Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 39.0 MPa | 5660 psi | 5 mm/min; ISO 527 |
Polimeri Europa Edistir N 1840 Polystyrene General purpose polystyrene combining easy flow and medium heat. Edistir N 1840 is suggested in extrusion for glossy capping of HIPS sheets and for blending with HIPS or clear SBS for stiffer therm.. |
|||
Tensile Strength at Break | 39.0 MPa | 5660 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Cycolac® MG8000SR ABS This data was supplied by SABIC-IP for the Americas region. |
|||
Tensile Strength at Break | 39.0 MPa | 5660 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Cycolac® MG8000SR ABS (Europe-Africa-Middle East) This data was supplied by SABIC-IP for the Europe-Africa-Middle East region. |
|||
Tensile Strength at Break | 39.0 MPa | 5660 psi | Type I, 5 mm/min; ASTM D 638 |
SABIC Innovative Plastics Geloy FXTW30PE ASA Pearlescent GELOY ASA resin with copper-look for capstock extrusion. Outstanding weatherability.This data was supplied by SABIC-IP for the Americas region. |
|||
Tensile Strength at Break | 39.0 MPa | 5660 psi | ASTM D638 |
SABIC Innovative Plastics LNP FARADEX AS003 ABS LNP* Faradex* AS003 is a compound based on Acrylonitrile Butadiene Styrene resin containing 15% Stainless Steel. Added features of this material include: Electrically Conductive, EMI/RFI Shielding... |
|||
Tensile Strength at Break | 39.0 MPa | 5660 psi | ASTM D638 |
SABIC Innovative Plastics LNP FARADEX AS003 ABS (Europe-Africa-Middle East) LNP* Faradex* AS003 is a compound based on Acrylonitrile Butadiene Styrene resin containing Stainless Steel. Added features of this material include: Electrically Conductive, EMI/RFI Shielding. |
|||
Tensile Strength at Break | 39.0 MPa | 5660 psi | ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP AL001 ABS LNP LUBRICOMP* AL-4010 HP is a compound based on Acrylonitrile Butadiene Styrene resin containing 5% PTFE. Added features of this material include: Internally Lubricated. |
|||
Tensile Strength at Break | 39.0 MPa | 5660 psi | ASTM D638-02 |
Ipiranga Petrochem MB 0434 LS-L MDPE IPQ employs Spherilene technology from Basell in the production of MDPE. The raw materials, which are supplied by COPESUL, are pre-treated and fed into gas-phase reactors, where medium density polye.. |
|||
Tensile Strength at Break | 39.0 MPa | 5660 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics NORYL PX6120 PPE+PS (Asia Pacific) Noryl PX6120 is an unfilled material with good flow, high Impact and chemical resistance against cleaners. Noryl PX6120 is developed for personal care appplications. |
|||
Tensile Strength at Break | 39.0 MPa | 5660 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP KX06415 Acetal Copolymer LNP LUBRICOMP* KX06415 is a compound based on Acetal Copolymer resin containing 10% PTFE, 10% Aramid Powder. Added features of this material include: Easy Molding, Heat Stabilized, Wear Resistant. |
|||
Tensile Strength at Break | 39.0 MPa | 5660 psi | Type I, 50 mm/min; ASTM D 638 |
SABIC Innovative Plastics Xenoy® X6125 PBT+PC Unreinforced, impact modified, thermoplastic alloy (PBT+PC). High impact strength while retaining mechanical and thermal properties.This data was supplied by SABIC-IP for the Americas region. |
|||
Tensile Strength at Break | 39.0 MPa | 5660 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Xenoy® X6125 PBT+PC Unreinforced, impact modified, thermoplastic alloy (PBT+PC). High impact strength while retaining mechanical and thermal properties.This data was supplied by SABIC-IP for the Americas region. |
|||
Tensile Strength at Break | 39.0 MPa | 5660 psi | ISO 527 |
SABIC Innovative Plastics LNP Stat-loy 9X05426C PMMA LNP* Stat-loy* 9X05426C is a compound based on PMMA resin containing Anti-Static. Added features of this material include: Antistat.This data was supplied by SABIC-IP for the Americas region. |
|||
Tensile Strength at Break | 39.0 MPa | 5660 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP STAT-LOY 9X07438 ASA+PC LNP* STAT-LOY* 9X07438 is a compound based on Polycarbonate/ASA containing Proprietary Filler(s). Added features of this grade include: Antistatic, Colorable, Weatherable. |
|||
Tensile Strength at Break | 39.0 MPa | 5660 psi | ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP MF001AS PP (Asia Pacific) LNP* Thermocomp* MF001AS is a compound based on Polypropylene resin containing Glass Fiber. Added features of this material include: Heat Stabilized. |
|||
Tensile Strength at Break | 39.0 MPa | 5660 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP V1000SU PA LNP* Thermotuf* V1000SU is a compound based on Nylon resin. Added features of this material include: Heat Stabilized, UV Stabilized. |
|||
Tensile Strength at Break | 39.0 MPa | 5660 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics NORYL PX1007 PPE+PS Noryl* PX1007 is an unfilled non-chlorinated, non-brominated flame retardant PPE/HIPS grade. |
|||
Tensile Strength at Break | 39.0 MPa | 5660 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP KAL22M Acetal Copolymer LNP LUBRICOMP* KAL22M is a compound based on Acetal Copolymer resin containing 10% PTFE, 10% Aramid. Added features of this material include: Wear Resistant. |
|||
Tensile Strength at Break | 39.0 MPa | 5660 psi | ISO 527 |
SABIC Innovative Plastics LNP STAT-LOY KX96821 Acetal LNP STAT-LOY* KX96821 is a compound based on Acetal resin containing Proprietary Filler(s). Added feature of this material is: Antistat. |
|||
Tensile Strength at Break | 39.0 MPa | 5660 psi | ASTM D 638 |
Cossa Polimeri ESTADIENE 1640 AS Acrylonitrile Butadiene Styrene General purpose ABSGood impact resistance, high melt flow rate, high gloss, with antistatic, excellent processabilityInformation provided by Cossa Polimeri S.r.l. |
|||
Tensile Strength at Break | 39.0 MPa | 5660 psi | ISO 527-1/-2 |
Covestro Desmopan® W DP89043D Polyurethane PreprocessingMax. Water content |
|||
Tensile Strength at Break | 39.0 MPa | 5660 psi | ASTM D412 |
Alliance Polymers Zythane™ 6090A Thermoplastic Polyurethane Elastomer Zythane™ 6090A is a polycaprolactone-based TPU specifically formulated for injection molding applications .It exhibits excellent low compression set, abrasion resistance and toughness and has good .. |
|||
Tensile Strength at Break | 39.0 - 46.0 MPa | 5660 - 6670 psi | 5 mm/min.; IS 867-1963 |
Amity Thermosets ATF 197 Phenolic Molding Inorganic and glass Filler, Compression Molded Characteristics:Flame retardantSpark resistant Good electrical insulationHeat stability ( 200°C )Good mouldability Low water absorptionLow shrinkageColor-blackSoft/medium flow Applications:Switchg.. |
|||
Tensile Strength at Break | 39.0 MPa | 5660 psi | ASTM D638-08 |
3M Scotchkote™ 2400 Pipe Renewal Liner NSF/ANSI-61 certified polyurea formulation is 100% solids and contains no epoxy resin. It is designed to help solve a wide variety of problems common to potable water systems. It utilizes a trenchle.. |
|||
Tensile Strength at Break | 39.0 MPa | 5660 psi | ASTM D638 |
Beijing Chemical Industry KAIFA® GL3200 ABS Flame-Retardant Grade Good flammabilityInformation provided by Beijing Chemical Industry Research Institute (Group) |
|||
Tensile Strength at Break | >= 39.0 MPa | >= 5660 psi | JIS K7127 |
Asahi Glass Fluon® ETFE Film Applications: Electronics, Energy Saving, Wallpaper, Sound Suppression Walls, Aviation and SpaceInformation provided by Asahi Glass Company, Inc. |
|||
Tensile Strength at Break | 39.0 MPa | 5660 psi | ASTM D638 |
Asahi Glass Fluon® P-802UP PFA Perfluoropolymer Fluon® PFA is a copolymer of tetrafluoroethylene (C2F4) and perfluoroalkoxyethylene, which has excellent chemical, electrical, mechanical and surface properties. PFA retains many inherent character.. |
|||
Tensile Strength at Break | 39.0 MPa | 5660 psi | ISO 527-2 |
Ascend Performance Materials Vydyne® 41 Nylon 66, Conditioned Vydyne® 41 is a general-purpose, impact-modified PA66 resin. Available in natural, it is recognized for all the processing and property advantages inherent to PA66 with the addition of improved imp.. |
|||
Tensile Strength at Break | 39.0 MPa | 5660 psi | ISO 527-2 |
Ascend Performance Materials Vydyne® 41H Nylon 66, Impact Modified, Conditioned Vydyne® 41H is a general-purpose, impact-modified PA66 resin. Available in natural, it is heat-stabilized for improved resistance to elevated temperatures. The heat stabilization package for Vydyne.. |
|||
Tensile Strength at Break | 39.0 MPa | 5660 psi | ASTM D412 |
Alliance Polymers Zythane™ 7090A Thermoplastic Polyurethane Elastomer Zythane™ 7090A is a polyether-based TPU specifically formulated for extrusion molding applications .It exhibits excellent low compression set, abrasion resistance and toughness and has good hydroly.. |