Amity Thermosets ATF 197 Phenolic Molding Inorganic and glass Filler, Compression Molded

Category Polymer , Thermoset , Filled/Reinforced Thermoset , Phenolic
Manufacturer Amity Thermosets
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Amity Thermosets ATF 197 Phenolic Molding Inorganic and glass Filler, Compression Molded.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Characteristics:Flame retardantSpark resistant Good electrical insulationHeat stability ( 200°C )Good mouldability Low water absorptionLow shrinkageColor-blackSoft/medium flow Applications:Switchgear components exposed to sparkAutomotive ( electrical, electronic ) partsDecor items ( ash trays )Superior quality handles & knobs often exposed to flameAutomotive lamp caps Moudlings exposed to warm & humid climateMoulding exposed to low intensity flame and spark, etc.Information provided by Amity Thermosets Limited
Physical Properties Metric English Comments
Density 1.45 - 1.60 g/cc
0.0524 - 0.0578 lb/in³
Molding; IS 867-1963
Apparent Bulk Density 0.680 - 0.800 g/cc
0.0246 - 0.0289 lb/in³
IS 867-1963
Water Absorption 0.15 - 0.30 %
0.15 - 0.30 %
IS 13411-1993
Linear Mold Shrinkage 0.0045 - 0.0055 cm/cm
0.0045 - 0.0055 in/in
IS 13411-1992
Mechanical Properties Metric English Comments
Tensile Strength at Break 39.0 - 46.0 MPa
5660 - 6670 psi
5 mm/min.; IS 867-1963
Shear Strength 66.0 - 75.0 MPa
9570 - 10900 psi
2mm/min.; IS 867-1963
Izod Impact, Notched 0.220 - 0.300 J/cm
0.412 - 0.562 ft-lb/in
IS 13411-1992
Electrical Properties Metric English Comments
Volume Resistivity 3.2e+11 - 1.0e+12 ohm-cm
3.2e+11 - 1.0e+12 ohm-cm
IS 3396-1979
Surface Resistance 3.2e+10 - 3.2e+11 ohm
3.2e+10 - 3.2e+11 ohm
IS 3396-1979
Dielectric Strength 6.50 - 7.50 kV/mm

@Temperature 90.0 °C
165 - 191 kV/in

@Temperature 194 °F
IS 2584-1963
Comparative Tracking Index >= 150 V
>= 150 V
2824-1975
Processing Properties Metric English Comments
Mold Temperature 160 - 180 °C
320 - 356 °F
Injection Pressure 15.68 - 34.3 MPa
2274 - 4970 psi
Mold Pressure
Cure Time 0.333 - 0.500 min
0.00556 - 0.00833 hour
per mm
Shelf Life 12.0 Month