Huntsman IROGRAN® PS 455-215 TPU-Polyester
| Category | Polymer , Thermoplastic , Polyurethane, TP , Thermoplastic Polyurethane (TPUR), Polyester Grade |
| Manufacturer | Huntsman Corporation |
| Trade Name | IROGRAN® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Huntsman IROGRAN® PS 455-215 TPU-Polyester.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Polyester-based grades with a broad processing window ideally suited for cast, flat die and flown film lines.Information provided by Alliance Polymers
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in³ | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 78 | 78 | ASTM D2240 |
| Hardness, Shore D | 31 | 31 | ASTM D2240 |
| Tensile Strength at Break | 39.2 MPa | 5690 psi | ASTM D412 |
| Elongation at Break | 610 % | 610 % | ASTM D412 |
| 50% Modulus | 0.000689 GPa | 0.100 ksi | ASTM D412 |
| 100% Modulus | 0.00124 GPa | 0.180 ksi | ASTM D412 |
| 300% Modulus | 0.00552 GPa | 0.800 ksi | ASTM D412 |
| Rebound | 45 % | 45 % | Bayshore; ASTM D2632 |
| Tear Strength | 57.8 kN/m | 330 pli | ASTM D624 |
| Taber Abrasion, mg/1000 Cycles | 10 | 10 | ASTM D3389 |
| Abrasion | 54 | 54 | mm<sup>3</sup>; DIN 53516 |
| Compression Set | 34 % @Temperature 22.8 °C, Time 79200 sec |
34 % @Temperature 73.0 °F, Time 22.0 hour |
ASTM D395 |
| 82 % @Temperature 70.0 °C, Time 79200 sec |
82 % @Temperature 158 °F, Time 22.0 hour |
ASTM D395 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 129 - 142 °C | 264 - 288 °F | TMA Melt Range |
| Vicat Softening Point | 61.0 °C | 142 °F | ASTM D1525 |
| Glass Transition Temp, Tg | -32.0 °C | -25.6 °F | Midpoint; ASTM E 1269 |
Users viewing this material also viewed the following:
- MV Labs BI400 BiCl3 Bismuth chloride
- SABIC Innovative Plastics Cycoloy® C6200 PC+ABS
- Kinlead HSD12 Normal Grade Heat Sealable Film (thickness: 30 µm)
- Ineos Nova T443B Expandable Polystyrene
- Michelman® Licomer® W 19 Anionic / Nonionic polyethylene emulsion
- SABIC Innovative Plastics LNP STAT-KON DX09315C PC (Asia Pacific)
- Samsung Cheil Industries Starex® TX-0530T TRABS, Unreinforced
- A. Schulman POLYBATCH™ Canyon 10290U/4 Concentrate Based In LLDPE
- ExxonMobil Paxon™ AM55-003 Blow Molding Resin (discontinued **)
Copyright © lookpolymers.com All Rights Reserved