- Polymer Property : Tensile Strength at Break = 68.0 MPa
Polymer Property : Tensile Strength at Break = 68.0 MPa Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 68.0 MPa | 9860 psi | |
| Plastcom SLOVAMID 66 MI PA66, improved strength FeaturesModified with thermoplastic reactive caoutchouc, determined for mouldings with high toughness also at minus temperatures. Eligible application for ski-shoes, helmets for sport and other safe.. |
|||
| Tensile Strength at Break | 68.0 MPa | 9860 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics Cycolac® INP576 ABS+SAN Can be used as compounding additives for polymer blends. Medium molecular weight SAN. Can be blended with high rubber graft modifier resins to produce customized ABS properties. Suitable for direc.. |
|||
| Tensile Strength at Break | 68.0 MPa | 9860 psi | Type I, 50 mm/min; ASTM D638 |
| SABIC Innovative Plastics Lexan® 101 PC (Asia Pacific) Nonhalogenated, 7.0 MFR, for thicker sections without sinks. |
|||
| Tensile Strength at Break | 68.0 MPa | 9860 psi | Type I, 50 mm/min; ASTM D638 |
| SABIC Innovative Plastics Lexan® 101R PC (Asia Pacific) Nonhalogenated. 7.0 MFR, for thicker sections without sinks. Internal mold release. |
|||
| Tensile Strength at Break | 68.0 MPa | 9860 psi | Type I, 50 mm/min; ASTM D 638 |
| SABIC Innovative Plastics Lexan® 105 PC General purpose low flow Polycarbonate powder gradeThis data was supplied by SABIC-IP for the Americas region. |
|||
| Tensile Strength at Break | 68.0 MPa | 9860 psi | Type I, 50 mm/min; ASTM D638 |
| SABIC Innovative Plastics Lexan® 124 PC (Asia Pacific) 17.5 MFR, for small, intricate parts. FDA food contact compliant in limited colors. Effective January 15th, 2007 this grade is no longer supported with biocompatibility information and should not .. |
|||
| Tensile Strength at Break | 68.0 MPa | 9860 psi | Type I, 50 mm/min; ASTM D 638 |
| SABIC Innovative Plastics Lexan® 221 PC 17.5 MFR, for small, intricate parts. Improved flame retardance.This data was supplied by SABIC-IP for the Americas region. |
|||
| Tensile Strength at Break | 68.0 MPa | 9860 psi | Type I, 50 mm/min; ASTM D638 |
| SABIC Innovative Plastics Lexan® 221 PC (Asia Pacific) 17.5 MFR, for small, intricate parts. Improved flame retardance. |
|||
| Tensile Strength at Break | 68.0 MPa | 9860 psi | Type I, 50 mm/min; ASTM D638 |
| SABIC Innovative Plastics Lexan® 221R PC (Asia Pacific) 17.5 MFR, for small, intricate parts. Improved flame retardance. Internal mold release. |
|||
| Tensile Strength at Break | 68.0 MPa | 9860 psi | Type I, 50 mm/min; ASTM D 638 |
| SABIC Innovative Plastics Lexan® 945ASR PC Lexan* 945ASR Polycarbonate (PC) resin is a non-filled, injection moldable grade. This non-chlorinated, non-brominated flame retardant PC has an UL-94 V0 rating and is available in transparent and t.. |
|||
| Tensile Strength at Break | 68.0 MPa | 9860 psi | 50 mm/min; ISO 527 |
| SABIC Innovative Plastics Lexan® FXD9945A PC UV stabilzed Visualfx FR PC with non-brominated and non-chlorinated flame retardant systems. It is available Only in white diffused effect(WH8B111X) meeting UL-94 V0 at 2mm for thin wall application.. |
|||
| Tensile Strength at Break | 68.0 MPa | 9860 psi | 50 mm/min; ISO 527 |
| SABIC Innovative Plastics Lexan® HFD1413 PC Copolymer 11 MFR LEXAN High Flow Ductile Copolymer |
|||
| Tensile Strength at Break | 68.0 MPa | 9860 psi | Type I, 50 mm/min; ASTM D638 |
| SABIC Innovative Plastics Lexan® HP2C PC (Asia Pacific) Med/high flow polycarbonate. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 or USP Class VI). EtO and steam sterilizable. Contains m.. |
|||
| Tensile Strength at Break | 68.0 MPa | 9860 psi | Type I, 50 mm/min; ASTM D638 |
| SABIC Innovative Plastics Lexan® HPS2R PC Med/high flow polycarbonate. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 or USP Class VI). EtO, steam, e-beam and gamma sterilizable.. |
|||
| Tensile Strength at Break | 68.0 MPa | 9860 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics Lexan® JK500 PC+ABS (Asia Pacific) 10% GR, ECO conforming FR, PC+ABS for thinwall molding applications. |
|||
| Tensile Strength at Break | 68.0 MPa | 9860 psi | Type I, 50 mm/min; ASTM D 638 |
| SABIC Innovative Plastics Lexan® ML7678 PC 17.5 MFR, for small, intricate parts. FDA food contact compliant in limited colors. Enhanced mold release package.This data was supplied by SABIC-IP for the Americas region. |
|||
| Tensile Strength at Break | 68.0 MPa | 9860 psi | Type I, 50 mm/min; ASTM D 638 |
| SABIC Innovative Plastics Lexan® OQ2220 PC Ophthalmic/safety lens market. OQ2xxx series in all transparent tints. Dedicated equipment, stringent production control conditions.This data was supplied by SABIC-IP for the Americas region. |
|||
| Tensile Strength at Break | 68.0 MPa | 9860 psi | Type I, 50 mm/min; ASTM D638 |
| SABIC Innovative Plastics Lexan® 101 PC UL rated HB as of 10/97. 200 series recommended when V-2 rating required. Nonhalogenated, 7.0 MFR, for thicker sections without sinks. |
|||
| Tensile Strength at Break | 68.0 MPa | 9860 psi | Type I, 50 mm/min; ASTM D638 |
| SABIC Innovative Plastics Lexan® 144R PC UL rated HB. 200 series recommended when V-2 rating required. MFR 10.5. Internal mold release. FDA food contact compliant in limited colors.Effective January 15th, 2007 this grade will no longer .. |
|||
| Tensile Strength at Break | 68.0 MPa | 9860 psi | 50 mm/min; ISO 527 |
| SABIC Innovative Plastics Lexan® HPH4704 PPC (Europe-Africa-Middle East) High heat specialty polycarbonate. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 or USP Class VI). EtO, steam, gamma and e-beam steril.. |
|||
| Tensile Strength at Break | 68.0 MPa | 9860 psi | Type I, 50 mm/min; ASTM D638 |
| SABIC Innovative Plastics Lexan® HPS6R PC Low/med flow polycarbonate. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 or USP Class VI). Contains a higher amount of mold release t.. |
|||
| Tensile Strength at Break | 68.0 MPa | 9860 psi | ISO 527 |
| SABIC Innovative Plastics LNP COLORCOMP DX04401H PC LNP* COLORCOMP* DX04401H is an unfilled Polycarbonate. Added feature of this grade is: Healthcare. |
|||
| Tensile Strength at Break | 68.0 MPa | 9860 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics LNP Thermocomp MX06050 PP (Europe-Africa-Middle East) LNP* THERMOCOMP* MX06050 is a compound based on Polypropylene resin containing Glass Fiber. Added features include; Heat Stabilized.This data was supplied by SABIC-IP for the Europe-Africa-Middle Ea.. |
|||
| Tensile Strength at Break | 68.0 MPa | 9860 psi | ISO 527-2/50 |
| Styron CALIBREâ„¢ 2061-15 Polycarbonate Resin Overview: CALIBREâ„¢ 2061-15 resin is suitable for steam and ethylene oxide sterilization required by the health care industry. CALIBRE 2061-15 provides excellent heat resistance, impact strength.. |
|||
| Tensile Strength at Break | 68.0 MPa | 9860 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics NORYL GTX GTX975 PPE+PA NORYL GTX975 is a 18% mineral filled material especially designed for in- or on-line painted exterior automotive trim part, e.g. tankflaps and corner panels. This material combines high stiffness an.. |
|||
| Tensile Strength at Break | 68.0 MPa | 9860 psi | 50 mm/min; ISO 527 |
| SABIC Innovative Plastics Noryl LS175 PPE+HIPS Noryl* LS175 modified polyphenylene ether resin is an unfilled grade suitable for both extrusion and injection molding conversion routes. It uses non-chlorinated, non-brominated FR additives to del.. |
|||
| Tensile Strength at Break | 68.0 MPa | 9860 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics NORYL EM7301F PPE+PS 10% glass-reinforced. HDT 252F. Good flow and polyurethane foam adhesion. Black only. |
|||
| Tensile Strength at Break | 68.0 MPa | 9860 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics NORYL GTX GTX675 PPE+PA6 Noryl GTX* GTX675 Resin is a blend of Polyphenylene Ether(PPE) + Polyamide(PA) resin that is mineral filled, conductive, and suitable for injection molding. The conductivity level is optimized to a.. |
|||
| Tensile Strength at Break | 68.0 MPa | 9860 psi | Type I, 50 mm/min; ASTM D 638 |
| SABIC Innovative Plastics Lexan® FXE101 PC Transparent PC. ILLUMINATE special effects (fluorescent/edge glow colors). 7.0 MFR, for thicker sections without sinks.This data was supplied by SABIC-IP for the Americas region. |
|||
| Tensile Strength at Break | 68.0 MPa | 9860 psi | 50 mm/min; ISO 527 |
| SABIC Innovative Plastics Lexan® HFD1433 PC Copolymer (Europe-Africa-Middle East) 11 MFR LEXAN High Flow Ductile Copolymer UV stabilized, available in transparent colors only |
|||