Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 39.2 MPa | 5690 psi | ASTM D638 |
Samsung Cheil Industries Starex® VH-0850 ABS, Unreinforced
(discontinued **) Amorphous Acrylonitrile Butadiene Styrene (ABS)Characteristics: Flame Retardant: Balance of Properties (Impact, Mechanical and Heat)Applications: Computer, Monitor and Printer Housings, Microwave Co.. |
|||
Tensile Strength at Break | 39.2 MPa | 5690 psi | ASTM D412 |
Huntsman IROGRAN® PS 455-215 TPU-Polyester Polyester-based grades with a broad processing window ideally suited for cast, flat die and flown film lines.Information provided by Alliance Polymers |
|||
Tensile Strength at Break | 39.2 MPa @Thickness 2.00 mm |
5690 psi @Thickness 0.0787 in |
50mm/min; ASTM D638 |
LG Chemical KEYFLEX BT HB9255D Ester Type TPE Description: TPC-ET, Blow Moldable, Medium Modulus, Black ColorApplication: Air duct, Hose & TubingCAS: 37282-12-5, 24968-12-5 and 1333-86-4Information provided by LG Chemical |
|||
Tensile Strength at Break | 39.2 MPa | 5690 psi | 5 mm/min; ASTM D638 |
Samsung Cheil Industries Starex® HG-0760LT ABS, Unreinforced Information provided by Samsung Cheil Industries. |
|||
Tensile Strength at Break | 39.2 MPa | 5690 psi | ASTM D638 |
Samsung Cheil Industries Starex® SF-0505H MABS, Unreinforced Scratch Resistant Information provided by Samsung Cheil Industries. |
|||
Tensile Strength at Break | 39.2 MPa | 5690 psi | 50 mm/min; ASTM D638 |
Samsung Cheil Industries Infino® WP-1041G PC/ABS, Unreinforced Metal Plating Grade Information provided by Samsung Cheil Industries. |
|||
Tensile Strength at Break | 39.2 MPa | 5690 psi | 5 mm/min; ASTM D638 |
Samsung Cheil Industries Starex® HG-0760LT ABS, Unreinforced Information provided by Samsung Cheil Industries. |
|||
Tensile Strength at Break | 39.2 MPa | 5690 psi | ASTM D638 |
Samsung Cheil Industries Starex® SF-0505H MABS, Unreinforced Scratch Resistant Information provided by Samsung Cheil Industries. |
|||
Tensile Strength at Break | 39.2 MPa | 5690 psi | 50 mm/min; ASTM D638 |
Supreme Petrochem SP 255 Toughened Polystyrene Characteristics Superior flexibility Excellent flow grade High ball drop strength Good clarityProcessing Extrusion Thermoforming Injection MoldingApplications Transparent hangers, stationery it.. |
|||
Tensile Strength at Break | 39.2 MPa | 5690 psi | 50 mm/min; ASTM D638 |
Supreme Petrochem SP 6456 High Heat Polystyrene Characteristics High heat resistance & strength Very good flow properties Available in any dark colorsProcessing Injection moldingApplications Instrument enclosures TV components Electrical encl.. |
|||
Tensile Strength at Break | 39.2 MPa | 5690 psi | 78% Ret. |
UBE UBESTA® 3030U Nylon 12 (After Toluene for 1000 hours) Description: UBESTA has a strong resistance to chemicals. Under normal conditions, it is not significantly affected by alkalis, alcohols, ethers, ketones, hydrocarbons, lubricating oils, gasoline, c.. |
|||
Tensile Strength at Break | 39.2 MPa | 5690 psi | 50 mm/min; ASTM D638 |
Samsung Cheil Industries Infino® WP-1041G PC/ABS, Unreinforced Metal Plating Grade Information provided by Samsung Cheil Industries. |