Supreme Petrochem SP 255 Toughened Polystyrene
| Category | Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Impact Modified |
| Manufacturer | Supreme Petrochem LTD |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Supreme Petrochem SP 255 Toughened Polystyrene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Characteristics Superior flexibility Excellent flow grade High ball drop strength Good clarityProcessing Extrusion Thermoforming Injection MoldingApplications Transparent hangers, stationery items, medical products Extrusion thermoformed clear and deep draw containers Glossy, tough cap layer on HIPS SheetsMaterial Status: Commercial : ActiveAgency Ratings: FDA 21 CFR 177.1640Information provided by Supreme Petrochem LTD
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.03 g/cc | 1.03 g/cc | ASTM D792 |
| Melt Flow | 6.0 g/10 min @Load 5.00 kg, Temperature 200 °C |
6.0 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 39.2 MPa | 5690 psi | 50 mm/min; ASTM D638 |
| Elongation at Break | 10 % | 10 % | 50 mm/min; ASTM D638 |
| Flexural Strength | 53.9 MPa @Thickness 3.20 mm |
7820 psi @Thickness 0.126 in |
ASTM D790 |
| Flexural Modulus | 1.96 GPa @Thickness 3.20 mm |
284 ksi @Thickness 0.126 in |
ASTM D790 |
| Izod Impact, Notched | 2.00 J/cm @Thickness 3.20 mm |
3.75 ft-lb/in @Thickness 0.126 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 77.0 °C | 171 °F | ASTM D648 |
| Vicat Softening Point | 102 °C | 216 °F | 1kg / 120°C; ASTM D1525 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 2.0 % @Thickness 1.00 mm |
2.0 % @Thickness 0.0394 in |
|
| Transmission, Visible | 82 % @Thickness 1.00 mm |
82 % @Thickness 0.0394 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | <= 220 °C | <= 428 °F | |
| Mold Temperature | 40.0 - 50.0 °C | 104 - 122 °F |
Users viewing this material also viewed the following:
- Potters Industries Q-Cel® 7023S Hollow Engineered Glass Microspheres
- Polymer Resources NY6-IM1 Nylon 6, Impact Modified
- ICO Polymers ICORENEâ„¢ 150-1498 HDPE Rotational Molding Resin
- H.C. Starck Amperit® 519.074 Agglomerated, Sintered Tungsten Carbide-Cobalt 88-12 (WC-CO)
- Multibase Multi-Flex® D 2010 TPE Thermoplastic Elastomer
- SGL Carbon Group SIGRAFIL C® C30 S009 GLY Staple Carbon Fiber, Glycerine Sizing
- Formosa Plastics Formolon® NVW PVC
- Hexcel® HexPly® F185 Epoxy Resin, 1581 Glass Fabric
- A. Schulman POLYBATCH™ White HS8350 Concentrate Based In Impact Polystyrene
- Alliance BIF-17 Bonded (Composite) Magnetic Material
Copyright © lookpolymers.com All Rights Reserved