |
|||
Tensile Strength at Break | 12.0 MPa | 1740 psi | ISO R 527 |
Fainplast Compounds GS 8202 Flexible PVC, Injection Molding for Footwear Soles |
|||
Tensile Strength at Break | 12.0 MPa | 1740 psi | IEC 60811 |
Fainplast Compounds HAX HF 4021 Halogen Free PVC General purpose |
|||
Tensile Strength at Break | 12.0 MPa | 1740 psi | ISO R 527 |
Fainplast Compounds MPH 62/H Medical Flexible PVC, Extrusion Technical tubes and peristaltic pump segments no DOP |
|||
Tensile Strength at Break | 12.0 MPa | 1740 psi | ASTM D638 |
Aclo Accutech Polypropylene Copolymer CP0437C10L Calcium Reinforced |
|||
Tensile Strength at Break | 12.0 MPa | 1740 psi | ASTM D638 |
Azdel SuperLite® SL550700-100 PP Resin Matrix / 55% Glass Fiber (3 mm Molded Thickness) AZDEL SuperLite® SL550700-100 is a low pressure, thermoformable, thermoplastic composite of polypropylene and long chopped glass fibers. Usually combined with outer layers as needed for the applic.. |
|||
Tensile Strength at Break | 12.0 MPa | 1740 psi | ASTM D638 |
Braskem PB 682 LDPE Blow Molding Polyethylene Description: PB682 is a low density polyethylene (LDPE), produced under high pressure technology. The end products molded with this resin present good dimensional stability and high flexibility.Appl.. |
|||
Tensile Strength at Break | 12.0 MPa | 1740 psi | |
AorTech Biomaterials Elast-Eon™ E5-130 Biomedical Polyurethane Pellets Elast-Eon™ polymers are used in biomedical applications. They have high biostability so they can be used for long term implantation. |
|||
Tensile Strength at Break | 12.0 MPa | 1740 psi | ASTM D638 |
Arkema Group LOTADER® 3210 Terpolymer Ethylene - Acrylic Ester - Maleic Anhydride LOTADER 3210 is a random terpolymer of Ethylene, Acrylic Ester and Maleic Anhydride, polymerized by high-pressure autoclave process. Main applicationsLOTADER 3210 is a versatile adhesive for extrusi.. |
|||
Tensile Strength at Break | 12.0 MPa | 1740 psi | ISO R 527 |
Fainplast Compounds PM 64/OP Flexible PVC, Lead Free Gaskets, Opaque surface |
|||
Tensile Strength at Break | 12.0 MPa | 1740 psi | ASTM D638 |
Azdel SuperLite® SL551400-100 PP Resin Matrix / 55% Glass Fiber (6 mm Molded Thickness) AZDEL SuperLite® SL551400-100 is a low pressure, thermoformable, thermoplastic composite of polypropylene and long chopped glass fibers. Usually combined with outer layers as needed for the applic.. |