Polymer Property : Tensile Strength at Break = 9.00 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	9.00 MPa	1310 psi	ISO 527
Polimeri Europa Clearflex® MQ F0 Very Low Density Polyethylene Clearflex MQ F0 is a linear polyethylene, with antioxidants, characterized by a very low density (VLDPE).The resin shows an excellent balance between flexibility and impact resistance.Main Applicati..
Tensile Strength at Break	9.00 - 13.0 MPa	1310 - 1890 psi	ASTM D412
Proto3000 Objet Digital Materials™ DM_9610 Rubber-like Prototyping Polymer Primary material: TangoGraySecondary material: VeroBlackDigital Materials are made up of two Objet materials. The two materials are combined in specific concentrations and structures, to provide the..
Tensile Strength at Break	9.00 MPa	1310 psi	500mm/min; ASTM D638
Westlake EMAC® SP1402 Specialty Copolymer (discontinued **) EMAC resins adhere to and are compatible with a wide range of materials including paper, polyolefins, oriented polyolefins, polyesters, ionomers, PVdC, unplasticized PVC and other polar polymers. Fo..
Tensile Strength at Break	9.00 MPa	1310 psi	500 mm/min; ASTM D638
Eastman E6838-913P Polyethylene (discontinued **) Polyethylene E6838-913P natural is a specialty formulation suggested for high-speed extrusion coating applications. E6838-913P offers improvements over standard low-density polyethylene in adhesion ..
Tensile Strength at Break	9.00 MPa	1310 psi	50 mm/min test speed; ASTM D 638
NOVA Chemicals Sclair® 72A Butene Copolymer LLDPE Injection Molding Resin 72A complies with the U.S. FDA specifications for olefin polymers and may thus be used in the United States as an article or component of an article intended for use in contact with food. 72A is su..
Tensile Strength at Break	9.00 MPa	1310 psi	50 mm/min; ISO 527
SABIC Innovative Plastics NORYL WCP921A PPE-TPE Flexible Noryl* injection molding grade. Low specific gravity with good non-halogenated flame retardant performance. Developed for overmolding applications such as plugs, strain reliefs, and connect..
Tensile Strength at Break	9.00 MPa	1310 psi	50 mm/min; ISO 527
SABIC Innovative Plastics NORYL WCP921A PPE-TPE (Europe-Africa-Middle East) Flexible Noryl* injection molding grade. Low specific gravity with good non-halogenated flame retardant performance. Developed for overmolding applications such as plugs, strain reliefs, and connect..
Tensile Strength at Break	9.00 MPa	1310 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP PDXF89080 PE LNP* LUBRICOMP* PDXF89080 is a compound based on Polyethylene containing Proprietary Fillers. Added feature of this grade is: Wear Resistant.
Tensile Strength at Break	9.00 MPa	1310 psi	Type I, 50 mm/min; ASTM D638
SABIC Innovative Plastics NORYL WCD933 PPE-TPE (Europe-Africa-Middle East) Flexible and non-halogenated flame retardant extrusion grade intended for evaluation in applications such as insulation of HD 21.14 flexible cables. Flame retardant performance capable of meeting EN..
Tensile Strength at Break	9.00 MPa	1310 psi	500mm/min; ASTM D638 Type IV Specimen
Westlake EC1390AA Low Density Polyethylene WESTLAKE low-density polyethylene EC1390 is used primarily in extrusion-coating applications that require fast line speeds and relatively low coating weights. When compared with other low-density po..
Tensile Strength at Break	9.00 MPa	1310 psi	ASTM D638
ELASTO UK Dryflex® 420351S SBS Based Material, 35D Hardness, Natural The 400S-series is a good alternative for indoor applications and disposable articles that do not have high requirements for ageing and heat resistance. The raw materials are specially selected for..
Tensile Strength at Break	9.00 MPa	1310 psi	ASTM D638
ELASTO UK Dryflex® 602800S SEBS Based Material, Filled Qualities, 80A Hardness, Black The most significant features of the 600-series are the improved heat stability, the sound reduction and that the material enables an easy and secure pigmenting for the customer. A filled material ..
Tensile Strength at Break	9.00 MPa	1310 psi	ASTM D638
ELASTO UK Dryflex® 662750S SEBS Based Material, Semi-Filled Qualities, 75A Hardness, Black The 660-series is recommended when the properties of the produced detail requires the advantages of the 500-series in combination with the 600-series. A semi-filled material can therefore combine t..
Tensile Strength at Break	9.00 MPa	1310 psi	ASTM D638
ELASTO UK Dryflex® 662800S SEBS Based Material, Semi-Filled Qualities, 80A Hardness, Black The 660-series is recommended when the properties of the produced detail requires the advantages of the 500-series in combination with the 600-series. A semi-filled material can therefore combine t..
Tensile Strength at Break	9.00 MPa	1310 psi	ISO R 527
Fainplast Compounds GS 55 Flexible PVC, Injection Molding for Footwear Tennis shoes
Tensile Strength at Break	9.00 MPa	1310 psi	ISO R 527
Fainplast Compounds GS 58/O Flexible PVC, Injection Molding for Footwear Antislip soles, opaque surface
Tensile Strength at Break	9.00 MPa	1310 psi	IEC 60811
Fainplast Compounds HAX HF 039/31 Halogen Free PVC Sheathing, insulation; high flexibility
Tensile Strength at Break	9.00 MPa	1310 psi	ISO 527-1/-2
DuPont Performance Polymers Hytrel® HTR8351 NC021 Polyester Elastomer TPC-ET (Unverified Data**) 30 Shore D Easy-to-Strip UV Stabilized Polyester Elastomer with Non-discoloring Stabilizer Developed for Extrusion Information provided by DuPont Performance Polymers
Tensile Strength at Break	9.00 MPa	1310 psi	ASTM D638
Arkema Group LOTRYL® 20 MA 08 Copolymer Ethylene - Methyl Acrylate LOTRYL® 20 MA 08 is a random copolymer of ethylene and methyl acrylate made by high-pressure radicalar polymerisation process. Due to the high methyl acrylate content, LOTRYL® 20 MA 08 is a polyme..
Tensile Strength at Break	9.00 MPa	1310 psi	ASTM D638
Arkema Group LOTADER® 3430 Terpolymer Ethylene - Acrylic Ester - Maleic Anhydride LOTADER 3430 is a random terpolymer of Ethylene, Acrylic Ester and Maleic Anhydride, polymerized by high-pressure autoclave process. LOTADER 3430 is a versatile adhesive for extrusion coating or lam..
Tensile Strength at Break	9.00 MPa	1310 psi	ASTM D638
Arkema Group LOTADER® 4503 Terpolymer Ethylene - Acrylic Ester - Maleic Anhydride LOTADER 4503 is a random terpolymer of Ethylene, Acrylic Ester and Maleic Anhydride, polymerized by high-pressure autoclave process.LOTADER 4503 is a versatile adhesive for extrusion lamination, des..
Tensile Strength at Break	9.00 - 11.0 MPa	1310 - 1600 psi	ISO 527-1
Adamas Adalon® 453 PTFE, Mica filler Information provided by Adamas, HPM
Tensile Strength at Break	9.00 MPa	1310 psi	ASTM-D638
Braskem IF33 LLDPE Injection Molding Polyethylene Copolymer IF33 is a linear low-density polyethylene, narrow molecular weight butene-1 copolymer produced by the solution process for injection molding applications. It offers high fluidity, good flexibility, ..
Tensile Strength at Break	9.00 MPa	1310 psi	ASTM-D638
Braskem IJ33D LLDPE Injection Molding Polyethylene Copolymer IJ33D is a linear low-density polyethylene, narrow molecular weight butene-1 copolymer produced by the solution process for injection molding applications. It offers high fluidity, excellent flexibi..
Tensile Strength at Break	>= 9.00 MPa	>= 1310 psi
Beijing Evergrow Resources PTFE, 24% Bronze, 12% Glass Fiber, 6% Graphite Filled Filled PTFE article is manufactured by molding method with filled PTFE resin. Filled PTFE resin is manufactured by compounding PTFE granular resin with filler. Broadly speaking PTFE compounds have t..