Samsung Cheil Industries Infino® WP-1041G PC/ABS, Unreinforced Metal Plating Grade

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Samsung Cheil Industries Infino® WP-1041G PC/ABS, Unreinforced Metal Plating Grade.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by Samsung Cheil Industries.
Physical Properties Metric English Comments
Specific Gravity 1.05 g/cc
1.05 g/cc
ASTM D792
Linear Mold Shrinkage, Flow 0.0050 - 0.0060 cm/cm

@Thickness 3.20 mm
0.0050 - 0.0060 in/in

@Thickness 0.126 in
ASTM D955
Linear Mold Shrinkage, Transverse 0.0050 - 0.0060 cm/cm

@Thickness 3.20 mm
0.0050 - 0.0060 in/in

@Thickness 0.126 in
ASTM D955
Melt Flow 3.0 g/10 min

@Load 2.16 kg,
Temperature 250 °C
3.0 g/10 min

@Load 4.76 lb,
Temperature 482 °F
ASTM D1238
31 g/10 min

@Load 10.0 kg,
Temperature 250 °C
31 g/10 min

@Load 22.0 lb,
Temperature 482 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 105
105
ASTM D785
Tensile Strength at Break 39.2 MPa
5690 psi
50 mm/min; ASTM D638
Tensile Strength, Yield 49.0 MPa
7110 psi
50 mm/min; ASTM D638
Elongation at Break 100 %
100 %
50 mm/min; ASTM D638
Tensile Modulus 1.91 GPa
277 ksi
50 mm/min; ASTM D638
Flexural Strength 65.7 MPa
9530 psi
2.8 mm/min; ASTM D638
Flexural Modulus 1.91 GPa
277 ksi
2.8 mm/min; ASTM D638
Izod Impact, Notched 2.45 J/cm

@Thickness 6.35 mm,
Temperature -30.0 °C
4.59 ft-lb/in

@Thickness 0.250 in,
Temperature -22.0 °F
ASTM D256
3.92 J/cm

@Thickness 3.17 mm,
Temperature -30.0 °C
7.35 ft-lb/in

@Thickness 0.125 in,
Temperature -22.0 °F
ASTM D256
4.12 J/cm

@Thickness 6.35 mm,
Temperature 23.0 °C
7.71 ft-lb/in

@Thickness 0.250 in,
Temperature 73.4 °F
ASTM D256
5.39 J/cm

@Thickness 3.17 mm,
Temperature 23.0 °C
10.1 ft-lb/in

@Thickness 0.125 in,
Temperature 73.4 °F
ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 100 °C

@Thickness 6.40 mm
212 °F

@Thickness 0.252 in
ASTM D648
Vicat Softening Point 111 °C
232 °F
B/50; ISO R306