Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 111 MPa | 16100 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics Lexan® HFD4413 PC Lexan* HFD4413 is a 30% glass filled, injection moldable grade designed for high flow and superior surface appearance. Internal mold release. |
|||
Tensile Strength at Break | 111 MPa | 16100 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics Lexan® HFD4413 PC (Asia Pacific) Lexan* HFD4413 is a 30% glass filled, injection moldable grade designed for high flow and superior surface appearance. Internal mold release. |
|||
Tensile Strength at Break | 111 MPa | 16100 psi | 5 mm/min; ISO 527 |
Lavergne VYPET VNT 340 PET 40% Glass - Mineral Reinforced Vypet VNT 340 is a 40% glass/mineral reinforced PET injection molding compound designed for electrical and structural applications, with High Dielectric StrengthFeatures: High temperature performanc.. |
|||
Tensile Strength at Break | 111 MPa | 16100 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP STAT-KON DE0026 PC (Europe-Africa-Middle East) LNP* Stat-kon* DC-1002 FR is a compound based on Polycarbonate resin containing Flame Retardant, Carbon Fiber. Added features of this material include: Flame Retardant, Electrically Conductive. |
|||
Tensile Strength at Break | 111 MPa | 16100 psi | ASTM D638 |
SABIC Innovative Plastics LNP STAT-KON DX04489C PC LNP STAT-KON* DX04489C is a high modulus compound based on Polycarbonate resin containing Proprietary Filler(s). Added features of this material include: Clean Compounding System, Electrically Con.. |
|||
Tensile Strength at Break | 111 MPa | 16100 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics Valox® SHF436HR PBT PBT, Super High Flow, 30% glass reinforced,hydrolytically resistant. |
|||
Tensile Strength at Break | 111 MPa | 16100 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics Valox® SHF436HR PBT (Asia Pacific) PBT, Super High Flow, 30% glass reinforced,hydrolytically resistant. |
|||
Tensile Strength at Break | 111 MPa | 16100 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics Valox® SHF436HR PBT (Europe-Africa-Middle East) PBT, Super High Flow, 30% glass reinforced,hydrolytically resistant. |
|||
Tensile Strength at Break | 111 MPa | 16100 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP STAT-KON Lexan_LCF1506 PC LNP* Stat-kon* Lexan_LC1500N compound is a 15% carbon fiber, 6% PTFE reinforced polycarbonate. |
|||
Tensile Strength at Break | 111 MPa | 16100 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP STAT-KON Lexan_LCF1506 PC (Europe-Africa-Middle East) LNP* Stat-kon* Lexan_LCF1506 is a 15% carbon fiber, 6% PTFE reinforced polycarbonate. |
|||
Tensile Strength at Break | 111 MPa | 16100 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP Stat-kon ZX05043 PPE+PS (Europe-Africa-Middle East) LNP* Stat-kon* ZX05043 is a compound based on PPE+PS Blend resin containing Glass Fiber, PTFE, Carbon Fiber.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region. |
|||
Tensile Strength at Break | 111 MPa | 16100 psi | ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP DX06410 PC (Asia Pacific) LNP* Thermocomp* DX06410 is a compound based on Polycarbonate resin containing Glass Fiber. Added features of this material include: Easy Molding, Mold Release. |
|||
Tensile Strength at Break | 111 MPa | 16100 psi | ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP QF004 PA 6/10 LNP* THERMOCOMP* QF004 is a compound based on Nylon 6/10 resin containing 20% Glass Fiber. |
|||
Tensile Strength at Break | 111 MPa | 16100 psi | ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP QF004 PA 6/10 (Asia Pacific) LNP* Thermocomp* QF004 is a compound based on Nylon 6/10 resin containing Glass Fiber. |
|||
Tensile Strength at Break | 111 MPa | 16100 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP WF006L PBT LNP* THERMOCOMP* WF006L is a compound based on PBT resin containing 30% Glass Fiber. Added feature of this material is: Low Extractible. |
|||
Tensile Strength at Break | 111 MPa | 16100 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP ZF006 PPE+PS LNP* THERMOCOMP* ZF006 is a compound based on PPE+PS resin containing 30% Glass Fiber. |
|||
Tensile Strength at Break | 111 MPa | 16100 psi | ASTM D638 |
SABIC Innovative Plastics LNP STAT-KON DEL36 PC (Asia Pacific) LNP* Stat-kon* DEL36 is a compound based on Polycarbonate resin containing PTFE, Carbon Fiber. Added features of this material include: Electrically Conductive, , Internally Lubricated. |
|||
Tensile Strength at Break | 111 MPa | 16100 psi | Type I, 5 mm/min; ASTM D 638 |
SABIC Innovative Plastics LNP Thermocomp LFZ42XXC PEEK LNP THERMOCOMP* LFZ42XXC is a compound based on Polyetheretherketone resin containing Glass Fiber, Milled Glass. Added features of this material include: Low Warpage.This data was supplied by SABIC.. |
|||
Tensile Strength at Break | 111 MPa | 16100 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics Lexan® HFD4413 PC (Europe-Africa-Middle East) Lexan* HFD4413 is a 30% glass filled, injection moldable grade designed for high flow and superior surface appearance. Internal mold release. |
|||
Tensile Strength at Break | 111 MPa | 16100 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP STAT-KON Lexan_LCF1506 PC (Asia Pacific) 15% carbon fiber, 6% PTFE reinforced polycarbonate. |
|||
Tensile Strength at Break | 111 MPa | 16100 psi | ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP DX06410 PC LNP* THERMOCOMP* DX06410 is a compound based on Polycarbonate resin containing 20% Glass Fiber. Added features of this material include: Easy Molding, Mold Release. |